Search

In this study, the ball-on-disk sliding wear and tribocorrosion behavior in the H2SO4 and HCl solution of NiCoCrMoCu alloys with carbon additions of 0.2, 1, 1.5, and 2 wt.% with the Al2O3 ball as a counterpart was investigated systematically. Obvious tribocorrosion antagonistic effects were found after wear in both aqueous solutions. Compared with dry sliding wear conditions, the lubrication effect of the aqueous solution significantly reduces the wear rate of the alloy, and the reduction effect in the H2SO4 aqueous solution was more obvious than that in HCl. The antagonistic effects of the 0.2C and 1C alloys decrease with the load and sliding rate, while those of the 1.5C and 2C alloys increase. The (coefficient of friction) COF and wear rate under different loads and sliding rates were analyzed using the response surface analysis (RSM) method. It was found that the COF mainly showed dependence on the sliding rate, while the wear rate showed dependence on load and sliding speed. [ABSTRACT FROM AUTHOR]

In this study, ball-on-disk dry sliding wear behavior of Ni-Co-Cr-Mo-Cu alloys with carbon contents of 0.2, 1, 1.5, 2 wt.% with Al2O3 ball as a counterpart was investigated systematically. Alloys containing 0.2 and 1 wt.% carbon exhibit dispersed carbides, serving as matrix strengthener, while higher alloying of carbon (1.5, 2 wt.%) will induce the aggregation of carbides, acting as load bearer. Therefore, with increasing carbon content, the propensity of plastic deformation and oxidative lubrication is reduced, the roughness of worn surface is decreasing, and the wear mechanism is also altered from adhesive wear to fatigue wear. Significant reduction of wear rate by alloying high carbon content demonstrated the feasibility of carbides-reinforced Ni-Co-Cr-Mo-Cu alloys. [ABSTRACT FROM AUTHOR]

The Portevin-Le Châtelier (PLC) effect in a powder metallurgy (PM) Co-Ni-based superalloy was systematically investigated via the tensile tests at temperatures ranging from 200 to 600 °C and strain rates at 1.0 × 10−4 to 1.0 × 10−2. Both normal and inverse PLC effects were observed in the PLC regime, and the former appeared in the A and B types at a low temperature, whilst the latter appeared in the C type at an elevated temperature. Both positive and negative strain rate sensitivities (SRS) were shown in PLC regime, and SRS should be derived from same types of serrations. Based on the calculated activation energy, the substitutional atom Mo is considered to take primary responsibility for the PLC effect in present alloy. [ABSTRACT FROM AUTHOR]

Microstructure and mechanical properties of novel Ni-20Co-12Cr superalloys, with and without Nb addition, were systematically studied during long-term thermal exposure. With increased exposure time, the average diameter of the γ′ precipitates increased in both alloys in succession; this is more obviously observed in alloy containing 1 wt% Nb (1Nb). It is suggested that Nb increased the γ′ coarsening rate by accelerating the diffusion of Al and Nb in γ matrix. In addition, the γ′ phase fraction is increased by about 4% in 1Nb compared to the alloy without Nb (0Nb). The morphology of the γ′ phase changed from near-spherical to cuboidal shape during exposure in both alloys. Due to the increased γ/γ′ lattice misfit by Nb addition, 1Nb alloy showed an earlier tendency of shape change. Vickers hardness results revealed that the overall hardness decreased with the exposure time because the size increment of the γ′ precipitate weakened the precipitates strengthening and Orowan strengthening. [ABSTRACT FROM AUTHOR]

This research was aimed at investigating the high temperature oxidation behavior of Inconel 718 superalloy fabricated by electron beam melting with the building direction of 0°, 55° and 90° deviation from the Z axis of cylindrical samples. Columnar γ-fcc phase with preferred crystal orientations was found in all specimens. With the temperature ranging from 700 to 1000 °C, the 0° sample, symbolized by the lowest grain boundary density, and largest grain size, reveals the best oxidation performance. It is concluded that the building direction has more impact on the amount of grain boundary density than crystal orientation, which determined the oxidation resistance. [ABSTRACT FROM AUTHOR]