Search

One of the major challenges in membrane manufacturing today is to reduce the environmental footprint by promoting biobased raw materials and limiting the use of toxic solvents. In this context, environmentally friendly chitosan/kaolin composite membranes, prepared using phase separation in water induced by a pH gradient, have been developed. Polyethylene glycol (PEG) with a molar mass ranging from 400 to 10,000 g·mol -1 was used as a pore forming agent. The addition of PEG to the dope solution strongly modified the morphology and properties of the formed membranes. These results indicated that PEG migration induced the formation of a network of channels promoting the penetration of the non-solvent during the phase separation process, resulting in an increase in porosity and the formation of a finger-like structure surmounted by a denser structure of interconnected pores of 50-70 nm in diameter. The hydrophilicity of the membrane surface increased likely related to PEG trapping in the composite matrix. Both phenomena were more marked as the PEG polymer chain was longer, resulting in a threefold improvement in filtration properties.

The shortage of drinking water is a major problem in the rural areas of the Mekong Delta, especially, when surface water, a main local direct drinking water source is being threatened by pesticide pollution and salinity intrusion. A hybrid process coupling electrodialysis (ED) and nanofiltration (NF) is proposed as an effective process easy to setup in a small plant to treat complex matrix with high salinity and pesticide concentration as is the Mekong Delta surface water. Performance of the ED-NF integration was evaluated with synthetic solutions based on the comparison with a single NF step generally used for pesticide removal. Both energy consumption and water product quality were considered to assess process efficiency. The ED stage was designed to ensure a 50% removal of salinity before applying NF. As expected, the NF rejection is better in the hybrid process than in a case of a single NF step, especially for pesticide rejection. The integration of a NF stage operated with NF270 membrane consumes less energy than that with NF90 membrane but its efficiency was observed not high enough to respect the Vietnamese guidelines. Using NF90, the optimal recovery rate of the NF stage varies from 30 to 50% depending on the salt content in the feed.

This article presents a novel procedure for preparing porous membranes from water-soluble polymers involving the formation of a Pickering emulsion. Gelatin is a biodegradable biopolymer obtained by the partial hydrolysis of collagen. A biopolymer such as gelatin is capable of adsorbing at an oil/water interface, resulting in decreased interfacial energy. Hence, gelatin is widely employed as an alternate for synthetic surfactants to stabilize emulsions in the food industry. However, high-molecular-weight gelatin leads to large emulsion droplets and poor emulsion stability. The amphoteric nature of graphene oxide (GO) nanosheets was helpful in stabilizing the oil/water interface and allows for the preparation of a stable gelatin/GO emulsion. Membranes fabricated using gelatin/GO have a uniformly distributed porous structure. However, prepared membranes are highly hydrosoluble, so the membranes were cross-linked without affecting their morphology. XRD results evidenced that gelatin effectively exfoliated the graphite oxide which is essential to stabilizing the emulsion. Fabricated gelatin/GO membranes possess uniformly distributed pores and are highly stable in aqueous solution. Pure water filtration tests were conducted on the membranes. The permeability results proved that the membranes fabricated by a Pickering emulsion are promising materials for filtration.