The band gaps of isostructural Bi2OS2 and LaOBiS2 were examined using optical absorption and discussed with the band structures calculated based on the crystal structures determined using synchrotron X-ray diffraction. The Bi 6p and S 3p orbitals in the Bi-S plane were computationally predicted to constitute the bands near the Fermi level. The optical reflectance spectra of Bi2OS2 and LaOBiS2 showed optical band gaps of ca. 1.0 eV, which were close to the computationally calculated direct band gaps of ca. 0.8 eV. Our results show that Bi2OS2 and LaOBiS2 are semiconductors containing direct band gaps of 0.8-1.0 eV, and they are suggested to be candidates for optoelectronic materials in the near-infrared region without highly toxic elements., Comment: in Solid State Communications (2015)

The crystal structures of superconducting LaO1-xFxBiS2 (x ~ 0.23, 0.46) were determined by single-crystal X-ray diffraction analysis. Their space group was P4/nmm. Distortion of the Bi-S plane changed when the F content was increased from 0.23 to 0.46, and a nearly flat Bi-S plane was formed at x ~ 0.46. Computational calculations supported this effect of F doping on distortion of Bi-S plane. LaO1-xFxBiS2 with higher F contents were computationally predicted to be thermodynamically more unstable under ambient pressure. We discussed the bonding, conductivities, and synthetic routes of LaO1-xFxBiS2., Comment: Journal of Solid State Chemistry

F-substituted ROBiS2 (R = La, Ce, Nd) superconducting single crystals with different F concentration were grown successfully using CsCl/KCl flux. All the obtained single crystals had a plate-like shape with a well-developed ab-plane of 1-2 mm in size. The flux components of Cs, K, and Cl were not detected in the obtained single crystals by electron probe microanalysis. The grown single crystals of F-substituted LaOBiS2 and CeOBiS2 showed superconducting at about 3 K while the Tc of the F-substituted NdOBiS2 exhibited approximately 5 K. The superconducting anisotropy of the single crystals of F-substituted LaOBiS2 and NdOBiS2 was estimated to be 30-45 according to the effective mass model whereas those values were 13-21 for the F-substituted CeOBiS2 single crystals. The F-substituted CeOBiS2 single crystals exhibited magnetic order at about 7 K that apparently coexisted with superconductivity below around 3 K.

F-substituted NdOBiS2 superconducting single crystals were grown using CsCl/KCl flux. This is the first example of the single-crystal growth of a BiS2-based superconductor. The obtained single crystals had a plate-like shape with a size of 1-2 mm and a well-developed ab-plane. The crystal structure of the grown crystals was determined by single-crystal X-ray diffraction analysis to be the tetragonal space group P4/nmm (#129) with a = 3.996(3) A and c = 13.464(6) A. The chemical formula of the grown crystals was approximately Nd0.98(0.06)O0.7(0.1)F0.3(0.1)Bi0.98(0.04)S2, and Cs, K, and Cl were not detected in the grown crystals by electron probe microanalysis. The grown crystals had a critical temperature of approximately 5 K. The superconducting anisotropy of the single crystals was estimated to be about 30 from the effective mass model and the upper critical field., Comment: 27 pages, 9 figures