Herein we demonstrate the specifics of using the positron annihilation lifetime spectroscopy (PALS) method for the study of free volume changes in functional ceramic materials. Choosing technological modification of nanostructured MgAl 2 O 4 spinel as an example, we show that for ceramics with well-developed porosity positron annihilation is revealed through two channels: positron trapping channel and ortho-positronium decay. Positron trapping in free-volume defects is described by the second component of spectra and ortho-positronium decay process by single or multiple components, depending on how well porosity is developed and on the experimental configuration. When using proposed positron annihilation lifetime spectroscopy approaches, three components are the most suitable fit in the case of MgAl 2 O 4 ceramics. In the analysis of the second component, it is shown that technological modification (increasing sintering temperature) leads to volume shrinking and decreases the number of defect-related voids. This process is also accompanied by the decrease of the size of nanopores (described by the third component), while the overall number of nanopores is not affected. The approach to the analysis of positron annihilation lifetime spectra presented here can be applied to a wide range of functional nanomaterials with pronounced porosity.

Structural transformations caused by coarse-grained powdering and fine-grained mechanochemical milling in a dry mode were probed in high-temperature modification of tetra-arsenic tetra-sulfide known as β-As4S4. In respect to X-ray diffraction analysis, the characteristic sizes of β-As4S4 crystallites in these coarse- and fine-grained powdered pellets were 90 and 40 nm, respectively. Positron annihilation lifetime spectroscopy was employed to characterize transformations occurred in free-volume structure of these nanoarsenicals. Experimentally measured positron lifetime spectra were parameterized in respect to three- or two-term fitting procedures and respectively compared with those accumulated for single crystalline realgar α-As4S4 polymorph. The effect of coarse-grained powdering was found to result in generation of large amount of positron and positronium Ps trapping sites inside arsenicals in addition to existing ones. In fine-grained powdered β-As4S4 pellets, the positron trapping sites with characteristic free volumes close to bi- and tri-atomic vacancies were evidently dominated. These defects were supposed to originate from grain boundary regions and interfacial free volumes near aggregated β-As4S4 crystallites. Thus, the cumulative production of different positron traps with lifetimes close to defect-related lifetimes in realgar α-As4S4 polymorph was detected in fine-grained milled samples.