Search

Poly(propylene carbonate) (PPC) decomposes at high temperature to release CO2. This CO2-generation temperature of PPC can be reduced down to less than 80 °C with the aid of a photoacid generator (PAG). In the present work, we demonstrate that using an additional helper component, surface plasmonic gold nanorods (GNRs), the PPC degradation reaction can also be initiated by infrared (IR) irradiation. For this purpose, a PPC-containing nanoparticle formulation was developed in which PPC-based amphiphilic block copolymers (BCPs), poly(poly(ethylene glycol) methacrylate-b-propylene carbonate-b-poly(ethylene glycol) methacrylate) (PPEGMA-PPC-PPEGMA), were self-assembled with GNRs and PAG molecules via solvent exchange. Under IR irradiation, GNRs produce heat that can cause PPC to decompose into CO2, and PAG (after UV pretreatment) catalyzes this PPC degradation process. Two PPEGMA-PPC-PPEGMA materials were used for this study: PPEGMA7.3K-PPC5.6K-PPEGMA7.3K(“G7C6G7”) and PPEGMA2.1K-PPC5.6K-PPEGMA2.1K(“G2C6G2”). Addition of CTAB-coated GNRs dispersed in water to a G2C6G2 solution in DMF produced individually G2C6G2-encapsulated GNRs, whereas the same solvent exchange procedure resulted in the formation of polymer-coated GNR clusters when G7C6G7 was used as the encapsulating material. GNR/G2C6G2 NPs exhibited a surface plasmon resonance peak at 697 nm. The clustered morphology of G7C6G7-encapsulated GNRs caused a blue shift of the absorbance maximum to 511 nm. As a consequence, GNR/G2C6G2 NPs showed a greater absorbance/heat generation rate under IR irradiation than did GNR/G7C6G7 NPs. The IR-induced CO2generation rate was about 4.2 times higher with the GNR/G2C6G2+PAG sample than that with the GNR/G7C6G7+PAG sample. Both GNR/G7C6G7+PAG and GNR/G2C6G2+PAG systems produced ultrasound contrast enhancement effects under continuous exposure to IR light for >20 min; contrast enhancement was more spatially uniform for the GNR/G2C6G2+PAG sample. These results support the potential utility of PPC as a CO2-generating contrast agent in ultrasound imaging applications.

We envision that CaWO4(CWO) nanocrystals have the potential for use in biomedical imaging and therapy because of the unique ways this material interacts with high-energy radiation. These applications, however, require development of nanoparticle (NP) formulations that are suitable for in vivo applications; primarily, the formulated nanoparticles should be sufficiently small, chemically and biologically inert, and stable against aggregation under physiological conditions. The present study demonstrates one such method of formulation, in which CWO nanoparticles are encapsulated in bioinert block copolymer (BCP) micelles. For this demonstration, we prepared three different CWO nanocrystal samples having different sizes (3, 10, and 70 nm in diameter) and shapes (elongated vs truncated rhombic). Depending on the specific synthesis method used, the as-synthesized CWO NPs contain different surfactant materials (citric acid or cetyltrimethylammonium bromide or a mixture of oleic acid and oleylamine) in the coating layers. Regardless of the type of surfactant, the original surfactant coating can be replaced with a new enclosure formed by BCP materials using a solvent-exchange method. Two types of BCPs have been tested: poly(ethylene glycol-block-n-butyl acrylate) (PEG-PnBA) and poly(ethylene glycol-block-d,l-lactic acid) (PEG-PLA). Both BCPs are able to produce fully PEGylated CWO NPs that are stable against aggregation under physiological salt conditions for very long periods of time (at least three months). The optical and radio luminescence properties of both BCP-encapsulated and surfactant-coated CWO NPs were extensively characterized. The study confirms that the BCP coating structure does not influence the luminescence properties of CWO NPs.