Search

Osteoporotic femur fractures are the most common fragility fracture and account for approximately one million injuries per year. Local intervention by intra-marrow injection is potentially a good choice for preventing osteoporotic bone loss when the osteoporotic femoral fracture was treated. Previously, it was shown that trace element co-doped calcium phosphate (teCaP) implants could stimulate osteoporotic bone marrow mesenchymal stem cell activity in vitro and bone regeneration in femoral bone defects in osteoporotic animal models. They hypothesized that local intra-marrow injection of teCaP particles could improve bone function because the teCaP can sustain release of biologically essential inorganic minerals and improve bone remodeling in osteoporosis. The teCaP and CaP particles were synthesized in simulated body fluid with and without adding silicon, zinc and strontium ions. Female rats (8 months) were ovariectomized (OVX) or sham-operated, and then intervened in the femoral marrow space at 12 months old. Groups include: (1) saline water; (2) CaP particles; and (3) teCaP particles. After 2-3 months of intervention, the sham groups showed higher bone mineral density (MBD) in the femur, and teCaP group increased the BMD in the OVX groups. The compressive strength of the OVX-teCaP group was significantly higher than that in the OVX-CaP group. Significant differences between OVX-teCaP and OVX-CaP groups were found for bone mineral microarchitecture, bone mineral density, and trace mineral content, but not for feces composition. These results confirm the teCaP particles could suppress osteoporotic bone loss by local intramarrow injection. Therefore, this biomaterial could be used as a next-generation combination treatment for osteoporotic trauma and osteoporosis itself. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 1422-1432, 2017., (© 2017 Wiley Periodicals, Inc.)

Mechanical strength and its long-term stability of bioceramic scaffolds is still a problem to treat the osteonecrosis of the femoral head. Considering the long-term stability of diopside (DIO) ceramic but poor mechanical strength, we developed the DIO-based porous bioceramic composites via dilute magnesium substituted wollastonite reinforcing and three-dimensional (3D) printing. The experimental results showed that the secondary phase (i.e. 10% magnesium substituting calcium silicate; CSM10) could readily improve the sintering property of the bioceramic composites (DIO/CSM10- x , x  = 0-30) with increasing the CSM10 content from 0% to 30%, and the presence of the CSM10 also improved the biomimetic apatite mineralization ability in the pore struts of the scaffolds. Furthermore, the flexible strength (12.5-30 MPa) and compressive strength (14-37 MPa) of the 3D printed porous bioceramics remarkably increased with increasing CSM10 content, and the compressive strength of DIO/CSM10-30 showed a limited decay (from 37 MPa to 29 MPa) in the Tris buffer solution for a long time stage (8 weeks). These findings suggest that the new CSM10-reinforced diopside porous constructs possess excellent mechanical properties and can potentially be used to the clinic, especially for the treatment of osteonecrosis of the femoral head work as a bioceramic rod.

Tissue integration of orbital implants, following orbital enucleation treatment, represents a challenge for rapid fibrovascularization, long-time stability, anti-infection, and even induction of vascule regeneration. The objective of this study was to develop porous calcium-magnesium silicate materials, with good stability, bioactivity, and antibacterial potential as new orbital fillers. Three-dimensional (3D) diopside scaffolds (low dissolvability) were fabricated by direct ceramic ink writing assembly and then followed by one-step sintering at 1150 °C for 3 h. The pore wall of the scaffold was modified by another calcium-magnesium silicate, such as bredigite or akermanite, which dissolves quickly but shows greater angiogenic potential. These two Ca-Mg-silicates can be coated onto the pore strut, and the coating layers were observed to slowly dissolve in Tris buffer. The vascularization-favorable Cu ions, which had been doped into the bredigite or akermanite coating, could also be measured in the immersion medium. A primary angiogenic test in a panniculus carnosus muscle model in rabbit indicated that the Cu-doped bredigite and akermanite coatings were significantly beneficial for the neovascularization in the early stages. These results suggest that the diopside-based porous materials modified with functional coatings hold great potential for application in orbital reconstruction.

The regeneration and repair of damaged load-bearing segmental bones require considerable mechanical strength for the artificial implants. The ideal biomaterials should also facilitate the production of porous implants with high bioactivity desirable for stimulating new bone growth. Here we developed a new mechanically strong, highly bioactive dilute magnesium-doped wollastonite (CaSiO 3 -Mg; CSi-Mg) porous scaffold by the robocasting technique. The sintered scaffolds had interconnected pores 350 µm in size and over 50% porosity with appreciable compressive strength (>110 MPa), 5-10 times higher than those of pure CSi and β-TCP porous ceramics. Extensive in vitro and in vivo investigations revealed that such Ca-silicate bioceramic scaffolds were particularly beneficial for osteogenic cell activity and osteogenic capacity in critical size femoral bone defects. The CSi-Mg porous constructs were accompanied by an accelerated new bone growth (6-18 weeks) and a mechanically outstanding elastoplastic response to finally match the strength (10-15 MPa) of the rabbit femur host bone after 18 weeks, and the material itself experienced mild resorption and apatite-like phase transformation. In contrast, the new bone regeneration in the β-TCP scaffolds was substantially retarded after 6-12 weeks of implantation, and exhibited a low level of mechanical strength (<10 MPa) similar to the pure CSi scaffolds. These results suggest a promising application of robocast CSi-Mg scaffolds in the clinic, especially for the load-bearing bone defects.

Objective: To fabricate organic-inorganic composite tissue engineering scaffolds for reconstructing calcified cartilage layer based on three-dimensional (3D) printing technique., Methods: The scaffolds were developed by 3D-printing technique with highly bioactive calcium-magnesium silicate ultrafine particles of 1%, 3% and 5% of mass fraction, in which the organic phases were composed of type I collagen and sodium hyaluronate. The 3D-printed scaffolds were then crosslinked and solidified by alginate and CaCl₂ aerosol. The pore size and distribution of inorganic phase were observed with scanning electron microscope (SEM); the mechanical properties were tested with universal material testing machine, and the porosity of scaffolds was also measured., Results: Pore size was approximately (212.3 ± 34.2) μm with a porosity of (48.3 ± 5.9)%, the compressive modulus of the scaffolds was (7.2 ± 1.2) MPa, which was irrelevant to the percentage changes of calcium-magnesium silicate, the compressive modulus was between that of cartilage and subchondral bone., Conclusion: The porous scaffolds for calcified cartilage layer have been successfully fabricated, which would be used for multi-layered composite scaffolds in osteochondral injury.