To enhance the friction and wear performance of cemented carbide, textured microholes were machined on micro Electron Discharge Machining (EDM) on the tool rake face, and Calcium Fluoride (CaF₂) powders were burnished into the microholes. The friction and wear characteristics of the microhole-textured tool filled with CaF₂ were investigated using sliding friction tests and dry cutting tests. Results exhibited that the working temperature could affect the tribological performance of the microhole-textured tool filled with CaF₂ due to the temperature-sensitive nature of CaF₂. There is no obvious lubrication effect for the textured tool filled with CaF₂ at room temperature, while it was shown to be more effective in improving tribological property at a cutting speed of higher than 100 m/min with a corresponding to cutting temperature of 450 °C. The possible mechanisms for the microhole-textured tool filled with CaF₂ were discussed and established.

In order to enhance the tribological performance of YT14 carbide, pure Zr coating was deposited on the substrate surface using a multi-arc ion plating method. The surface topography, adhesion strength, thickness, and micro-hardness of the Zr coating were tested. Dry sliding friction experiments against a 40Cr hardened steel ring were conducted with Zr-coated carbides and traditional ones. The average coefficients of friction were measured and compared. The wear characteristics of the samples were examined by scanning electron microscope (SEM) and energy dispersive X-ray analysis (EDX). The test results indicated that the Zr coating deposited on the carbide surface exhibited excellent adhesive strength and lower hardness. The average friction coefficient of Zr coated carbide decreased by 20%⁻30% in comparison with that of the uncoated one. The Zr coated carbide could reduce the adhesive wear compared with the uncoated one, and the main tribological degradation mechanisms of the coating were abrasive wear, coating flaking and delamination., Competing Interests: The authors declare no conflict of interest.