Search

The setting processes in KetacCem, AquaCem and Fuji I glass-ionomer dental cements (GIC) as well as in the resin-modified glass-ionomer dental cement (RM-GIC) Fuji Plus have been studied by proton spin–lattice, T1, and spin–spin, T2, relaxation. The setting time dependence of the degree of hydration was studied as well. In contrast to zinc oxide dental cements, the changes in T1 and T2 are determined by the interactions of the water with the internal surface. Proton nuclear magnetic resonance relaxation is thus suitable to follow the setting of GIC and RM-GIC and gives valuable information on the GIC hardening dynamics.

The irradiation time of a visible-light-activated composite necessary to achieve full polymerization throughout the material was studied. Curing-time dependence on the thickness of the material was also investigated. To monitor the visible light-activation effect, the free radical concentration was measured as a function of irradiation time. If the composite sample is less than 0.5 mm thick and exposed to light for a time interval recommended by the manufacturer, full radical concentration is indeed created uniformly. This is not the case in thicker samples. Electron paramagnetic resonance (EPR) was used to monitor the concentration of free radicals in the samples. The number of radicals was monitored as a function of irradiation time during which the radicals were generated in samples 0.5, 0.8, 2.0, 3.0 and 5.0 mm thick. An EPR X-band spectro-meter was used to detect the free radical spectra. The number of free radicals per unit mass as a function of irradiation time shows that 60% of the maximum concentration of radicals in a 1 mm sample is reached in 24 s curing time, while in thicker samples it takes hundreds of seconds. On the basis of the experiments, a depth and irradiation time-dependent radical concentration model was developed. This model shows that a 2.0 mm thick sample is cured at the bottom side if irradiated for 60 s. It is proposed that the measure of the degree of polymerization in composite materials should be the polymerization of the bottom layer of the sample which is modelled from the number of free radicals generated in the sample.

The nuclear magnetic resonance spin-grouping technique has been applied to dentin from human donors of different ages. The apparent T2, T1, and T1 rho have been determined for natural dentin, for dentin which has been dried in vacuum, and for dried dentin which has been rehydrated in an atmosphere with 75% relative humidity. All apparent spin relaxation has been analyzed for exchange between the spin groups in which the dentin protons exist; the analyses incorporate the results of selective inversion recovery T1 measurements which better probe the effects of exchange. The exchange analyses of the high fields and rotating frame spin-lattice relaxation have also been correlated to determine uniquely the inherent relaxation parameters of the proton spin groups constituting the dentin magnetization. The natural dentin contains protons on water, protein, and hydroxy apatite; these spins contribute 50%, 45%, and 5% to the total dentin proton magnetization, respectively. The water exists in three distinct environments, the dynamics of each environment has been modeled. In the natural dentin 30% of the water undergoes uni-axial reorientation. 52% of the water has similar relaxation characteristics to bound water hydrating a large molecule, and the majority of the remaining water acts as bulk water undergoing isotropic reorientation. The results are independent of the age of the donor.

The irradiation time of a visible-light-activated composite necessary to achieve full polymerization throughout the material was studied. Curing-time dependence on the thickness of the material was also investigated. To monitor the visible light-activation effect, the free radical concentration was measured as a function of irradiation time. If the composite sample is less than 0.5 mm thick and exposed to light for a time interval recommended by the manufacturer, full radical concentration is indeed created uniformly. This is not the case in thicker samples. Electron paramagnetic resonance (EPR) was used to monitor the concentration of free radicals in the samples. The number of radicals was monitored as a function of irradiation time during which the radicals were generated in samples 0.5, 0.8, 2.0, 3.0 and 5.0 mm thick. An EPR X-band spectro-meter was used to detect the free radical spectra. The number of free radicals per unit mass as a function of irradiation time shows that 60% of the maximum concentration of radicals in a 1 mm sample is reached in 24 s curing time, while in thicker samples it takes hundreds of seconds. On the basis of the experiments, a depth and irradiation time-dependent radical concentration model was developed. This model shows that a 2.0 mm thick sample is cured at the bottom side if irradiated for 60 s. It is proposed that the measure of the degree of polymerization in composite materials should be the polymerization of the bottom layer of the sample which is modelled from the number of free radicals generated in the sample.

Partial dentures with free end saddles, classified as K I and II present special design problems because of the different properties of tooth support and mucosa support. The main principle is that strait saddles are designed as tooth-born, however in curved saddles tooth and mucosa-born dentures are preferred. The article describes so called "altered cast" clinical and laboratory procedure which prevents rocking of the denture around the fulcrum line in patients with resilient alveolar ridge mucosa. Besides that some typical designs of partial dentures are presented.

Direct retainers or clasps are the most demanding structural elements of the partial denture. Numerous clasps which are presented in the literature are divided into two main groups according to their design and function: clasps with occlusal approach (circumferential clasps) and clasps with gingival approach (vertical projection clasps). Number of clasps described in the article are satisfactory for creative design of all removable dentures in the partially edentolous mouth.

Removable partial denture with a rigid metal construction meets the three main requirements of the up-to-date prosthodontics, i.e. properly directed chewing forces through accurate proprioceptive control of the masticatory muscles and preservation of the healthy periodontal tissues. Because of its flexibility the acrylic partial denture does not fulfill the above mentioned criteria so it can be, except in particular clinical indications, considered as a temporary and transitional prosthodontic treatment.

The spin-spin, T2, and spin-lattice, T1, relaxation times and the magnetization of protons were measured in human enamel. The proton free induction decay was analyzed into solid-like interstitial water, enamel apatite, and semiliquid-like water components. The solid-like interstitial water was evaluated to be approximately 5 wt% and the semiliquid-like water to be approximately 1 to 2%. Neither in wet nor in dry natural enamel does the solid water exchange upon deuteration nor can it be extracted in vacuum. The semiliquid natural water, which is in the closed pores of the structure in the two samples above also remains unexchanged upon an 8 hr deuteration and cannot be extracted in a vacuum. With the lineshape-relaxation correlation NMR the free induction decays from heads and tails of the enamel rods were resolved. The solid-like water with T2 of approximately 14 microseconds and the apatite with a T2 of approximately 61 microseconds have T2's too short to be observed in an NMR zeugmatogram. Therefore only the semiliquid water component having an apparent T*2 of about 240 microseconds would contribute to the NMR image of human enamel. Since the relative intensity of this proton magnetization component in tooth is quite small the NMR image of tooth would show primarily the dentin and liquids within the tooth and on its surface.