Search

Chitosan/gelatin and chitosan/gelatin/zeolite films prepared by solvent casting method are impregnated with a mixture of thymol and carvacrol using a green solvent, supercritical carbon dioxide at 35 °C and 30 MPa, during 18 h. Proposed method enables preparation of biocompatible and biodegradable blends with strong antioxidant and antibacterial activity, whereby amounts of loaded thymol/carvacrol (TC) mixture are in the range from 3.3% to 6%. After initial burst release, both types of films exhibit gradual release of bioactive compounds, with around 72% and 96% of impregnated TC mixture released in water and phosphate buffered saline solution (pH 7.4) during tested period of 10 days, respectively. Results of water vapor transmission rate (>76 g m−2 day−1) confirm that prepared composites are suitable for wound dressing application. Thermal analysis shows superior properties of prepared TC loaded films compared to control samples. In addition, mechanical and structural properties, as well as solubility and swelling behavior of the obtained films are investigated in detail. [ABSTRACT FROM AUTHOR]

The integrated supercritical fluid extraction–impregnation process (SFE-SSI) was performed to fabricate material with antiviral properties against the herpes simplex virus (HSV). Cotton gauze and starch/chitosan polymer films (SCF) were impregnated with components extracted from Melissa officinalis at 10 MPa and 40 °C using a green medium, supercritical carbon dioxide (scCO2). The influences of the processing mode regarding the flow of the supercritical fluid through the system, and the mass ratio of the plant material and the solid carrier, on the impregnation yield of M. officinalis extract were studied. The results revealed that the introduction of a fresh amount of CO2 into the system enabled the highest impregnation yield of 2.24% for cotton gauze and 8.71% for SCF. The presence of M. officinalis extract on the surface of both impregnated cotton gaze and SCF was confirmed by FTIR and GC analyses after the re-extraction of the impregnated samples. The M. officinalis impregnated materials showed a strong inhibitory effect against Bovine herpesvirus type 1 (BHV-1). [ABSTRACT FROM AUTHOR]

Poly(lactic acid) (PLA) stands out as the most promising biodegradable alternative to conventional petrochemical‐based polymers for manufacturing of high‐performance materials applied in medicine, pharmacy, food, textile, and electronic industry. This review was aimed to present the conventional and up‐to‐date technologies for PLA processing including melt blending and molding, hot melt extrusion, 3D printing, foaming, impregnation, thermally induced phase separation, nano‐ and microparticles preparation, wet and dry spinning processes. In addition, the effect of the processing parameters and polymer characteristics on the properties of the final material was elaborated. Diverse possibilities to tailor properties of PLA‐based materials by variation in polymer characteristics and concentration, solvent selection, drying method, processing pressure and temperature, incorporation of bioactive components, and so on were highlighted. The examples of the relations between processing methods, parameters, and end‐product properties are given for a better understanding of all aspects that need to be perceived for fabrication of PLA‐based materials with required performances. [ABSTRACT FROM AUTHOR]

Novel composites based on natural zeolite—clinoptilolite and monoterpene phenols—thymol and carvacrol were prepared by supercritical solvent impregnation (SSI) in supercritical carbon dioxide (scCO2) at 30 MPa and 35 °C during 18 h. The content of phenols in composites (thymol—23.0 and carvacrol—19.1 wt%) was determined using both C,H,N and thermal analysis (TGA); interactions of the phenols with the zeolite lattice studied by Fourier transform infrared spectroscopy (FTIR) and powder X-ray diffraction (PXRD) showed that the zeolite lattice was preserved in the composites. The composites exhibited antibacterial activity toward Gram-negative bacteria Escherichia coli DSM 498 and Gram-positive bacteria Staphylococcus aureus ATCC 25923 in different water media (phosphate buffer solution, spring water and lake water). After 1 h carvacrol-containing clinoptilolite showed better antibacterial activity than composite with thymol. Both composites expressed bactericidal effect after 24 h of contact. Leaching of the phenols from composite in water was more pronounced from thymol (22.7–32.1%) than for carvacrol (6.2–8.9%) suggesting influence of steric effect on the desorption process. [ABSTRACT FROM AUTHOR]

In the present study, supercritical solvent impregnation (SSI) has been applied to incorporate thymol into bio-composite polymers as a potential active packaging material. Thymol, a natural component with a proven antimicrobial activity, was successfully impregnated into starch-chitosan (SC) and starch-chitosan-zeolite (SCZ) films using supercritical carbon dioxide (scCO2) as a solvent. Experiments were performed at 35 °C, pressures of 15.5 and 30 MPa, and an impregnation time in the range of 4–24 h. The highest impregnation yields of SC films with starch to chitosan mass ratios of 1:1 and 1:2 were 10.80% and 6.48%, respectively. The addition of natural zeolite (15–60%) significantly increased the loading capacity of films enabling thymol incorporation in a quantity of 16.7–27.3%. FTIR and SEM analyses were applied for the characterization of the films. Mechanical properties and water vapor permeability of films before and after the impregnation were tested as well. Thymol release kinetics in deionized water was followed and modeled by the Korsmeyer-Peppas and Weibull model. SCZ films with thymol loading of approximately 24% exhibited strong antibacterial activity against E. coli and methicillin-resistant Staphylococcus (S.) aureus (MRSA). [ABSTRACT FROM AUTHOR]