Abstract Carbonaceous and carbon‐coated electrodes are ubiquitous in electrochemical energy storage and conversion technologies due to their electrochemical stability, lightweight nature, and relatively low cost. However, traditional reliance on conductive additives and binders leads to impermanent electrical pathways. Here, a general approach is presented to fabricate robust electrodes with a progressive failure mechanism by introducing carbide‐based interconnects grown via carbothermal conversion of (5 wt%) titanium hydride nanoparticles. This method concurrently enhances both electrical and mechanical properties within the electrode architecture. The resulting chemical bonding between active materials establishes a novel mechanism to maintain stable electrical pathways during cycling. Employed as Li‐ion battery anodes, these electrodes exhibit improved cyclability, achieving 80% capacity retention after 800 fast‐charge cycles at moderate loading (1 mAh cm−2). High loading cells with areal capacity of 3 mAh cm−2 show significantly improved cycle life over the same number of cycles. This performance improvement is attributed to the absence of significant impedance growth and a thinner solid electrolyte interphase (SEI) layer formed at high current densities (4C) as demonstrated by X‐ray photoelectron spectroscopy and transmission electron microscopy studies. The enhanced conductivity facilitates SEI formation, lowering ionic impedance and mitigating lithium plating, ultimately leading to the reported extended cycle life.

Commercial Li-ion batteries typically incorporate a small amount of high-capacity silicon (Si)-based materials in the composite graphite-based anode to increase the energy density of the battery. However, very little is known about the effects of Si on the fast-charging behavior of composite anodes. Herein, we examine the effects of the Si/graphite ratio in the composite anode on the fast-charging behavior of full cells. We show that addition of Si increases the rate capability from 1C to 8C and improves the capacity retention in early cycles at 6C due to reduced overpotential in constant current charging cycles. The impacts of Si content on fast-charging aging were identified by Post-Test characterization. Despite realizing benefits of available capacity and reduced Li plating at 6C, silicon–electrolyte interactions lead the time-dependent cell performance to fade quickly in the long term. The Post-Test analysis also revealed the thickening of the electrode and nonuniform distribution of electrolyte decomposition products on the Si-containing anodes, as well as the organic-rich solid electrolyte interphase (SEI), which are the factors behind cell degradation. Our study sheds insight on the advantages and disadvantages of Si/graphite composite anodes when they are used in fast-charging applications and guides further research in the area by designing an optimized composition of Si incorporated in a mature graphite matrix.