Effects of tetrahydrofuran (THF) concentration on the mixed methane hydrate formation, dissociation, and stability were investigated. The experiment was conducted at 286.2 K and 6 MPa in a quiescent reactor. The presence of THF below 2.5 mol% did not show the evidence of hydrate formation. However, the concentration above 2.5 mol% enhanced the methane formation rate and the methane consumption. Increasing the THF concentration decreased the induction time as the result of the decrease in the surface tension. Moreover, the methane uptake and formation rate increased with the THF concentration due to the higher degree of hydrate nucleation. The methane recovery after the dissociation experiment showed up to 96%. Furthermore, the hydrate stability increased, and the hydrate dissociation kinetics decreased with the increase in the THF concentration. The optimum THF concentration to enhance and improve the hydrate formation kinetics and stability is its stoichiometric concentration.

Sodium dodecyl sulfate (SDS) markedly improved tetrahydrofuran (THF) - assisted methane hydrate formation. Firstly, methane hydrate formation with different THF amount, 1, 3, and 5.56 mol%, was studied. SDS with 1, 4, and 8 mM was then investigated for its roles on the methane hydrate formation with and without THF. The experiments were conducted in a quiescent condition in a fixed volume crystallizer at 8 MPa and 4°C. The results showed that almost all studied THF and SDS concentrations enhanced the methane hydrate formation kinetics and methane consumption compared to that without the promoters, except 1 mol% THF. Although, with 1 mol% THF, there were no hydrates formed for 48 hours, the addition of just 1 mM SDS surprisingly promoted the hydrate formation with a significant increased in the kinetics. This prompts the use of methane hydrate technology for natural gas storage application with minimal promoters.

Two types of mixed matrix membranes were developed by UOP in the late 1980s. The first type includes adsorbent polymers, such as silicalite-cellulose acetate (CA), NaX-CA, and AgX-CA mixed matrix membranes. The silicalite-CA has a CO(2)/H(2) selectivity of 5.15 +/- 2.2. In contrast, the CA membrane has a CO(2)/H(2) selectivity of 0.77 +/- 0.06. The second type of mixed matrix membrane is PEG-silicone rubber. The PEG-silicone rubber mixed matrix membrane has high selectivity for polar gases, such as SO(2), NH(3), and H(2)S.