In order to study the effect of brine environment on the performance of oil well cement fluid loss additive (FLA) sodium p-styrene sulfonate/N-methylol acrylamide/itaconic acid (SSS/HAM/IA), the water loss of three different cement slurry systems added with different FLA additions (fresh water cement slurry, semi-saturated brine cement slurry and saturated brine cement slurry) were tested at 90°C and 150°C. The results show that SSS/HAM/IA has good salt tolerance. The water loss of three cement slurry systems was controlled within 100mL with FLA addition adjusted in the range of 1%~3% below 150 °C. The salt tolerance mechanism of SSS/HAM/IA was analyzed based on the microstructure of the three system terpolymer solutions characterized under environmental scanning electron microscopy (ESEM).

To adequately understand the waterborne epoxy resin and enhance the compressive, tensile strength of oil-well cement stone, the cement composite materials were prepared with different addition of waterborne epoxy resin, and the specimens were cured for 3days, 7 days, 14days, 28days at 50°C thermostatic water bath to test the compressive strength and tensile strength, respectively. The results showed when the content of resin emulsion is 30%, the compressive strength and tensile strength of the cement are increased by 303.09% and 306.04% compared with pure cement, respectively. Obviously, in the mechanical performance testing, oil-well cement stone modified by waterborne epoxy resin have been significantly improved compared with the pure cement. To explore the enhanced microstructure of oil-well cement modified with waterborne epoxy resin, the cement specimens were prepared with 30% waterborne epoxy resin analyzed by scanning electron microscopy (SEM).