Search

The purpose of this study was to compare the tensile bond strength of composite resin bonded to erbium:yttrium-aluminium-garnet (Er:YAG) laser-prepared dentine after different durations of acid etching. The occlusal third of 68 human third molars was removed in order to expose the dentine surface. The teeth were randomly divided into five groups: group B (control group), prepared with bur and total etch system with 15 s acid etching [37% orthophosphoric acid (H3PO4)]; group L15, laser photo-ablated dentine (200 mJ) (laser irradiation conditions: pulse duration 100 A mu s, air-water spray, fluence 31.45 J/ cm(2), 10 Hz, non-contact hand pieces, beam spot size 0.9 mm, irradiation speed 3 mm/s, and total irradiation time 2 x 40 s); group L30, laser prepared, laser conditioned and 30 s acid etching; group L60, laser prepared, laser conditioned and 60 s acid etching; group L90, laser prepared, laser conditioned and 90 s acid etching. A plot of composite resin was bonded onto each exposed dentine and then tested for tensile bond strength. The values obtained were statistically analysed by analysis of variance (ANOVA) coupled with the Tukey-Kramer test at the 95 % level. A 90 s acid etching before bonding showed the best bonding value (P < 0.05) when compared with all the other groups including the control group. There is no significance difference between other groups, nor within each group and the control group. There was a significant increase in tensile bond strength of the samples acid etched for 90 s.

Several studies in the literature have previously shown that the bond strength of a composite bonded to dentin is almost equivalent as when dentin is prepared by either bur or Er:YAG laser. The aim of this preliminary study is to assess the hypothesis that dentin conditioning at low fluency by means of Er:YAG laser can improve the value of adhesion of composites resin to dentin. Sixty surfaces of caries-free human third molars extracted for orthodontic purposes were randomly divided into five groups of 12 teeth. The bur group was the control, prepared using bur, group L was prepared using Er:YAG 200 mJ, SSP (50 µs), 20 Hz, 15 seconds of sweeping, for groups L80, L100, L120, they were prepared first, with the same parameters of the group L 200, and then they received a conditioning, which is, respectively, 15 s of irradiations at: 80 mJ (SSP, 10 Hz), 100 mJ (SSP, 10 Hz), and 120 mJ (SSP, 10 Hz). All samples were restored in a single-component adhesive system: Xenon (DENTSPLY), and ceramX (DENTSPLY) as the resin composite. The specimens were submitted to tensile bond strength test using a universal testing machine. Data were submitted to statistical analysis using ANOVA coupled to a Tukey-Kramer test at the 95% level. The mean values in MPa were 33.3 for group B, 36.73 for group L 200, 41.7 for group L80, 37.9 for group L100, and 39.1 for group L120. Our results showed that dentin conditioning at a low fluency of 12.58 J/cm(2) per pulse, with 80 mJ output energy and 50-µs pulse duration can significantly improve tensile bond strength of a composite bonded to Er:YAG laser-prepared dentine.

Several studies in the literature have previously shown that the bond strength of a composite bonded to dentin is almost equivalent as when dentin is prepared by either bur or Er:YAG laser. The aim of this preliminary study is to assess the hypothesis that dentin conditioning at low fluency by means of Er:YAG laser can improve the value of adhesion of composites resin to dentin. Sixty surfaces of caries-free human third molars extracted for orthodontic purposes were randomly divided into five groups of 12 teeth. The bur group was the control, prepared using bur, group L was prepared using Er:YAG 200 mJ, SSP (50 µs), 20 Hz, 15 seconds of sweeping, for groups L80, L100, L120, they were prepared first, with the same parameters of the group L 200, and then they received a conditioning, which is, respectively, 15 s of irradiations at: 80 mJ (SSP, 10 Hz), 100 mJ (SSP, 10 Hz), and 120 mJ (SSP, 10 Hz). All samples were restored in a single-component adhesive system: Xenon (DENTSPLY), and ceramX (DENTSPLY) as the resin composite. The specimens were submitted to tensile bond strength test using a universal testing machine. Data were submitted to statistical analysis using ANOVA coupled to a Tukey-Kramer test at the 95% level. The mean values in MPa were 33.3 for group B, 36.73 for group L 200, 41.7 for group L80, 37.9 for group L100, and 39.1 for group L120. Our results showed that dentin conditioning at a low fluency of 12.58 J/cm(2) per pulse, with 80 mJ output energy and 50-µs pulse duration can significantly improve tensile bond strength of a composite bonded to Er:YAG laser-prepared dentine.