By employing the melt-quenching technique, the ZnO–SrO–B2O3–PbO (ZSBP) glasses have been successfully fabricated. The derivative of Absorption Spectra Fitting (DASF) method was used to study the energy band gap (Eg) of the glasses which decreases from 3.57 eV to 3.39 eV. The structural properties have been studied using the Raman spectroscopy. The glass transition temperature (Tg) decreases with increase in concentration of the lead oxide. The current study examines the radiation shielding properties at 30.80–444 keV. The addition of PbO to the glasses resulted in a proportionate increase in the mass attenuation coefficient (MAC), suggesting a diminishing tendency in radiation transmission. At 30.80 keV, the MAC values are extremely high and range from 18.06 to 21.11 cm2/g. As density rises, the half value layer (HVL) decreases. In addition, the average HVL (HVL‾) decreases. The glass thickness required to reduce the radiation intensity to 90 %, 50 %, 25 %, and 10 % of its initial value is investigated at an energy of 35.80 keV. The T90 %, T50 %, T25 %, and T10 % values are 0.0020, 0.0132, 0.0264, and 0.0439 cm, respectively. The results suggest that a greater thickness of the radiation barrier is necessary to attain the necessary degree of attenuation.

Abstract Laser ablation synthesis in liquid solution (PLAL) is a green technique that allows for the physical formation of nanomaterials. This study indicates the preparation of stable gold nanoparticles (AuNPs) in Gum Arabic (GA) solution via laser ablation as a CT contrast agent. The optical properties were achieved using the absorption spectroscopic technique whereas the morphology and size distribution were investigated by TEM and ImageJ software. TEM image shows greater stability and spherical shape of GA-AuNPs with smaller size at 1.85 ± 0.99 nm compared to AuNPs without GA. The absorption spectrum of pure AuNPs has a lower absorption peak height in the visible range at λ = 521 nm, while the spectrum of GA-AuNPs has a higher plasmon peak height at λ = 514 nm with a blue shift towards lower wavelengths. The concentration of GA that dissolved in 10 mL of DI water via laser ablation is set at 20 mg. Increasing the number of pulses has only a minor effect on particle size distribution, which remains tiny in the nanometer range (less than 3 nm). For energies greater than 200 mJ, there is a blue shift toward shorter wavelengths. As the concentration of GA-AuNPs increases, the CT number is also increased indicating good image contrast. It can be concluded that there is a positive and significant influence of GA as a reducing agent for AuNPs, and a contrast agent for CT imaging which highlights its superiority in future medical applications.

Three high entropy materials (La2O3+TiO2+Nb2O5+WO3+X2O3 coded as LTNWM1, LTNWM2, and LTNWM3 for X = B, Ga, and In) produced by aerodynamic containerless processing were evaluated for optical attributes, and their gamma-radiation absorption abilities were investigated in this report. Optical related parameters such as the molar refractivity (Rm), optical transmission (T), molar polarizability (αm), metallization criterion (M), reflection loss (RL), static (εstatic), and optical (εoptical) dielectric constants were estimated through standard expressions, while photon attenuation parameters were estimated from data from photon transmission simulations in FLUKA code and XCOM software. The attenuation parameters were calculated for a wide energy photon spectrum (15 keV–15 MeV). LTNWM1, LTNWM2, and LTNWM3 had Rm values of 18.94 cm3/mol, 21.45 cm3/mol, and 26.09 cm3/mol respectively. The αm has a value of 7.52 × 10−24 cm3 for LTNWM1, 8.51 × 10−24 cm3 for LTNWM2, and 10.35 × 10−24 cm3 for LTNWM3. The photon shielding parameters evaluated by FLUKA and XCOM are compatible. The mass attenuation coefficient for the glasses was between 0.0338 and 52.8261 cm2/g, 0.0336–58.0237 cm2/g, and 0.0344–52.1560 cm2/g for LTNWM1, LTNWM2 and LTNWM3, respectively. The effective atomic number at 1.5 MeV was 18.718, 20.857, and 22.440 for LTNWM1, LTNWM2, and LTNWM3, respectively. The shielding parameters of the HMOs compared to traditional gamma radiation absorbers are exceptional and highlight the potential of using them as optically transparent gamma-shields.

Abstract New homologues series of liquid crystalline materials namely, (E)-3-methoxy-4-[(p-tolylimino)methyl]phenyl 4-alkloxybenzoates (I-n), were designed and evaluated for their mesomorphic and optical behavior. The prepared series constitutes three members that differ from each other by the terminally attached alkoxy chain group, these vary between 6 and 12 carbons. A laterally OCH3 group is incorporated into the central benzene ring in meta position with respect to the ester moiety. Mesomorphic characterizations of the prepared derivatives are conducted using differential scanning-calorimetry (DSC), polarized optical-microscopy (POM). Molecular structures were elucidated by elemental analyses and NMR spectroscopy. DSC and POM investigations revealed that all the synthesized derivatives are purely nematogenic exhibiting only nematic (N) mesophase, except for the longest chain derivative (I-12) that is dimorphic possesses smectic A and N phases. Moreover, all members of the group have a wide mesomorphic range with high thermal nematic stability. A comparative study was established between the present derivative (I-6) and their previously prepared isomer. The results indicated that the location exchange of the polar compact group (CH3) influences the N mesophase stability and range. The electrical measurements revealed that all synthesized series I-n show Ohmic behaviors with effective electric resistances in the GΩ range. Under white light illumination, the effective electric conductivity for the compound I-8 is five times that obtained in dark conditions. This derivative also showed two direct optical band gaps in the UV and visible light range. In addition, I-6 has band energy gaps of values 1.07 and 2.79 eV, which are suitable for solar energy applications.

We theoretically demonstrated optical phase switches in light storage-like experiments. Typical light storage (LS) and retrieval experiments consist of the probe field in the probe channel with writing and reading fields across the drive branch, as well as its recovery. The probe and first drive pulses as the standard electromagnetically induced transparency (EIT) effect of storing light are used in the proposed scheme for the atomic excitations. A train of probe pulses is used after a short storage period to induce Raman gain in the drive channel. The proposed scheme was applied to alkali-metal atoms such as 23Na, 87Rb, and 39K vapours. Spatiotemporal phase variations for generated drive pulses were found to shape in the form of discrete phase distributions. The proposed approach in the process of obtaining phase discrete distributions for different irradiation intensities was tested. For weak fields, the discrete distributions were distinct as a result of the differences in the upper hyperfine structure (hf) and the atomic relaxations. However, for moderate fields, the discrete phase distributions are smeared by the atomic relaxations.

Novel cubic microstructures for the purposes of plasmonic Ag-based NPs were made using biological wastes produced from a microbial culture of Bacillus cereus (B. cereus) employing a bottom-up approach for the biosynthesis of metal-based nanomaterials. The unique surface plasmon resonance (SPR) of the as-prepared Ag-based NPs was detected at 405 nm. The infra-red spectrum revealed that the used biological waste effectively stabilized our Ag-based NPs. Scanning and transmission electron microscopes were used in order to evaluate the sizes and shapes of the distinctive structures present in our samples. The Ag NPs had a face-centered cubic structure, with a size of 64.4 nm for the (200) nano-crystallites, according to the X-ray diffraction that was conducted. The zeta potential was found to be −19.5 mV and the dynamic light scattering (DLS) size was 238.8 nm. Methylene blue’s (MB) reaction with NaBH4 was used in order to measure the catalytic activity of the generated Ag-based NPs over a period of 1 to 5 min. With an astonishing reaction rate of 0.2861 min−1, the MB elimination percentage reached 67% in just 5 min, displaying outstanding catalytic activity. This work can therefore encourage the use of this biowaste for the ecologically benign, cost-effective, and long-term synthesis of innovative Ag-based nanoparticles and nanostructures, as well as in their use as catalysts in the catalytic reduction in MB.

The present study investigates the transient spectrum (TS) of a two-level system that interacts with a generalized squeezed state without using the rotating wave approximation (RWA). We consider the purity of the optical field, which is developed in a generalized squeezed state, utilizing the linear entropy. The analytic expressions of the TS and field purity (FP) of the bipartite system are evaluated. Moreover, the study exhibits the influence of the squeezed parameter and some photons transition on the TS and FP. We obtain that the control of the FP may be generated based on an adequate choice of the photons transition and squeezed parameter. Such results can be utilized in the understanding and development of various tasks of quantum physics and optics.

For a safe environment, humanity should be oriented towards renewable energy technology. Water splitting (WS), utilizing a photoelectrode with suitable thickness, morphology, and conductivity, is essential for efficient hydrogen production. In this report, iridium oxide (IrOx) films of high conductivity were spin-cast on glass substrates. FE-SEM showed that the films are of nanorod morphology and different thicknesses. UV-Vis spectra indicated that the absorption and reflectance of the films depend on their thickness. The optical band gap (Eg) was increased from 2.925 eV to 3.07 eV by varying the spin speed (SS) of the substrates in a range of 1.5 × 103–4.5 × 103 rpm. It was clear from the micro-Raman spectra that the films were amorphous. The Eg vibrational mode of Ir–O stretching was red-shifted from 563 cm−1 (for the rutile IrO2 single crystal) to 553 cm−1. The IrOx films were used to develop photoelectrochemical (PEC) hydrogen production catalysts in 0.5M of sodium sulfite heptahydrate Na2SO3·7H2O (2-electrode system), which exhibits higher hydrogen evaluation (HE) reaction activity, which is proportional to the thickness and absorbance of the used IrOx photocathode, as it showed an incident photon-to-current efficiency (IPCE%) of 7.069% at 390 nm and −1 V. Photocurrent density (Jph = 2.38 mA/cm2 at −1 V vs. platinum) and PEC hydrogen generation rate (83.68 mmol/ h cm2 at 1 V) are the best characteristics of the best electrode (the thickest and most absorbent IrOx photocathode). At −1 V and 500 nm, the absorbed photon-to-current conversion efficiency (APCE%) was 7.84%. Electrode stability, thermodynamic factors, solar-to-hydrogen conversion efficiency (STH), and electrochemical impedance spectroscopies (EISs) were also studied.

We examine how the weak excitation regime of a quantum well confined in a semiconductor microcavity (SM) influences the dynamics of quantum coherence and the total phase. We analyze the impact of the physical parameters on different quantumness measures, and illustrate their numerical results. We show that the amount of the coherence and total phase in the SMs for multi-photon excitation can be improved and controlled by the strength of the field, exciton-photon coupling, cavity dissipation rate, and excitonic spontaneous emission rate. We illustrate how the fidelity varies depending on the physical parameters. These results might have far-reaching ramifications not just in quantum information processing and optics, but also in physics at large.

A systematic treatment of the influence of the optical feedback (OFB) and the ratio of the radiative and the non-radiative recombination lifetime (τr/τnr) on the relative intensity noise (RIN) and the system dynamics of a semiconductor laser (SL) is presented. We found that the ratio τr/τnr causes a significant change in the intensity of noise, states, and route to chaos of such a system. Laser transit from a continuous wave (CW) to a periodic oscillation (PO) becomes faster in terms of the OFB strength by increasing the ratio τr/τnr. The route to chaos was identified in three distinct operating regions, namely, PO, period doubling (PD), and sub-harmonics (SH), which are dependent on the ratio τr/τnr, and injection current. In the route to chaos regime, the ratio τr/τnr triggers a slight shift in the frequency with reference to the frequency of the solitary laser. At upmost levels of the current, the highest value of the ratio τr/τnr stabilizes the laser and stimulates it to operate in CW or PO. In the strong OFB region, when the ratio τr/τnr increases, the chaotic operation changed to CW or PO operation and RIN is suppressed close to the quantum noise level.

The emission spectrum of a qubit (two-level atom) system that interacts with a field in the framework of parity deformations is investigated in this paper. The model consists of a qubit coupled to a single-mode field within the parity deformed Jaynes-Cummings model (PDJCM) based on the λ-analog of the quantum harmonic oscillator algebra. We numerically evaluate the atomic emission spectrum (AES), by considering the influence of the deformed parameter and half-band-width of the spectrometer. Moreover, the dependence of the spectrum peaks on the detuning parameter is discussed. Finally, we study the variation of the geometric phase of the whole system state modelled by the PDJCM in terms of the main physical parameters.

A p-n nanocomposite based on TiO2 nanotubes (NTs) and NiO nanoparticles (NPs) was designed and optimized in this study to improve the photocatalytic performance of methylene blue (MB). The hydrothermal technique has been used to produce TiO2/NiO nanocomposites with different NiO NPs weight ratios; 1TiO2:1NiO, 1TiO2:2NiO, and 1TiO2:3NiO. The crystal phase, chemical composition, optical properties, and morphology of TiO2/NiO were explored by various techniques. TiO2 NTs have a monoclinic structure, while NiO NPs have a cubic structure, according to the structural study. The bandgap of TiO2 NTs was reduced from 3.54 eV to 2.69 eV after controlling the NiO NPs weight ratio. The TiO2/2NiO nanocomposite showed the best photodegradation efficiency. Within 45 min of solar light irradiation, the efficiency of MB dye degradation using TiO2/2NiO hits 99.5% versus 73% using pure TiO2 NTs. Furthermore, the catalytic photodegradation efficiency did not deteriorate significantly even after five reusability cycles, intimating the high stability of the TiO2/2NiO nanocomposite. This suggests that the loading of NiO NPs into TiO2 NTs lowers the recombination of photo-produced electron/hole pairs and enlarged solar spectral response range, which results in improved photocatalytic activity. The mechanism of charge transfer in the TiO2/NiO and kinetic models were discussed for the photodegradation of MB.

An amendment to this paper has been published and can be accessed via a link at the top of the paper.

We propose a new kind of Schrödinger cat state introduced as a superposition of spin coherent states in the framework of noncommutative spaces. We analyze the nonclassical features for these noncommutative deformed states in terms of the main physical parameters. The physical importance of deformed states is that they provide a convenient description of a large set of laser systems. As an application, we develop the Jaynes–Cummings model by considering the interaction among atoms and cat state fields associated to deformed spin algebras. In this context, we show the dynamical behavior of the nonlocal correlation and nonclassical properties in these quantum systems.