The performance of superparamagnetic polymer composite microdevices is highly dependent on the magnetic particle content. While high loading levels are desired for many applications, the UV absorption of these nanoparticles limits the overall thickness of the fabricated microstructures and subsequently their capability of magnetic interaction. The combination of a visible-light-sensitive photoinitiator and particle self-organization is proposed to extend the exposure depth limitation in Epon SU-8 based superparamagnetic polymer composites. While superparamagnetic iron oxide particles strongly absorb i-line radiation required to cross-link the Epon SU-8 polymer matrix, we propose the utilization of H-Nu 470 photoinitiator to expand the photosensitivity of the composite toward the visible spectrum, where the dispersed nanoparticles are more transparent. The novel photoinitiator preserves the composite’s superparamagnetic properties as well as a homogeneous particle distribution. As a result, particle load or resist thickness can be more than doubled while maintaining exposure time. The self-organization of ordered magnetic structures allows for an additional increase in exposure depth of up to 40%, resulting in a 2.5-fold saturation magnetization.

Thick polycrystalline pure PbTiO3films with nano size grains were synthesized for the first time by aerosol deposition. Annealed 7 μm thick films exhibit well-saturated ferroelectric hysteresis loops with a remanent polarization and coercive field of 35 μC/cm2and 94 kV/cm, respectively. A large-signal effective d33,effvalue of >60 pm/V is achieved at room temperature. The measured ferroelectric transition temperature (Tc) of the films ∼550 °C is >50 °C higher than the reported values (∼490 °C) for PbTiO3ceramics. First-principles calculations combined with electron energy loss spectroscopy (EELS) and structural analysis indicate that the film is composed of nano size grains with slightly decreased tetragonality. There is no severe off-stoichiometry, but a high compressive in-plane residual stress was observed in the film along with a high transition temperature and piezoelectric response. The ferroelectric characteristics were sustained until 200 °C, providing significant advancement toward realizing high temperature piezoelectric materials.