The Vickers hardness of polycrystalline {\gamma}-B was measured using a diamond indentation method. The elastic properties of polycrystalline {\gamma}-B (B=213.9 GPa, G=227.2 GPa, and E=503.3 GPa) were determined using ultrasonic measurement at ambient condition. Under the loading force up to 20 N, our test gave an average Vickers hardness in the asymptotic-hardness region of 30.3 GPa. The average fracture toughness was measured as 4.1MPa m1/2. Additionally, We also measured the hardness and elastic properties of polycrystalline {\beta}-B and PcBN for comparison. The hardness and elastic properties for polycrystalline {\gamma}-B was found to be very close to that of PcBN. Our results suggest that the polycrystalline {\gamma}-B could be a superhard polycrystalline material for industrial applications., Comment: 16 pages

The phase relations in boron have been investigated at high pressure and high temperature using a multianvil apparatus, and the quenched sample has been analyzed by x-ray diffraction, Raman spectra and transmission electron microscopy. We demonstrate that {\gamma}-B28 can be synthesized over a wide P-T range, and T-B50 is obtained at higher temperatures and similar pressures. The phase boundary of the {\beta}-B106, {\gamma}-B28 and T-B50 is determined at pressures between 7 and 18 GPa and the temperatures of 500-2200 {\deg}C. The results suggest that T-B50 might be an intermediate phase-metastable, formed for kinetic reasons (Ostwald rule) on the way from {\beta}-B106 to T-192 and {\gamma}-B28 to T-192., Comment: 14 pages, 4 figures