The formic acid (CH2O2) decomposition over sulfated zirconia (SZ) catalysts prepared under different synthesis conditions, such as calcination temperature (500–650 °C) and sulfate loading (0–20 wt.%), was investigated. Three sulfate species (tridentate, bridging bidentate, and pyrosulfate) on the SZ catalysts were characterized by using temperature-programmed decomposition (TPDE), Fourier-transform infrared spectroscopy (FTIR), and X-ray photoelectron spectroscopy (XPS). The acidic properties of the SZ catalysts were investigated by the temperature-programmed desorption of iso-propanol (IPA-TPD) and pyridine-adsorbed infrared (Py-IR) spectroscopy and correlated with their catalytic properties in formic acid decomposition. The relative contributions of Brønsted and Lewis acid sites to the formic acid dehydration were compared, and optimal synthetic conditions, such as calcination temperature and sulfate loading, were proposed.

Graphene nanoparticles coated with tannic acid were synthesized as non-halogen flame retardants; further, these nanoparticles were electrospun with polyurethane to produce multifunctional composite nanofibers. The composite nanofibers showed improved flame retardant, antimicrobial, and mechanical properties with increasing amounts of bio-based, non-halogen flame retardant. For instance, at 5 wt% of flame retardant, the peak heat release rate was reduced from 340.75 to 235.23 W/g along with 500% and 135% improvement in the antimicrobial activity and Young's modulus, respectively, compared to neat polyurethane fibers. These multifunctional composite nanofibers have potential applications in various fields, such as automobile, construction, and biomedical device.