Development of a dental alloy with high Au content is based on the ternary system of Au-Pt-Zn with a nominal composition of 86,9Au-9,9Pt-1,5Zn, and about 1,5 wt.% micro-alloying elements (In, Ir, Rh). The results analyses of different heat-treated states showed that the optimal mechanical properties and hardness of an Au-Pt-Zn alloy can be reached with combinations of heat treatment for 20 minutes at 723 K and then slowly cooling, if the alloy was annealed at 1223 K for 30 minutes and the water quenched. Research results confirmed that the microstructure of the Au-Pt-Zn alloy consists of two phases: α1-phase rich in Au (main phase) and α2-phase rich in Pt (minor phase). During XRD analysis and use of the Rietveld method, it was found that the α1-phase content is about 98,5 wt.% while the content of α2-phase is 1,5 wt.%. STA analyses show that the Au-Pt-Zn alloy has a solidus temperature of about 1292 K and a liquidus temperature of about 1412 K. Razvoj dentalne slitine s visokim sadržajem zlata zasnovan je na ternarnom sustavu Au-Pt-Zn s nominalnim sastavom 86,9Au-9,9Pt-1,5Zn i oko 1,5 mas. % mikrolegirajučih elemenata (In, Ir, Rh). Rezultati analize su pokazali da se u slučaju slitine odžarene kod 1223 K u trajanju od 30 minuta i zakaljena u vodi optimalna mehanička svojstva i tvrdoća Au-Pt-Zn slitine mogu postići kombinacijom toplinske obrade na 720 oC u trajanju 20 minuta s naknadnim sporim hlađenjem. Rezultati istraživanja su potvrdili da se mikrostruktura Au-Pt-Zn slitine sastoji od dvije faze: α1-faze bogate sa zlatom (primarna faza) i α2 - faze bogate s platinom (sekundarna faza). Tijekom XRD analize i primjenom Rietveldove metode utvrđeno je da je sadržaj α1-faze oko 98,5 mas. %, dok je sadržaj α2-faze iznosio oko 1,5 mas. %. STA analiza je pokazala da je Au-Pt-Zn slitina imala solidus temperaturu oko 1292 K, a likvidus temperaturu oko 1412 K.

Silver alloys with tellurium, selenium and sulphur fulfil the conditions for the internal oxidation. Microstructure of these alloys consists of matrix (dilute solid solution) and particles of intermetallic compounds. Internal oxidation of ternary alloys is very similar to that of the binary alloys, but there are also distinctions in thermodynamics properties of alloying elements. At the direct oxidation of the particles of the intermetallic compound the phenomena of the selective oxidation was observed. Concentration of more reactive elements is increasing in the oxidized part of the particles of the intermetallic compound (Te in AgTeSe alloys). Therefore the precipitated oxides formed with diffusional internal oxidation are richer with less reactive alloying element (Se in AgTeSe alloy). In the precipitated oxide particles the concentration of selenium is more than twice higher than of tellurium. Legure srebra s telurom, selenom i sumporom ispunjavaju uvjete za unutarnju oksidaciju. Mirkostruktura ovih legura sastoji se od osnove (razrijeđena kruta otopina) i čestica intermetalnih spojeva. Unutarnja oksidacija ternarnih legura veoma je slična onoj za binarne legure, ali postoje i razlike u termodinamičkim svojstvima legirajućih elemenata. Kod izravne oksidacije čestica intermetalnog spoja zapažena je pojava selektivne oksidacije. Koncentracija reaktivnijih elemenata raste u oksidiranom dijelu čestica intermentalnog spoja (Te u AgTeSe leguri). Prema tome precipitirani oksidi nastali difuzijskom unutarnjom oksidacijom su bogati s manje reaktivnim legirajućim elementom (Se u AgTeSe leguri). U percipitiranim oksidnim česticama koncentracija selena je dvostruko veća nego telura.

V prispevku obravnavamo proces notranjega ogljičenja, s katerim lahko izdelamo diskontinuirni kompozit Cu-C. Proces notranjega ogljičenja poteka brez pojava precipitacijske fronte, s sočasnim izločanjem grafitnih delcev po celotnem volumnu, potem ko se v trdni raztopini Cu-matice doseže, na defektih v kristalni mreži pa preseže nasičenost ogljika. Z analizo notranje ogljičenih vzorcev različnih izhodnih mikrostruktur Cu, ki so vsebovale različne vrste in koncentracije defektov (praznine, kristalne meje, dislokacije), smo ugotavljali vpliv izhodne mikrostrukture čistega Cu oz. posameznih vrst defektov na proces notranjega ogljičenja. Na osnovi dobljenih rezultatov in analiz lahko povzamemo, da pri notranjem ogljičenju različnih mikrostruktur čistega bakra precipitirajo iz kristalne mreže submikrometrsko majhni delci grafita. Volumenski delež in velikost grafitnih delcev sta odvisna od izhodne mikrostrukture bakra, temperature in časa notranjega ogljičenja. Največja gostota in najbolj enakomerna razporeditev grafitnih delcev sta doseženi pri gašenih vzorcih, kar kaže, da so klasterji praznin najbolj primerni element kristalne mreže za tvorbo grafitnih delcev. This paper presents the internal carbonisation process involved in the fabrication of a discontinuous Cu-C composite. The precipitation process of carbon particles does not involve the precipitation of the carbonisation front but a simultaneous precipitation of carbon particles throughout the entire volume of the Cu-matrix. The carbon concentration in the matrix reaches its maximum solubility, whereas the carbon super saturation is achieved on the defects in the crystall lattice. With an analysis of internally carbonised samples, containing different types and densities of defects (vacancies, crystall grains, dislocations) we attempted to identify the influence of the initial, pure copper microstructure and the separate types of defects on the internal carbonisation process. On the basis of the results and analyses we concluded that with internal carbonisation of the pure copper microstructure the submicron graphite particles were formed. The volume fraction and the size of the precipitated graphite particles depend on the initial copper microstructure, on the temperature and on the time of internal carbonisation. The highest density and the most uniform distribution were obtained with quenched samples. The results have shown that the clusters of vaccancies are the strongest traps for carbon atoms and the most favorable places for graphite precipitation.

In this paper we present a composite with fine dispersion of nano-sized bubbles, which can be formed by internal oxidation of fine dispersed graphite particles. For this purpose the initial pure Cu ribbons were internally carbonised to obtain very fine, some 100 nm-sized graphite particles homogeneously distributed in the Cu matrix. By the internal oxidation process the reaction of dissolved oxygen with graphite yields the gas products (CO, CO2) which cannot be dissolved in the crystal lattice of the metal. The gas products are meshed in the space previously occupied by graphite and they have a greater specific volume than the solid graphite, thus establishing the compressive stresses in the metalic matrix and consequently causing the strengthening offect. On the other hand, such stress fields can react with sliding dislocation, whereby they impede the dislocation motion and consequently we would expect that the composite mechanical properties would be improved. In this paper we present the composite with the fine dispersion of nano-sized bubbles, which can be formed by the internal oxidation of fine dispersed graphite particles. For this purpose the initial pure Cu ribbons were internally carbonised to obtain very fine some 100 nm sized graphite particles homogeneously distributed in the Cu matrix. By the internal oxidation process the reaction of dissolved oxygen with graphite yields the gas products (CO, CO2), which cannot be dissolved in crystal lattice of the metal. The gas products are meshed in the space previously occupied by graphite and they have a greater specific volume than solid graphite, thus establishing the compressive stresses in the metallic matrix and consequently causing the strengthening effect. On the other hand, such stress field can react with sliding dislocation, whereby they impede the dislocation motion and consequently it would expect that the composite mechanical properties would be improved.

In this article we describe the microstructural changes in the heat affected zone (HAZ) of the tool steel W. Nr. 1.2379, which was surfaced or welded by the submerged arc welding technique (SAW) with different welding parameters. Microstructure of the welds and of the surfacing welds was analysed by optical and scanning electron microscope. In this research, we particularly studied microstructural changes in the area of primary chromium carbides in the HAZ and their effect on the weld crystalization. We came to the conclusion that the temperature in the HAZ is high enough during the welding process that it caused primary carbides to dissolve and concentration of the carbide-forming elements and carbon increased in the surrounding austenite matrix area to eutectic composition, which remelts and solidified as secondary eutectic (ledeburite).

In this work we studied the response of newly developed armored steel plates PROTAC 500 to the ballistic testing with armored piercing bullets with a core of tungsten carbide, charge 7.62 mm. Interactions between the bullets and the steel plate was investigated by standard metallographic and mechanical testing methods. We were interested in the geometric features of interaction, the phenomenon of adiabatic shear bands (ASB), cracks and local failure, local melting and interaction of the components and plate with metal balls fragments in the melt, rate of deformation and the steel hardening.

A study was made of the weldability of 4-mm-thick aluminium-alloy 5083 plates using friction-stir welding. A plan of experiments was prepared based on the abilities of a universal milling machine, where the tool-rotation speed varied from 200 r/min to 1250 r/min, the welding speed from 71 mm/min to 450 mm/min and the tool tilt angle was held constant at 2. The factors feed per revolution (FPR) and revolution per feed (RPF) were introduced to get a better insight into the friction-stirring process. Samples for microstructure analyses, Vickers micro-hardness measurements and special miniature tensile-testing samples were prepared. The microstructure was prepared for observation on a light microscope under a polarised light source. A set of optimal welding parameters was determined at a FPR of 0.35 mm/r, at which quality welds can be made with a minimal increase in the weld hardness and an up to 15 % drop in the tensile strength. Izdelana je študija varivosti 4 mm debele pločevine iz aluminijeve zlitine 5083 pri varjenju s trenjem in mešanjem. Načrt eksperimentov je bil pripravljen na podlagi sposobnosti univerzalnega frezalnega stroja. Spreminjali smo hitrost vrtenja orodja od 200-1250 r/min, hitrost varjenja 71-450 mm/min, kot nagiba orodja pa je bil konstanten pri 2°. Vpeljana sta bila faktorja podajanje na vrtljaj (FPR) in obratov na podajanje (RPF), s katerima bolj nazorno prikažemo vpliv parametrov procesa. Iz izdelanih varov smo pripravili vzorec za analizo mikrostrukture, vzorec za meritev trdote po Vickersu ter posebne miniaturne epruvete za natezni preizkus. Mikrostruktura je bila pripravljena za opazovanje na svetlobnem mikroskopu v polarizirani svetlobi. Optimalni parametri varjenja so bili ugotovljeni pri FPR 0,35 mm/r, pri čemer dobimo kakovostne zvare, z minimalnim povečanjem trdote vara in do 15-odstotnim padcem natezne trdnosti.

In this work the results of the transformation kinetics of austenite heat resistant stainless steel with 2.27 wt.% silicon were presented. This work concerns the microstructural and fractography analysis during isothermal heat treatment of the steel using optical microscopy (OM) and scanning electron microscopy (SEM) equipped with energy dispersive spectroscopy (EDS). Firstly the steel was solution annealed at 1100 °C for 15 minutes to obtain a homogeneous starting conditions. After that, test samples were isothermal annealed in the temperature range from 600 to 900 °C at different annealing times (from 1 to 956 hours). Microhardness of samples was performed by Vickers method (HV0.3). Results of microstructural and fractography analysis as well as the hardness before and after isothermal heat treatment are shown. Thermodynamic calculation of equilibrium phases using ThermoCalc computer program was performed. It was found that the microstructure of steel after isothermal annealing was consisted of austenite and sigma phase. This phase was observed both at grain boundaries and within the austenite grains. In this case the formation of sigma phase is directly from austenite. Initial precipitation of the sigma phase took place along austenite grain boundaries. Morphology of sigma phase is spherical-oval like. With longer times the sigma phase continued to grow in size to agglomerate and coalesce in the form large angular particles, sometimes clustered at grain boundaries. At temperature of 600 °C the hardness becomes increasing after annealing of 48 hours, while in the temperature range 700-900 °C the hardness increases with annealing times higher from 8 hours.

After the black-oxide coating brown stains were observed forming on the surfaces of grey-cast-iron hot plates made for an electric stove. These stains were metallographically examined using a scanning electron microscope (SEM) equipped with an energy-dispersive X-ray spectrometer (EDXS). For the phase identification we also employed X-ray diffraction (XRD) analyses. The results of the analyses indicated that the stained surfaces of the hot plates were covered with whiskers of hematite (Fe2O3), while on the surfaces of the non-defective hot plates only magnetite (Fe3O4) was present. The thermodynamic calculations confirmed the possibility of the formation of hematite (Fe2O3) as a result of the oxidation of magnetite (Fe3O4) if the partial pressure of oxygen is increased during the black-oxide-coating process.

Results of microstructural and fractographic analysis and hardness testing of heat-resistant stainless steel with 2.27% Si carried out after isothermal annealing at 600°C are presented. Isothermal annealing times were different, from 1 to 702 hours. The microstructural and fractographic analysis were performed with scanning electron microscopy (SEM). The microstructure of investigated steel demonstrated the presence of austenite and little precipitates on grain boundaries. Results of EDX analysis of the precipitates were shown that contents of chromium increasing and nickel decreasing with annealing duration. Also, hardness values were increased (from 163 to 205 HV) with isothermal annealing duration. Fracture surface modes of steel were cleavage transcristalline with inoculation before annealing, and intercristalline and fragile after 702 hours of annealing.

In present work, the hardness, fracture mode and microstructure of heat resistant stainless steel AISI 310S before and after solution heat treatment were investigated. Temperature of solution heat treatment was 1100°C/30 minutes and after solution heat treatment the samples were quenched in water (15°C). Microstructure and fracture surface analysis were carried out with scanning electron microsope (SEM) and energy dispersive X-ray spectrometer (EDX). Microstructure of steel before heat treatment consisted of austenite and delta ferrite. Also, microstructure of steel after solution heat treatment and quenching was heterogeneous and consisted of austenite and delta ferrite. Sigma phase particles were not observed. Solution heat treatment a slight influence on the hardness decreasing (from 203 to 170 HV). Fracture surface before and after solution heat treatment characterized by a ductile fracture mode.

The subject of investigation was the effect of post-weld heat treatment (PWHT) on mechanical properties, hardness distribution across the welded joints, and on the microstructure of AISI 316L austenitic stainless steel weld metal. Steel plates of 15 mm thickness were welded by manual electric arc welding and treated at 600–900°C. The tensile strength increased and impact energy values decreased with the increasing annealing temperature. The hardness test results for the weld metal, which were approximately equal before PWHT and after it, were higher than those for the base metal and the heat-affected zone. The weld metal microstructure was examined by means of an optical microscope and a scanning electron microscope. It demonstrated the presence of austenite, ferrite and microslag inclusions before PWHT, and that of sigma phase after PWHT. Also, the presence of complex Mn-Cr-Si-Ti inclusions in small holes was observed in tensile and impact (Charpy) tested specimens.

U radu su prikazani rezultati ispitivanja metodama bez razaranja, mehaničkih svojstava i mikrostrukture lima iz austenitnog čelika AISI 321 prije i nakon zavarivanja. Lim dimenzija 300x300x10 mm pripremljen je za zavarivanje u obliku sučeljenog V-spoja. Korijen zavara provaren je REL postupkom, a popuna TIG postupkom. Ispitivanja bez razaranja sastojala su se od radiografskih ispitivanja i ispitivanja penetrantima. Mikrostrukturna ispitivanja su obuhvaćala određivanje mikrostrukture zavarenog spoja optičkim mikroskopom. Mjerenje sadržaja delta-ferita provedeno je pomoću feritoskopa. Ispitivanjem bez razaranja utvrđeno je postojanje greške u obliku neprovarenog korijena zavara. Mikrostruktura osnovnog materijala bila je gotovo potpuno austenitna, a zone taljenja austenitno- feritna. Sadržaj delta ferita u osnovnom materijalu iznosio je ispod 1%, dok je u zoni taljenja iznosio oko 8%.

In this paper we present a composite with fine dispersion of nano-sized bubbles, which can be formed by internal oxidation of fine dispersed graphite particles. For this purpose the initial pure Cu ribbons were internally carbonised to obtain very fine, some 100 nm-sized graphite particles homogeneously distributed in the Cu matrix. By the internal oxidation process the reaction of dissolved oxygen with graphite yields the gas products (CO, CO2) which cannot be dissolved in the crystal lattice of the metal. The gas products are meshed in the space previously occupied by graphite and they have a greater specific volume than the solid graphite, thus establishing the compressive stresses in the metalic matrix and consequently causing the strengthening offect. On the other hand, such stress fields can react with sliding dislocation, whereby they impede the dislocation motion and consequently we would expect that the composite mechanical properties would be improved.

Results of mechanical testing and of microstructural analysis of AISI 316L austenitic stainless steel carried out before and after welding and post-weld heat treatment are presented. Steel plates of 15 mm thickness were welded by manual electric arc welding process. Heat treatment consisted of annealing at 600, 700, 800, and 900 °C for two hours, and was followed by cooling in the air. For microstructure examination an optical microscope and a scanning electron microscope were used. The weld metal microstructure demonstrated the presence of austenite, ferrite, and microslag inclusions before annealing, and of sigma phase after annealing. The tensile strength increased and impact energy values decreased with the increasing annealing temperature. Complex Mn-Cr-Si-Ti inclusions in the dimples were observed in the tensile and Charpy tested specimens.

In this study the hardenability, the cooling rates and microstructures of low alloy Cr-Mo and Mn-Mo steels were investigated. The cooling rate determines of amount of martensite structure. Hardenability test was carried out by Jominy method. Microstructure was determined using a scanning electron microscopy (SEM). The cooling rates in the temperature range between 1133 and 973 K at different distances from the quenched end of low alloy Cr-Mo and Mn-Mo steels were found. Also the hardness and microstructures against the distances from quenched end are determined. The economical way of increasing the hardenability of steels (at constant carbon content) is to increase the manganese content.

A survey of the solidification structure of austenitic stainless steels is presented. The solidification occurs, depending on the content of the main alloying elements, with the primary formation of delta-ferrite or austenite. In the case of primary solidification of delta-ferrite, this phase reacts with the residual melt producing austenite with a peritectic reaction. The hot workability of the as-solidified microstructure is better in the case of primary solidification of delta-ferrite, since, in this case, the accumulation of impurities in the final melt is prevented. Some impurities, slightly soluble or insoluble in the solid phase at solidification, e.g., lead, decrease the hot workability significantly, which is also lowered in the case of the segregation of soluble impurities at the boundary of austenite and delta-ferrite. The integrity of the continuous cast slab can be improved and the cracking by hot rolling can be prevented by an optimal adiustment of the steel chemical composition and the parameters of continuous casting. Laboratory tests of one-pass rolling of wedge-shaped specimens of industrial steels have confirmed the recommendations and the conclusions in the quoted references. Podan je pregled literature o strjevalni strukturi avstenitnih nerjavnih jekel. Strjevanje se začne v odvisnosti od vsebnosti glavnih legirnih elementov, s primarno kristalizacijo delta-ferita ali avstenita. V primeru primarnega nastanka delta-ferita nastane pri nadaljevanju strjevanja s peritektično reakcijo med trdno fazo in preostalo talino avstenit. Vroča preoblikovalnost jekla s strjevalno mikrostrukturo je boljša pri primarni kristalizaciji delta-ferita, ker ta prepreči koncentracijo nečistoč v jeklu v zadnji meddendritni talini. Nekatere nečistoče, ki so netopne ali malo topne v trdni fazi pri kristalizaciji, npr. svinec, močno zmanjšajo vročo preoblikovalnost jekla s strjevalno strukturo, ki se zmanjša tudi zaradi segregacije topnih nečistoč na meji med avstenitom in delta-feritom. Integriteto kontinuirno litih slabov in obseg razpok pri vročem valjanju je mogoče doseči z uravnoteženjem kemične sestave taline in parametrov kontinuirnega litja. Laboratorijski preizkusi z valjanjem klinastih preizkušancev iz industrijskega jekla s strjevalno strukturo v enem prehodu so potrdili sklepe in priporočila v citiranih referencah.

Poznato je da troska ima veoma važnu ulogu tijekom proizvodnje čelika. U ovom su radu prikazani rezultati karakterizacije skrutnute elektropećne troske nastale tijekom industrijske proizvodnje niskolegiranog krom-molibdenskog čelika (42CrMo4). Karakterizacija troske dobivena je pomoću brojnih komplementarnih metoda (DTA, TGA, DSC, SEM, EDS, PIXE i XRD). Utvrđen je fazni sastav troske i distribucija faza. Nakon 50 minuta upuhivanja kisika troska se primarno sastoji od FeO (wüstite), beta-Ca_2SiO_4 (larnite) i 3CaO×Fe_2O_3×3SiO_2 (andradide). Završna troska uzeta iz lonca prije kontinuiranog lijevanja sadrži: 3CaO×Fe_2O_3×3SiO_2, (Ca, Mn)_2SiO_4 i Mg(Al, Fe)_2O_4 (ferrian-spinel) kao i manji udio K_2Na_4Ca_2Al_6Si_5O_24(CrO_4)_2, FeO i beta- Ca_2SiO_4.

U radu su prikazani rezultati ispitivanja mehaničkih svojstava i mikrostrukture cijevi iz niskolegiranog krom-molibdenskog čelika. Čelik dobiven u industrijskim uvjetima valjan je u toplovaljane bešavne cijevi (promjera 159 mm i debljine stijenke 8 mm). Nakon toga cijevi su se postupkom hladnog pilgerovanja reducirale na vanjski promjer 130 mm i debljinu stijenke 6, 2 mm te su odžarene na 700°C u peći pod zaštitnom atmosferom. Mehanička i mikrostrukturna analiza provedene su na uzorcima nakon žarenja. Mikrostruktura je analizirana pretražnom elektronskom mikroskopijom (SEM) uz primjenu energetsko disperzijske spektralne analize. Utvrđena je bainitna mikrostruktura s izlučenim karbidnim česticama cementitnog tipa. Oko pukotina uz vanjsku stijenku cijevi zapažena je prisutnost kompleksnih oksidnih uključaka.

The effect of post-weld heat treatment on mechanical properties, microstructure and fracture mode of low-alloyed CrMoNb steel was examined using an optical microscope, and a scanning and transmission electron microscopes. Steel plates, 18 mm thick, were welded by means of the submerged arc welding technique and then heat treated in the temperature range from 475 to 700°C. It was found that the tensile strength, hardness and impact energy values decrease with the increasing annealing temperature, except for annealing at 550°C and 625°C. Anomalies were attributed to the precipitation of fine carbides. Complex cementite proved to be beneficial in controlling the fracture mechanism in impact (Charpy V-notch) and tensile tested specimens.

U radu su prikazani rezultati mikrostrukturne analize optičkim, pretražnim i transmisijskim mikroskopom niskolegiranog Cr-Mo-Nb čelika prije i nakon zavarivanja. Zavarivanje lima debljine 18 mm provedeno je TIG (za korijen zavara) iu EPP postupkom (za popunu zavara). Provedena je mikrostrukturna analiza osnovnog metala, zone utjecaja topline i zone taljenja. Zapažena su područja bainitne i feritno-perlitne mikrostrukture s pojavom igličastih mikrostruktura te izlučenih karbida cementitnog (M3C) tipa.

U radu su prikazani rezultati fraktografske analize prijelomnih površina ostataka uzoraka nakon ispitivanja mehaničkih svojstava i udarne radnje loma zone taljenja niskolegiranog Cr-Mo-Nb čelika nakon EPP zavarivanja. Ispitivanja su provedena pretražnim elektronskim mikroskopom (SEM) opremljenim sustavom za energetsko disperzijsku (EDS) analizu. Utvrđeno je da su prijelomne površine karakterizirane sitnojamičastim duktilnim prijelomom. Iniciranje prijeloma odvijalo se na međupovršinama karbid/metalna osnova i uključak troske/metalna osnova. Zapažena su i područja krhkog transkristalnog prijeloma.

The article discussed the morphology, microstructure and chemical composition of the boundary layer in explosive welding of low-carbon steel and tantalum plates. Pools of melt composed of both metals and having a heterogeneous chemical composition appear on the boundary layer. This phenomenon is the results of incomplete mixing of both: molten metals due to rapid cooling and solidification. Within the pools of alloy, a large number of non-metallic oxide inclusions, products of deoxidation of molten alloys, can be found. The main component of the non-metal inclusions is Ta2O5, which also contains iron, manganese and aluminium oxides. The most probable source of oxygen is the oxide scale from the surface of the low-carbon steel, which was poorly cleaned prior to welding.

On the basis of experimentally obtained data, it was established that a very thin layer of a melt is generated at the explosive welding of two metals at the bond interface within which impurities flow at the bond during melting. Rapid cooling after the collision generates an alloy of different structure and very small grains of an average thickness approximately 1 to 2 mm. The generation of such an amorphous layer in the bond area has been noticed with various metal combinations and represents a fundamental mechanism of explosive welding of metals. Using the metallographic analysis, the development of the vortices which were formed by the explosive welding of low-carbon steel and titanium plates is described in the paper., Na osnovi eksperimentalnih rezultata utvrđeno je da pri eksplozijskom zavarivanju dvaju metala na međupovršini spoja nastaje veoma tanki sloj rastaljenog metala unutar kojeg dolazi do istjecanja nečistoća tijekom taljenja. Velika brzina hlađenja nakon sudara dovodi do nastanka sitnozrnate legure drugačije strukture s proječnom veličinom od 1 do 2 mm. Zapaženo nastajanje amorfnog sloja na području spoja kod različitih kombinacija metalnih materijala predstavlja temeljni mehanizam eksplozijskog zavarivanja metala. Primjenom rezultata metalografske analize u radu je opisan razvoj vrtloga koji su nastali eksplozijskim zavarivanjem ploča iz niskougljičnog čelika i titana.

U radu su prikazani rezultati ispitivanja mehaničkih svojstava i mikrostrukture lima iz niskolegiranog Cr-Mo-Nb čelika. Lim debljine 18 mm pripremljen je za zavarivanje u obliku sučeljenog X-spoja. Korijen zavara provaren je TIG postupkom uz uporabu DCMS-IG elektrode promjera 2, 4 mm. Popuna zavarenog spoja ostvarena je EPP postupkom uporabom S2CrMo1 elektrode promjera 2 mm. Ispitivanje mikrostrukture čelika provedeno je skenirajućim elektronskim mikroskopom (SEM) koji ima sustav za energetsko disperzijsku spekroskopsku (EDS) analizu. Utvrđeno je da je mikrostruktura osnovnog materijala sastavljena od ferita i perlita. Mikrostrukturu zone taljenja nakon žarenja kod 700 °C karakterizira feritno-perlitna mikrostruktura s izlučenim karbidnim česticama. Prijelomne površine uzorka nakon ispitivanja žilavosti zone taljenja sadrže primarno jamičasti duktilni prijelom s određenim područjima transkristalnog prijeloma. Prijelom je započeo na međupovršinama karbidne čestice/metalna osnova.

In this work the results of phase composition of slag at industrial production of low alloy chromium-molybdenum steel (42CrMo4) in the electric arc furnace (EAF) were shown. Slag samples were analysed by the scanning electron microscopy (SEM), x-ray diffraction (XRD) and energy dispersive x-ray techniques. Slag samples were taken simultaneously with determination of chemical composition of the steel at the different times of production of the steel.

The manufacturing of metal composite materials with high rate energy concentration method bases on ultra high speed collision of metal plates to be bonded. Proper control of collision parameters ensures successful process development and hence good bond quality. Direct collision pressure measurements is very difficult because of high pressure levels (which could reach several hundred kbars) and its short duration (only 0, 001 second or less). By means of experimental work and mathematical modelling, good bond quality is achievable. It is controlled by non-destructive and mechanical testing methods, and by micro and macrostructure investigations.

This paper presents the internal carbonisation process involved in the fabrication of a discontinuous Cu-C composite. The precipitation process of carbon particles does not involve the precipitation of the carbonisation front but a simultaneous precipitation of carbon particles throughout the entire volume of the Cu-matrix. The carbon concentration in the matrix reaches its maximum solubility, whereas the carbon super saturation is achieved on the defects in the crystall lattice. With an analysis of internally carbonised samples, containing different types and densities of defects (vacancies, crystall grains, dislocations) we attempted to identify the influence of the initial, pure copper microstructure and the separate types of defects on the internal carbonisation process. On the basis of the results and analyses we concluded that with internal carbonisation of the pure copper microstructure the submicron graphite particles were formed. The volume fraction and the size of the precipitated graphite particles depend on the initial copper microstructure, on the temperature and on the time of internal carbonisation. The highest density and the most uniform distribution were obtained with quenched samples. The results have shown that the clusters of vaccancies are the strongest traps for carbon atoms and the most favorable places for graphite precipitation. V prispevku obravnavamo proces notranjega ogljičenja, s katerim lahko izdelamo diskontinuirni kompozit Cu-C. Proces notranjega ogljičenja poteka brez pojava precipitacijske fronte, s sočasnim izločanjem grafitnih delcev po celotnem volumnu, potem ko se v trdni raztopini Cu-matice doseže, na defektih v kristalni mreži pa preseže nasičenost ogljika. Z analizo notranje ogljičenih vzorcev različnih izhodnih mikrostruktur Cu, ki so vsebovale različne vrste in koncentracije defektov (praznine, kristalne meje, dislokacije), smo ugotavljali vpliv izhodne mikrostrukture čistega Cu oz. posameznih vrst defektov na proces notranjega ogljičenja. Na osnovi dobljenih rezultatov in analiz lahko povzamemo, da pri notranjem ogljičenju različnih mikrostruktur čistega bakra precipitirajo iz kristalne mreže submikrometrsko majhni delci grafita. Volumenski delež in velikost grafitnih delcev sta odvisna od izhodne mikrostrukture bakra, temperature in časa notranjega ogljičenja. Največja gostota in najbolj enakomerna razporeditev grafitnih delcev sta doseženi pri gašenih vzorcih, kar kaže, da so klasterji praznin najbolj primerni element kristalne mreže za tvorbo grafitnih delcev.

This work describes the hydrogen embrittlement damage of tubing made from a commercial low alloy manganese steel containing vanadium. Hydrogen charging of steels was carried out in 0.5 M H2SO4 solution which contained 10 mg/l As2O3 for 2 h under static load. Fractography was carried out using a scanning electron microscope (SEM) equipped with energy dispersive X-ray spectrometry (EDXS). Normalizing the tubing increased the yield strength. Tubing normalized at 900 °C is more resistant to hydrogen embrittlement (HE) compared to that in the as-received condition. The improved behaviour of steels when normalized at 900 °C can be attributed to a fine ferrite-pearlite microstructure (mean area of pearlite colonies 2.5 times smaller than in the as-received condition) and a beneficial variation in hydrogen trapping behaviour. Initiation of fracture occurred at complex inclusion/matrix interfaces. The size of the inclusions that caused fracture was 2 to 5 micrometer.

The paper describes experimental results of microstructural investigation of AlMg3 alloy before and after welding by TIG technique. Microstructure of base metal contained from 74.8%Al-17.3%Fe-4.9%Mn-1.8%Mg-1.2%Si as well as 97.3% Al and 2.7% Mg phases. Using SEM and EDX analysis was found that (Fe, Ti, Cr) C and copper sulphide particles as well as poosity are presented into weld metalat grain boundaries. Also the gas hole into weld metal was observed.

U ovom radu prikazani su rezultati ispitivanja mikrostrukture dupleks nehrđajućeg čelika prije i poslije zavarivanja. Dobiveni rezultati ukazuju da su u zoni utjecaja topline i zoni taljenja prisutne faze bogate kromom. Kvantitativna analiza EDS metodom pokazale je da je to faza koja se sastoji od 34.05%Cr-56.0%Fe-7.9%Ni-0.3%Mo- 0.7%Si(mas.%)

The scale formed on carbon steel blooms as a result of heating was analysed by means of light microscopy, scanning electron microscopy and X-ray diffraction.

In the presented investigation the causes of the screw damage on the head of a 1.8 liter gasoline car engine were examinated. The damage was the result of common disadvantageous environmental influences and reversed mechanical and temperature loads. V okviru predstavljene raziskave smo analizirali vzroke za poškodbo vijaka na glavi bencinskega motorja osebnega avtomobila s prostornino motorja 1,8 l. Poškodba do dokončne porušitve je nastajala določen čas in je posledica skupnega neugodnega vpliva okolice in menjajočih se mehanskih in temperaturnih obremenitev.

u ovom radu prikazani su rezultati istraživanja na cijevima iz niskolegiranog 2.25Cr-1Mo čelika. Mikrostruktura osnovnog materijala je feritno- perlitna. Pomoću skenirajuće elektronske mikroskopije (SEM) zapaženo je da su cijevi nakon dugotrajne uporabe imale izlučene karbide po granicama primarnog austenitnog zrna. Mikrostruktura zone utjecaja topline i zone taljenja sastavljena je od zrnatog i igličastog ferita s izlučenim karbidima (77, 3-81, 5%Fe, 11, 2-15, 7%C, 4, 7-4, 4%Cr, 0, 5%Mn i 2, 0-2, 3%Mo, mas.%).

U ovom radu prikazani su rezultati ispitivanja mehaničkih svojstava i mikrostrukture lima iz AlMg3 legure (debljina 7 i 4 mm) zavarenog TIG postupkom. Blokovi AlMg3 legure zagrijani su na 520oC i toplo valjani u lim debljine 7 mm. Nakon toga limovi su hladno valjani do debljine 4 mm. Zavarivanje lima provedeno je TIG postupkom primjenom dodatnog materijala iz AlMg5 legure. Prije i nakon zavarivanja ispitana su mehanička svojstva i mikrostruktura pomoću skenirajućeg elektronskog mikroskopa (SEM). Zapaženo je da su zavareni limovi debljine 7 mm tijekom vlačnog ispitivanja pucali na osnovnom materijalu, dok su limovi debljine 4 mm pucali u zoni taljenja. Mikrostruktura zone utjecaja topline i zone taljenja karakterizirane su brojnim intermetalnim fazama, te segregacijama bogatih s Mg.

The inhibition of surface corrosion of low-alloyed CrMo steel by proparylic alcohol was investigated using the methods of linear polarization and electrochemical impedance spectroscopy (EIS). Tests were carried out in a deareated 0.5M H2SO4 solution in the absence and in the presence of propargylic alcohol (5 mM) at different immersion times at open circuit potential. Proprgylic alcohol suppressed both the anodic and cathodic dissolution processes by adsorption and by blocking of active sites. The inhibition efficiency increased as a function of immersion time. The agreement between the inhibition efficiency values calculated from the two types of measurements was quite good. The thickness of the inhibitory film (0.46-0.82 nm) was calculated from EIS measurements.

U ovom radu prikazani su rezultati istraživanja površine hladno valjanih cijevi iz čelika St. 52.3. Nakon ispitivanja cijevi ultrazvukom na uzorcima s površinskim pukotinama provedena je analiza optičkom i skenirajućom elektronskom mikroskopijom (SEM). Optičkom mikroskopijom utvrđeno je prisustvo nemetalnih uključaka oko pukotina. Određena je dubina pukotine te raspodjela Fe, C, Mn i O oko pukotina pomoću valno disperzijskog spektrometra. Utvrđene pukotine vjerojatno su posljedica toplog valjanja cijevi koje su se pojavile tijekom hladnog valjanja.