Search

In the present study, the ability of a coating of zinc oxide (ZnO) powder to improve the fire-safety of wood exposed to radiative heat flux was examined, focusing on the ignition time of the wood. To test ZnO's efficiency on the wood substrate, two different amounts of ZnO (0.5 and 1 g ZnO per dm 2 ) were applied to the wood surface and exposed to radiative heat from a cone calorimeter wherein a pristine piece of wood with no ZnO treatment was taken as control. The experiments were conducted at three different irradiation levels i.e., 20, 35, and 50 kWm -2 . The results showed that applying ZnO on the surface of the wood significantly increased the ignition time (TTI). For the three different heat fluxes, using 0.5 g ZnO per dm 2 coating on the wood surface increased the TTI by 26-33 %. Furthermore, the application of 1 g of ZnO per dm 2 generated a TTI increment of 37-40 %. All three irradiation levels showed similar trends in TTI. The micrographs taken before and after combustion showed no significant disparity in the morphology of ZnO. The agglomerated ZnO particles on the wood surface remained intact after combustion. This study demonstrates a facile method of using ZnO to delay the ignition of wood. This could potentially impart fire-safety to wooden structures/façades in wildland-urban interfaces and elsewhere by reducing flame spread., Competing Interests: Declaration of competing interest All authors declare no financial/commercial conflicts of interest, with any parties., (Copyright © 2023 The Authors. Published by Elsevier B.V. All rights reserved.)

Calcium silicate hydrate (C-S-H) is the main hydration product of cementitious materials, often experiencing complex stress conditions in practical applications. Therefore, reactive molecular dynamics methods were used to investigate the mechanical response of the atomistic structure of C-S-H under various uniaxial and biaxial strain conditions. The results of uniaxial simulations show that C-S-H exhibits mechanical anisotropy and tension-compression asymmetry due to its layered atomistic structure. By fitting the stress-strain data, a stress-strain relationship that accurately represents the elastoplasticity of C-S-H was developed. The biaxial yield surface obtained from biaxial simulations was ellipsoidal, again reflecting the anisotropy and asymmetry of C-S-H. Four yield criteria (von Mises, Drucker-Prager, Hill, and Liu-Huang-Stout) were further investigated, and it was found that the Liu-Huang-Stout criterion can effectively capture all the major features of the yield surface. During a uniaxial tensile process in the z direction, multi-crack propagation was observed, which was aggravated and weakened by y direction tensile and compressive strains respectively. The results of chemical bond analyses revealed that, for different strain conditions, the Ca W -O S and Ca S -O S bonds play different roles in resisting deformation.

Filled hybrid composites are widely used in various structural applications where machining is critical. Hence, it is essential to understand the performance of the fibre composites' machining behaviour. As such, a new hybrid structural composite was fabricated with redmud as filler and sisal fibre as reinforcement in polyester matrix. The composite was then tested for its drilling performance. A comprehensive drilling experiment was conducted using Taguchi L27 orthogonal array. The effect of the drill tool point angle, the cutting speed, the feed rate on thrust force, delamination, and burr formation were analysed for producing quality holes. The significance of each parameter was analysed, and the experimental outcomes revealed some important findings in the context of the drilling behaviour of sisal fibre/polyester composites with redmud as a filler. Spindle speed contributed 39% in affecting the thrust force, while the feed rate had the maximum influence of ca. 38% in affecting delamination.

The present study is aimed at investigating the effect of hybridisation on Kevlar/E-Glass based epoxy composite laminate structures. Composites with 3 mm thickness and 16 layers of fibre (14 layers of E-glass centred and 2 outer layers of Kevlar) were fabricated using compression moulding technique. The fibre orientation of the Kevlar layers had 3 variations (0, 45 and 60°), whereas the E-glass fibre layers were maintained at 0° orientation. Tensile, flexural, impact (Charpy and Izod), interlaminar shear strength and ballistic impact tests were conducted. The ballistic test was performed using a gas gun with spherical hard body projectiles at the projectile velocity of 170 m/s. The pre- and post-impact velocities of the projectiles were measured using a high-speed camera. The energy absorbed by the composite laminates was further reported during the ballistic test, and a computerised tomographic scan was used to analyse the impact damage. The composites with 45° fibre orientation of Kevlar fibres showed better tensile strength, flexural strength, Charpy impact strength, and energy absorption. The energy absorbed by the composites with 45° fibre orientation was 58.68 J, which was 14% and 22% higher than the 0° and 60° oriented composites.

Functionalized polyacrylonitrile (PAN) nanofibers were used in the present investigation to enhance the fracture behavior of carbon epoxy composite in order to prevent delamination if any crack propagates in the resin rich area. The main intent of this investigation was to analyze the efficiency of PAN nanofiber as a reinforcing agent for the carbon fiber-based epoxy structural composite. The composites were fabricated with stacked unidirectional carbon fibers and the PAN powder was functionalized with glycidyl methacrylate (GMA) and then used as reinforcement. The fabricated composites' fracture behavior was analyzed through a double cantilever beam test and the energy release rate of the composites was investigated. The neat PAN and functionalized PAN-reinforced samples had an 18% and a 50% increase in fracture energy, respectively, compared to the control composite. In addition, the samples reinforced with functionalized PAN nanofibers had 27% higher interlaminar strength compared to neat PAN-reinforced composite, implying more efficient stress transformation as well as stress distribution from the matrix phase (resin-rich area) to the reinforcement phase (carbon/phase) of the composites. The enhancement of fracture toughness provides an opportunity to alleviate the prevalent issues in laminated composites for structural operations and facilitate their adoption in industries for critical applications.

Natural fibre-based composites are replacing traditional materials in a wide range of structural applications that are used in different environments. Natural fibres suffer from thermal shocks, which affects the use of these composites in cold environment. Considering these, a goal was set in the present research to investigate the impact of cryogenic conditions on natural fibre composites. Composites were developed using polyester as matrix and jute-fibre and waste Teak saw-dust as reinforcement and filler, respectively. The effects of six parameters, viz., density of saw-dust, weight ratio of saw-dust, grade of woven-jute, number of jute layers, duration of cryogenic treatment of composite and duration of alkaline treatment of fibres on the mechanical properties of the composite was evaluated with an objective to maximise hardness, tensile, impact and flexural strengths. Taguchi method was used to design the experiments and response-surface methodology was used to model, predict and plot interactive surface plots. Results indicated that the duration of cryogenic treatment had a significant effect on mechanical properties, which was better only up to 60 min. The models were found to be statistically significant. The study concluded that saw-dust of density 300 kg/m 3 used as a filler with a weight ratio of 13 wt.% and a reinforcement of a single layer of woven-jute-fibre mat of grade 250 gsm subjected to alkaline treatment for 4 h in a composite that has undergone 45 min of cryogenic treatment presented an improvement of 64% in impact strength, ca. 21% in flexural strength, ca. 158% in tensile strength and ca. 28% in hardness.

The global coronavirus disease 2019 (COVID-19) pandemic has rapidly increased the demand for facemasks as a measure to reduce the rapid spread of the pathogen. Throughout the pandemic, some countries such as Italy had a monthly demand of ca. 90 million facemasks. Domestic mask manufacturers are capable of manufacturing 8 million masks each week, although the demand was 40 million per week during March 2020. This dramatic increase has contributed to a spike in the generation of facemask waste. Facemasks are often manufactured with synthetic materials that are non-biodegradable, and their increased usage and improper disposal are raising environmental concerns. Consequently, there is a strong interest for developing biodegradable facemasks made with for example, renewable nanofibres. A range of natural polymer-based nanofibres has been studied for their potential to be used in air filter applications. This review article examines potential natural polymer-based nanofibres along with their filtration and antimicrobial capabilities for developing biodegradable facemask that will promote a cleaner production., (© 2021 The Authors. Journal of Applied Polymer Science published by Wiley Periodicals LLC.)

This investigation is carried out to understand the effects of water absorption on the mechanical properties of hybrid phenol formaldehyde (PF) composite fabricated with Areca Fine Fibres (AFFs) and Calotropis Gigantea Fibre (CGF). Hybrid CGF/AFF/PF composites were manufactured using the hand layup technique at varying weight percentages of fibre reinforcement (25, 35 and 45%). Hybrid composite having 35 wt.% showed better mechanical properties (tensile strength ca. 59 MPa, flexural strength ca. 73 MPa and impact strength 1.43 kJ/m 2 ) under wet and dry conditions as compared to the other hybrid composites. In general, the inclusion of the fibres enhanced the mechanical properties of neat PF. Increase in the fibre content increased the water absorption, however, after 120 h of immersion, all the composites attained an equilibrium state.