The fabrication of thinnest, yet undeformed membrane structures with nanometer resolution is a prerequisite for a variety of Microelectromechanical systems (MEMS). However, functionally relevant thin films are susceptible to growth-generated stress. To tune the performance and reach large aspect ratios, knowledge of the intrinsic material properties is indispensable. Here, we present a new method for stress evaluation through releasing defined micro-cantilever segments by focused ion beam (FIB) milling from a predefined free-standing membrane structure. Thereby, the cantilever segment is allowed to equilibrate to a stress-released state through measurable strain in the form of a resulting radius of curvature. This radius can be back-calculated to the residual stress state. The method was tested on a 20 nm and 50 nm thick tunnel-like ALD Image 1 membrane structure, revealing a significant amount of residual stress with 866 MPa and 6104 MPa, respectively. Complementary finite element analysis to estimate the stress distribution in the structure showed a 97% and 90% agreement in out-of-plane deflection for the 20 nm and 50 nm membranes, respectively. This work reveals the possibilities of releasing entire membrane segments from thin film membranes with a significant amount of residual stress and to use the resulting bending behavior for evaluating stress and strain by measuring their deformation.

The continued scaling in transistors and memory elements has necessitated the development of atomic layer deposition (ALD) of silicon nitride (SiNx), particularly for use a low k dielectric spacer. One of the key material properties needed for SiNx films is a low wet etch rate (WER) in hydrofluoric (HF) acid. In this work, we report on the evaluation of multiple precursors for plasma enhanced atomic layer deposition (PEALD) of SiNx and evaluate the film’s WER in 100:1 dilutions of HF in H2O. The remote plasma capability available in PEALD, enabled controlling the density of the SiNx film. Namely, prolonged plasma exposure made films denser which corresponded to lower WER in a systematic fashion. We determined that there is a strong correlation between WER and the density of the film that extends across multiple precursors, PEALD reactors, and a variety of process conditions. Limiting all steps in the deposition to a maximum temperature of 350 °C, it was shown to be possible to achieve a WER in PEALD SiNx of 6.1 Å/min, which is similar to WER of SiNx from LPCVD reactions at 850 °C.