1. Prevention of Corrosion in Structural Aluminum Alloys
- Author
-
ARIZONA STATE UNIV TEMPE DEPT OF MECHANICAL AND AEROSPACE ENGINEERING, Sieradzki, K., Carpenter, R. W., Newman, R. C., Dimitrov, N., Leclere, T. J., ARIZONA STATE UNIV TEMPE DEPT OF MECHANICAL AND AEROSPACE ENGINEERING, Sieradzki, K., Carpenter, R. W., Newman, R. C., Dimitrov, N., and Leclere, T. J.
- Abstract
We examined the general phenomenology associated with the corrosion of Al Alloy 2024-T3. Copper redistribution is controlled by S-phase dealloying and matrix dealloying. Matrix dealloying of aluminum occurs owing to the increased pH that develops at the alloy/electrolyte interface owing to oxygen reduction. We summarize results of a detailed investigation aimed at determining the mechanism and magnitude of the oxygen diffusion limited current density during corrosion of Al Atloy 2024-T3. Our results show that oxygen reduction occurs via the standard 4-electron mechanism and that the oxygen diffusion - limited current density has a value of approx. 25 uA cm(-2)., Original contains color plates: All DTIC reproductions will be in black and white.
- Published
- 2002