Actinide research at the nanoscale is gaining fundamental interest due to environmental and industrial issues. The knowledge of the local structure and speciation of actinide nanoparticles, which possibly exhibit specific physico-chemical properties in comparison to bulk materials, would help in a better and reliable description of their behavior and reactivity. Herein, the synthesis and relevant characterization of PuO2 and ThO2 nanoparticles displayed as dispersed colloids, nanopowders or nanostructured oxide powders, allow to establish a clear relationship between the size of the nanocrystals composing these oxides and their corresponding An(IV) local structure investigated by EXAFS spectroscopy. Particularly, the probed An(IV) first oxygen shell evidences an analogous behavior for both Pu and Th oxides. This observation suggests that the often observed and controversial splitting of the Pu-O shell on the Fourier transformed EXAFS signal of PuO2 samples is attributed to a local structural disorder driven by a nanoparticle surface effect rather than to the presence of PuO2+x species.

For the first time, stable intrinsic plutonium colloid was prepared by ultrasonic treatment of PuO2 suspensions in pure water at room temperature. The yield of Pu colloid was found to increase with PuO2 specific surface area and by using reducing carrier gas mixture. Kinetic data evidenced that both chemical and mechanical effects of ultrasound strongly contribute to the mechanism of Pu colloid formation. At first, the fragmentation of initial PuO2 particles accelerates the overall process providing larger surface of contact between cavitation bubbles and solids. Furthermore, hydrogen formed during sonochemical water splitting enables reduction of Pu(IV) to more soluble Pu(III), which then reoxidizes yielding Pu(IV) colloid. Sonochemical colloid was compared with hydrolytic one using HRTEM, Pu LIII XAS, and STXM/NEXAFS (O K-edge) techniques. Both colloids are composed of quasi-spherical nanocrystalline particles of PuO2 (fcc, Fm¯3 m space group) measuring about 7 nm and 3 nm, respectively. Moreover, HRTEM revealed nanostructured morphology for initial PuO2. The EXAFS spectra of colloidal PuO2 nanoparticles were fitted using triple oxygen shell model for the first coordination sphere of Pu(IV). HRTEM and EXAFS studies revealed the correlation between the number of Pu-O and Pu-Pu contacts and atomic surface-to-volume ratio of studied PuO2 nanoparticles. The STXM/NEXAFS study indicated that the oxygen state of hydrolytic Pu colloid is influenced by hydrolyzed Pu(IV) species in much more extent than PuO2 nanoparticles of sonochemical colloid. In general, hydrolytic and sonochemical colloids can be described as core-shell nanoparticles composed of quasi stoichiometric PuO2 core and hydrolyzed Pu(IV) moieties at the surface shell.