Search

In Ni(OH)2, a greater extent of band (3d electron states with eg symmetry) broadening can facilitate electron transfer from the electrocatalyst to the external circuit, leading to higher OER catalytic performance.

The electron-transfer process during the oxygen evolution reaction (OER) often either proceeds solely via a metal redox chemistry (adsorbate evolution mechanism (AEM), with metal bands around the Fermi level) or an oxygen redox chemistry (lattice oxygen oxidation mechanism (LOM), with oxygen bands around the Fermi level). Unlike the AEM, the LOM involves oxygen redox chemistry instead of metal redox, which leads to the formation of a direct oxygen-oxygen (OO) bond. As a result, such a process is able to bypass the rate-determining step, that is, OO bonding, in AEM, which highlights the critical advantage of LOM as compared to the conventional AEM. Thus, it has been well reported that LOM-based catalysts are able to demonstrate higher OER activities as compared to AEM-based catalysts. Here, a comprehensive understanding of the oxygen redox in LOM and all documented and possible characterization techniques that can be used to identify the oxygen redox are reviewed. This review will interpret the origins of oxygen redox in the reported LOM-based electrocatalysts and the underlying science of LOM-induced surface reconstruction in transition metal oxides. Finally, perspectives on the future development of LOM electrocatalysts are also provided.

Realizing an efficient electron transfer process in the oxygen evolution reaction by modifying the electronic states around the Fermi level is crucial in developing high-performing and robust electrocatalysts

Transparent ferroelectrics, with promising prospects in transparent optoelectronic devices, have unique advantages in self-powered photodetection. The self-powered photodetectors based on the photovoltaic effect have quicker responses and higher stability compared with those based on the pyroelectric effect. However, the ferroelectric ceramics previously applied are always opaque and have no infrared light-stimulated photovoltaic effect. Thus, it would be very meaningful to design photodetectors based on infrared light-stimulated photovoltaic effect and/or transparent ferroelectric ceramics. In this work, highly optical transparent pristine lead lanthanum zirconate titanate (PLZT) and band gap-engineered Ni-doped PLZT ceramics with excellent piezoelectric/ferroelectric properties were prepared by hot-pressing sintering. Stable and excellent photovoltaic performance was obtained for pristine PLZT and band gap-engineered PLZT. The value of short-circuit current density is at least 2 orders of magnitude larger than those in PLZT reported in previous works. The transparent PLZT and Ni-doped PLZT ferroelectric ceramics are applied as self-powered photodetectors for the first time for 405 nm and near-infrared light, respectively. The devices based on PLZT under 405 nm light exhibit high detectivity (7.15 × 107 Jones) and quick response (9.5 ms for rise and 11.5 ms for decay), and those devices based on Ni-doped PLZT, under near-infrared light filtered from AM 1.5 G simulated sunlight, also exhibit high detectivity (6.86 × 107 Jones) and short response time (8.5 ms), both presenting great potential for future transparent photodetectors.

Defect-engineered perovskite oxides that exhibit ferroelectric and photovoltaic properties are promising multifunctional materials. Though introducing gap states by transition metal doping on the perovskite B-site can obtain low bandgap (i.e., 1.1-3.8 eV), the electrically leaky perovskite oxides generally lose piezoelectricity mainly due to oxygen vacancies. Therefore, the development of highly piezoelectric ferroelectric semiconductor remains challenging. Here, inspired by point-defect-mediated large piezoelectricity in ferroelectrics especially at the morphotropic phase boundary (MPB) region, an efficient strategy is proposed by judiciously introducing the gap states at the MPB where defect-induced local polar heterogeneities are thermodynamically coupled with the host polarization to simultaneously achieve high piezoelectricity and low bandgap. A concrete example, Ni2+ -mediated (1-x)Na0.5 Bi0.5 TiO3 -xBa(Ti0.5 Ni0.5 )O3-δ (x = 0.02-0.08) composition is presented, which can show excellent piezoelectricity and unprecedented visible/near-infrared light absorption with a lowest ever bandgap ≈0.9 eV at room temperature. In particular, the MPB composition x = 0.05 shows the best ferroelectricity/piezoelectricity (d33 = 151 pC N-1 , Pr = 31.2 μC cm-2 ) and a largely enhanced photocurrent density approximately two orders of magnitude higher compared with classic ferroelectric (Pb,La)(Zr,Ti)O3 . This research provides a new paradigm for designing highly piezoelectric and visible/near-infrared photoresponsive perovskite oxides for solar energy conversion, near-infrared detection, and other multifunctional applications.