Search

Corrosion poses a significant threat to structural integrity, which results in surface degradation, mechanical failure, environmental pollution, and loss of life. Steel, a primary material used in various industries, has been subject to numerous corrosion prevention methods throughout history [1]. Protective coating has proven effective in extending steel structures' service life [2, 3]. Alloying, another essential methodology, involves adding alloying elements such as Cu, Cr, Ni, P, Si, and Mn to bulk steel. When exposed to a corrosive environment, these elements help form a protective passivation layer on the surface, thus protecting the material underneath [4]. Both protective coatings and alloying have their advantages and limitations. Applying protective coatings is time-consuming and expensive, requiring complex procedures for surface preparation and application [5, 6]. Alloying, on the other hand, involves adding expensive elements to the bulk material when only the surface is exposed to harsh environments. Moreover, alloying could alter the material’s mechanical properties of the bulk material, which is not always desirable. Surface alloying is an exciting technique to alter steel’s surface properties without compromising the properties of the bulk material. It has been implemented for several different purposes, such as enhancing surface hardness, scratch resistance, corrosion resistance, etc. Although the current surface alloying techniques successfully reduce the material cost, their application cost is significantly high as specialized equipment is required to perform complex procedures.

A unique apparatus has been developed to study velocity effects on corrosion processes, and has been used initially to expose single metals and galvanic couples of some common marine structural materials in synthetic seawater electrolyte, under controlled hydrodynamic conditions at various relative velocities. The sample-holder in the apparatus has a standard foil profile, with a turbulence trip wire at the leading edge. Direct determinations of turbulence intensity, boundary layer thickness, and surface shear stress were made at various velocities, enabling correlations of hydrodynamic models with electrochemical data and other observations of corrosion behavior. The effects of velocity and potential distribution on average corrosion rates, and on the mode and distribution of corrosive attack and corrosion products, have been studied. (Author)

Tato diplomová práce je zaměřena na tavení slitin na bázi Cu-Ni a výrobu odlitků z těchto slitin. Teoretická část práce zahrnuje seznámení se slitinami na bázi Cu-Ni včetně jejich vlastností a aplikací. V teoretické části jsou také popsány základní metody odplyňování a dezoxidace taveniny Cu-Ni a v jejím závěru je popsána slévárenská technologie výroby odlitků z Cu-Ni do pískových forem. V praktické části byly provedeny dva navrhnuté způsoby vedení tavby pro zvolenou slitinu mědiniklu (Cu-Ni) a monelu (Ni-Cu). Z těchto taveb byly vyrobeny odlitky zkušebního vzorku, odlitky pouzder a odlitky lopatek. Odlitky zkušebních vzorků a pouzder byly vyrobeny pomocí pískových forem a odlitky lopatek pomocí skořepinových forem. Dle vnitřní jakosti těchto odlitků byly vyhodnoceny navrhnuté způsoby vedení tavby. Mimo vnitřní jakosti odlitků bylo vyhodnoceno i chemické složení, mikrostruktura a mechanické vlastnosti., This master thesis is focused on melting of Cu-Ni based alloys and production of castings from these alloys. The theoretical part includes introduction of Cu-Ni based alloys and their properties and application. At the end of this part is production foundry technology of Cu-Ni alloys described. In the practical part two proposed melt controls for cupronickel (Cu-Ni) and for monel (Ni-Cu) have been performed. From these melts trial castings, castings of blades and bearings have been produced. The trial casting and the casting of bearing have been produced by using sand moulds and the casting of blade by using ceramic shell. According to internall quality of produced castings the performed melt controls have been evaluated. In addition to the internal quality of the castings, the chemical composition, microstructure and mechanical properties were evaluated.

Tato diplomová práce je zaměřena na tavení slitin na bázi Cu-Ni a výrobu odlitků z těchto slitin. Teoretická část práce zahrnuje seznámení se slitinami na bázi Cu-Ni včetně jejich vlastností a aplikací. V teoretické části jsou také popsány základní metody odplyňování a dezoxidace taveniny Cu-Ni a v jejím závěru je popsána slévárenská technologie výroby odlitků z Cu-Ni do pískových forem. V praktické části byly provedeny dva navrhnuté způsoby vedení tavby pro zvolenou slitinu mědiniklu (Cu-Ni) a monelu (Ni-Cu). Z těchto taveb byly vyrobeny odlitky zkušebního vzorku, odlitky pouzder a odlitky lopatek. Odlitky zkušebních vzorků a pouzder byly vyrobeny pomocí pískových forem a odlitky lopatek pomocí skořepinových forem. Dle vnitřní jakosti těchto odlitků byly vyhodnoceny navrhnuté způsoby vedení tavby. Mimo vnitřní jakosti odlitků bylo vyhodnoceno i chemické složení, mikrostruktura a mechanické vlastnosti., This master thesis is focused on melting of Cu-Ni based alloys and production of castings from these alloys. The theoretical part includes introduction of Cu-Ni based alloys and their properties and application. At the end of this part is production foundry technology of Cu-Ni alloys described. In the practical part two proposed melt controls for cupronickel (Cu-Ni) and for monel (Ni-Cu) have been performed. From these melts trial castings, castings of blades and bearings have been produced. The trial casting and the casting of bearing have been produced by using sand moulds and the casting of blade by using ceramic shell. According to internall quality of produced castings the performed melt controls have been evaluated. In addition to the internal quality of the castings, the chemical composition, microstructure and mechanical properties were evaluated.

Tato diplomová práce je zaměřena na tavení slitin na bázi Cu-Ni a výrobu odlitků z těchto slitin. Teoretická část práce zahrnuje seznámení se slitinami na bázi Cu-Ni včetně jejich vlastností a aplikací. V teoretické části jsou také popsány základní metody odplyňování a dezoxidace taveniny Cu-Ni a v jejím závěru je popsána slévárenská technologie výroby odlitků z Cu-Ni do pískových forem. V praktické části byly provedeny dva navrhnuté způsoby vedení tavby pro zvolenou slitinu mědiniklu (Cu-Ni) a monelu (Ni-Cu). Z těchto taveb byly vyrobeny odlitky zkušebního vzorku, odlitky pouzder a odlitky lopatek. Odlitky zkušebních vzorků a pouzder byly vyrobeny pomocí pískových forem a odlitky lopatek pomocí skořepinových forem. Dle vnitřní jakosti těchto odlitků byly vyhodnoceny navrhnuté způsoby vedení tavby. Mimo vnitřní jakosti odlitků bylo vyhodnoceno i chemické složení, mikrostruktura a mechanické vlastnosti., This master thesis is focused on melting of Cu-Ni based alloys and production of castings from these alloys. The theoretical part includes introduction of Cu-Ni based alloys and their properties and application. At the end of this part is production foundry technology of Cu-Ni alloys described. In the practical part two proposed melt controls for cupronickel (Cu-Ni) and for monel (Ni-Cu) have been performed. From these melts trial castings, castings of blades and bearings have been produced. The trial casting and the casting of bearing have been produced by using sand moulds and the casting of blade by using ceramic shell. According to internall quality of produced castings the performed melt controls have been evaluated. In addition to the internal quality of the castings, the chemical composition, microstructure and mechanical properties were evaluated.

Tato diplomová práce je zaměřena na tavení slitin na bázi Cu-Ni a výrobu odlitků z těchto slitin. Teoretická část práce zahrnuje seznámení se slitinami na bázi Cu-Ni včetně jejich vlastností a aplikací. V teoretické části jsou také popsány základní metody odplyňování a dezoxidace taveniny Cu-Ni a v jejím závěru je popsána slévárenská technologie výroby odlitků z Cu-Ni do pískových forem. V praktické části byly provedeny dva navrhnuté způsoby vedení tavby pro zvolenou slitinu mědiniklu (Cu-Ni) a monelu (Ni-Cu). Z těchto taveb byly vyrobeny odlitky zkušebního vzorku, odlitky pouzder a odlitky lopatek. Odlitky zkušebních vzorků a pouzder byly vyrobeny pomocí pískových forem a odlitky lopatek pomocí skořepinových forem. Dle vnitřní jakosti těchto odlitků byly vyhodnoceny navrhnuté způsoby vedení tavby. Mimo vnitřní jakosti odlitků bylo vyhodnoceno i chemické složení, mikrostruktura a mechanické vlastnosti., This master thesis is focused on melting of Cu-Ni based alloys and production of castings from these alloys. The theoretical part includes introduction of Cu-Ni based alloys and their properties and application. At the end of this part is production foundry technology of Cu-Ni alloys described. In the practical part two proposed melt controls for cupronickel (Cu-Ni) and for monel (Ni-Cu) have been performed. From these melts trial castings, castings of blades and bearings have been produced. The trial casting and the casting of bearing have been produced by using sand moulds and the casting of blade by using ceramic shell. According to internall quality of produced castings the performed melt controls have been evaluated. In addition to the internal quality of the castings, the chemical composition, microstructure and mechanical properties were evaluated.

Tato diplomová práce je zaměřena na tavení slitin na bázi Cu-Ni a výrobu odlitků z těchto slitin. Teoretická část práce zahrnuje seznámení se slitinami na bázi Cu-Ni včetně jejich vlastností a aplikací. V teoretické části jsou také popsány základní metody odplyňování a dezoxidace taveniny Cu-Ni a v jejím závěru je popsána slévárenská technologie výroby odlitků z Cu-Ni do pískových forem. V praktické části byly provedeny dva navrhnuté způsoby vedení tavby pro zvolenou slitinu mědiniklu (Cu-Ni) a monelu (Ni-Cu). Z těchto taveb byly vyrobeny odlitky zkušebního vzorku, odlitky pouzder a odlitky lopatek. Odlitky zkušebních vzorků a pouzder byly vyrobeny pomocí pískových forem a odlitky lopatek pomocí skořepinových forem. Dle vnitřní jakosti těchto odlitků byly vyhodnoceny navrhnuté způsoby vedení tavby. Mimo vnitřní jakosti odlitků bylo vyhodnoceno i chemické složení, mikrostruktura a mechanické vlastnosti., This master thesis is focused on melting of Cu-Ni based alloys and production of castings from these alloys. The theoretical part includes introduction of Cu-Ni based alloys and their properties and application. At the end of this part is production foundry technology of Cu-Ni alloys described. In the practical part two proposed melt controls for cupronickel (Cu-Ni) and for monel (Ni-Cu) have been performed. From these melts trial castings, castings of blades and bearings have been produced. The trial casting and the casting of bearing have been produced by using sand moulds and the casting of blade by using ceramic shell. According to internall quality of produced castings the performed melt controls have been evaluated. In addition to the internal quality of the castings, the chemical composition, microstructure and mechanical properties were evaluated.

Tato diplomová práce je zaměřena na tavení slitin na bázi Cu-Ni a výrobu odlitků z těchto slitin. Teoretická část práce zahrnuje seznámení se slitinami na bázi Cu-Ni včetně jejich vlastností a aplikací. V teoretické části jsou také popsány základní metody odplyňování a dezoxidace taveniny Cu-Ni a v jejím závěru je popsána slévárenská technologie výroby odlitků z Cu-Ni do pískových forem. V praktické části byly provedeny dva navrhnuté způsoby vedení tavby pro zvolenou slitinu mědiniklu (Cu-Ni) a monelu (Ni-Cu). Z těchto taveb byly vyrobeny odlitky zkušebního vzorku, odlitky pouzder a odlitky lopatek. Odlitky zkušebních vzorků a pouzder byly vyrobeny pomocí pískových forem a odlitky lopatek pomocí skořepinových forem. Dle vnitřní jakosti těchto odlitků byly vyhodnoceny navrhnuté způsoby vedení tavby. Mimo vnitřní jakosti odlitků bylo vyhodnoceno i chemické složení, mikrostruktura a mechanické vlastnosti., This master thesis is focused on melting of Cu-Ni based alloys and production of castings from these alloys. The theoretical part includes introduction of Cu-Ni based alloys and their properties and application. At the end of this part is production foundry technology of Cu-Ni alloys described. In the practical part two proposed melt controls for cupronickel (Cu-Ni) and for monel (Ni-Cu) have been performed. From these melts trial castings, castings of blades and bearings have been produced. The trial casting and the casting of bearing have been produced by using sand moulds and the casting of blade by using ceramic shell. According to internall quality of produced castings the performed melt controls have been evaluated. In addition to the internal quality of the castings, the chemical composition, microstructure and mechanical properties were evaluated.