This article presents the results of investigations on HR6W alloy and Sanicro 25 steel and the dissimilar welded joint made of them. The characteristic images of microstructure of the investigated materials in the as-received condition and following the creep test, observed with a scanning electron microscope (SEM), are shown. The X-ray analysis of phase composition of the existing precipitates was carried out. The method for evaluation of creep strength based on abridged creep tests carried out at a temperature higher than the design one is presented. The obtained results do not deviate from the values of creep strength determined in long-term creep tests. The maximum difference in creep strength of the investigated materials is ±20%, which is in compliance with the acceptable scatter band. The methodology presented can be used for verification of creep strength (life time) of the material of finished components to be operated under creep conditions.

This paper presents the characteristics of the performance of P91 (X10CrMoVNb9-1), P92 (X10CrWMoVNb9-2) and VM12 (X12CrCoWVNb12-2-2) steels used for condition assessment of the pressure components of boilers with supercritical steam parameters. Studies on the mechanical properties, microstructure tests using scanning and transmission electron microscopy, and X-ray analysis of the phase composition of precipitates were performed for selected steels in the as-received condition and after long-term annealing. These steel characteristics are used for the evaluation of the microstructural changes and mechanical properties of the material of components after long-term service. The result of this study is the database of material characteristics representing the mechanical properties related to the microstructure analysis and it can be used for diagnosis of the components of pressure parts of power boilers.