Search

The objective of this study is to examine the adsorption behavior of Sumifix Brilliant Orange 3R textile dye from aqueous solution on smectite sample, an abundant Amazon clay. The original smectite clay mineral has been collected from Amazon region, Brazil. The compound 2-aminomethylpyridine was anchored onto smectite surface by heterogeneous route. The ability of these materials to remove the Sumifix Brilliant Orange 3R textile dye from aqueous solution was followed by a series of adsorption isotherms, using a batchwise process. The maximum number of moles adsorbed was determined to be 1.26 and 2.07 mmol g(-1) for natural and modified clay samples, respectively. The energetic effects caused by dye cations adsorption were determined through calorimetric titrations. Thermodynamics indicated the existence of favorable conditions for such dye-nitrogen interactions., (Copyright © 2010. Published by Elsevier B.V.)

The synthetic imogolite sample was used for organofunctionalization process with 2-mercaptothiazoline (MTZ). The compound 2-mercaptothiazoline was anchored onto imogolite surface by heterogeneous route. Due to the increment of basic centers attached to the pendant chains the dye adsorption capability of the final chelating material, was found to be higher than is precursor. The ability of these materials to remove methylene blue from aqueous solution was followed by a series of adsorption isotherms at room temperature and pH 4.0. The maximum number of moles adsorbed was determined to be 40.32×10(-2) and 65.13×10(-2) mmol g(-1) for IMO and IMO(MTZ), respectively. The energetic effects caused by dye cations adsorption were determined through calorimetric titrations. Thermodynamics indicated the existence of favorable conditions for such methylene blue-nitrogen and sulfur interactions., (Copyright © 2010. Published by Elsevier B.V.)

The compound N-[3-(trimethoxysilyl)propyl]diethylenetriamine (MPDET) was anchored onto Amazon kaolinite surface (KLT) by heterogeneous route. The modified and natural kaolinite clay samples were characterized by transmission electron microscopy (TEM), scanning electron microscopic (SEM), N(2) adsorption, powder X-ray diffraction, thermal analysis, ion exchange capacities, and nuclear magnetic nuclei of (29)Si and (13)C. The well-defined peaks obtained in the (13)C NMR spectrum in the 5.0-62.1 ppm region confirmed the attachment of organic functional groups as pendant chains bonded into the porous clay. The adsorption of uranyl on natural (KLT) and modified (KLT(MPDET)) kaolinite clays was investigated as a function of the solution pH, metal concentration, temperature, and ionic strength. The ability of these materials to remove U(VI) from aqueous solution was followed by a series of adsorption isotherms adjusted to a Sips equation at room temperature and pH 4.0. The maximum number of moles adsorbed was determined to be 8.37 x 10(-3) and 13.87 x 10(-3) mmol g(-1) for KLT and KLT(MPDET) at 298 K, respectively. The energetic effects (Delta(int)H, Delta(int)G, and Delta(int)S) caused by metal cations adsorption were determined through calorimetric titrations., (Copyright 2010. Published by Elsevier B.V.)

The original sepiolite clay mineral has been collected from Amazon region, Brazil. The compound 2-aminomethylpyridine (AMP) was anchored onto Amazon sepiolite surface by heterogeneous route. The natural (SPT) and modified (SPT(AMP)) sepiolite samples were characterized by elemental analysis, SEM, N(2) adsorption, and nuclear magnetic nuclei of (29)Si and (13)C. The well-defined peaks obtained in the (13)C NMR spectrum in the 0-160 ppm region confirmed the attachment of organic functional groups as pendant chains bonded into the porous clay. The ability of these materials to remove As(V) from aqueous solution was followed by a series of adsorption isotherms at room temperature and pH 4.0. The maximum number of moles adsorbed was determined to be 7.26×10(-2) and 11.70×10(-2) mmol g(-1) for SPT and SPT(AMP), respectively. In order to evaluate the clay samples as adsorbents in dynamic system, a glass column was fulfilled with clay samples (1.0 g) and it was fed with 2.0×10(-2) mmol dm(-3) As(V) at pH 4.0. The energetic effects caused by metal cations adsorption were determined through calorimetric titrations. Thermodynamics indicated the existence of favorable conditions for such As(V)-nitrogen interactions., (Copyright © 2010. Published by Elsevier Inc.)

A Hectorite sample (H) has been chemically modified with N-propyldiethylenetrimethoxysilane and bis[3-(triethoxysilyl)propyl]tetrasulfide. The resulting materials (H(3TPT) and H(NPTM)) have been characterized through elemental analysis, X-ray diffractometry, carbon nuclear magnetic resonance in the solid state, textural analysis, and thermogravimetric analysis. The adsorption experiments were performed under batch process with pH, ionic strength, contact time, and uranyl concentration as variables. The attached basic centers adsorbed uranyl cation to give maxima adsorption capacity of 5.55+/-0.21, 14.86+/-0.05, and 18.99+/-0.05 x 10(-3) mmol g(-1) for H, H(3TPT), and H(NPTM), respectively. From calorimetric determinations the quantitative thermal effects for UO(2)(2+)/center interactions gave exothermic enthalpy (Delta(int)H=-6.90 to -7.88 kJ mol(-1)), negative Gibbs free energy (Delta(int)G=-22.34 to -24.56 kJ mol(-1)), and positive entropy (Delta(int)S=51.80-56.00 JK(-1)mol(-1)). These thermodynamic data confirmed the energetically favorable condition of such interaction solid/liquid for all systems., (Copyright 2009. Published by Elsevier Ltd.)

A hectorite (H) clay sample has been modified with 2-mercaptobenzimidazole (MBI) using homogeneous and heterogeneous routes. Both modification methodologies resulted in similar products, named H(HOM) and H(HET), respectively. These materials were characterized by CO(2) gas adsorption, elemental analysis, nuclear magnetic nuclei of carbon-13 and silicon-29. The effect of two variables (contact time and metal concentration) has been studied using batch technique at room temperature and pH 2.0. After achieving the best conditions for Cr(VI) adsorption, isotherms of this adsorbate on using the chosen adsorbents were obtained, which were fitted to non-linear Sips isotherm model. The maximum number of moles adsorbed was determined to be 11.63, 12.85 and 14.01 mmol g(-1) for H, H(HOM) and H(HET), respectively, reflecting the maximum adsorption order of H(HET)>H(HOM)>H. The energetic effects (Delta(int)H degrees , Delta(int)G degrees and Delta(int)S degrees ) caused by chromium ion adsorption were determined through calorimetric titrations.

Natural montmorillonite (M) and synthetic kanemite (K) have been functionalized with 1,4-bis(3-aminopropyl)piperazine reacted with methylacrylate to yield new inorganic-organic chelating materials. The original and modified materials were characterized by X-ray diffractometry, textural analysis, SEM and nuclear magnetic nuclei of carbon-13 and silicon-29. The chemically modified clay samples (M-APPMA and K-APPMA) showed modification of its physical-chemical properties including: specific area 45.0m(2)g(-1) (M) to 978.8 m(2)g(-1) (M-APPMA) and 23.5m(2)g(-1) (K) to 898.9 m(2)g(-1) (K-APPMA). The ability of these materials to remove thorium(IV), uranyl(VI) and europium(III) from aqueous solution was followed by a series of adsorption isotherms, which were fitted to non-linear Sips adsorption isotherm model. To achieve the best adsorption conditions the influence of pH and variation of metal concentration were investigated. The energetic effects (Delta(int)H degrees , Delta(int)G degrees and Delta(int)S degrees ) caused by metal ions adsorption were determined through calorimetric titrations.

The compound 5-amino-1,3,4-thiadiazole-thiol (ATT) was anchored onto an Amazon kanemite surface (K) by homogeneous and heterogeneous routes. Both kanemite modification methodologies resulted in similar products, named K(CTT) and K(ATT), respectively. The modified and natural kanemite samples were characterized by textural analysis, FT-Raman, and nuclear magnetic nuclei of (29)Si and (13)C. Elemental analysis proved that the matrix K(ATT) presented a higher ATT immobilization than K(CTT), with values 1.42 and 1.38 mmol g(-1), respectively. NMR and FT-Raman confirmed the immobilization of ATT on both surfaces. The ability of these materials to remove thorium(IV) from aqueous solution was followed by a series of adsorption isotherms adjusted to a Sips equation at room temperature and pH 4.0. The maximum number of moles adsorbed was determined to be 7.48x10(-3), 9.82x10(-3), and 12.94x10(-3) mmol g(-1) for K, K(CTT), and K(ATT), respectively. The energetic effects (Delta(int)H(o), Delta(int)G(o), and Delta(int)S(o)) caused by metal cation adsorption were determined through calorimetric titrations.

Diquite (D) and bentonite (B) mineral samples from the Amazon region, Brazil, were modified by MTTZ derivative (5-mercapto-1-methyltetrazole) using heterogeneous route. These materials were characterized by textural and elemental analysis, transmission electron microscopy (TEM), power X-ray diffraction and (13)C NMR spectroscopy. The chemically modified clay (D(MTTZ) and B(MTTZ)) samples showed modification of its physical-chemical properties including: specific area 41.4 (B) to 398.5m(2)g(-1) (B(MTTZ)) and 25.0 (D) to 178.8m(2)g(-1) (D(MTTZ)). The adsorption experiments performed under batch process with Th(IV) concentration, pH and contact time as variables. The ability of these materials to remove thorium from aqueous solution was followed by a series of adsorption isotherms adjusted to a Sips equation at room temperature and pH 2.0, with variable concentration of Th(IV). The maximum number of moles adsorbed was determined to be 10.45 x 10(-2) and 12.76 x 10(-2)mmol g(-1) for D(MTTZ) and B(MTTZ), respectively. The energetic effects (Delta(int)H degrees , Delta(int)G degrees and Delta(int)S degrees ) caused by thorium cation adsorption were determined through calorimetric titrations.

An analogue of heulandite was synthesized by using inorganic salts as a source for silicon and aluminum in the hydrothermal synthesis of the material. The resulting solid was modified by organofunctionalization with 1,4-bis(3-aminopropyl)piperazine and subsequent reaction with methylacrylate in a heterogeneous route. The original (HEU) and modified silicate (HEU(APPMA)) samples were characterized by textural analysis, SEM, and nuclear magnetic nuclei of (29)Si and (13)C. The chemically modified silicate sample showed modification of its physical-chemical properties including specific area 459.0-978.8 m(2) g(-1). The ability of this material to remove nickel(II), cobalt(II), and copper(II) from aqueous solutions was followed by a series of adsorption isotherms adjusted to a Sips equation. The quick adsorption process reached the equilibrium before 10, 15, and 20 min for Cu(II), Ni(II), and Co(II), respectively, with maximum adsorptions at pH 4.0. Based on the capacity of adsorption of HEU(APPMA) to interact with metal ions, the following results were obtained 12.9, 9.8, and 7.5 mmol g(-1) for Cu(II), Ni(II), and Co(II), respectively, reflecting a maximum adsorption order of Cu(II)>Ni(II)>Co(II). The energetic effects caused by metal cation adsorption were determined through calorimetric titrations.