Search

The effect of plastic deformation process on the dissolution rate of biocompatible Mg alloys was investigated. Two biocompatible MgLi1Ca0,2Zn1 and MgLi1Ca1Zn1 alloys were selected for the study. The alloys were deformed on a 100T press at a temperature of 350°C by conventional extrusion and by the equal channel angular extrusion process (ECAE). The grain size analysis showed a high degree of the grain refinement from approximately 110 mm in the initial state to 2.8 mm after the 3rd pass of the ECAE process. Compared to as-cast state, the degree of strengthening has increased after plastic forming. The results of biodegradation tests have shown a significant increase in corrosion rate after both conventional extrusion and ECAE, although after subsequent ECAE passes, this rate was observed to slightly decrease in the MgLi1Ca1Zn1 alloy. Based on the results of macro- and microstructure examinations, the corrosion progress in samples after the extrusion process was described. [ABSTRACT FROM AUTHOR]

The objective of the study was to determine the feasibility of plastic forming by hot rolling of the AA2519 aluminium alloy sheets and cladding these sheets with a layer of the EN AW-1050A alloy. Numerous hot-rolling tests were carried out on the slab ingots to define the parameters of the AA2519 alloy rolling process. It has been established that rolling of the AA2519 alloy should be carried out in the temperature range of 400-440°C. Depending on the required final thickness of the sheet metal, appropriate thickness of the EN AW-1050A alloy sheet, used as a cladding layer, was selected. As a next step, structure and mechanical properties of the resulting AA2519 alloy sheets clad with EN AW-1050A alloy was examined. The thickness of the coating layer was established at 0,3÷0,5mm. Studies covered alloy grain size and the core alloy-cladding material bond strength. [ABSTRACT FROM AUTHOR]

The aim of the study was to test and assess products extruded from the magnesium alloys type MgAlZn: AZ31, AZ61 and AZ80A alloys in the form of Ø35mm round bars and 80x15mm flat bars. The test material was extruded in a direct system with the ram feed speed of 1 mm/s and the extrusion ratio λ = 7 ÷ 9. The extruded bars were examined in as-extruded state and after heat treatment to the T5 temper and T6 temper. The strength properties were tested and microstructure was examined with calculation of the average grain size. [ABSTRACT FROM AUTHOR]

Contemporary materials engineering requires the use of materials characterised by high mechanical properties, as these precisely properties determine the choice of material for parts of machinery and equipment. Owing to these properties it is possible to reduce the weight and, consequently, the consumption of both material and energy. Trying to meet these expectations, the designers are increasingly looking for solutions in the application of magnesium alloys as materials offering a very beneficial strength-to-weight ratio. However, besides alloying elements, the properties are to a great extent shaped by the solidification conditions and related structure. The process of structure formation depends on the choice of casting method forced by the specific properties of casting or by the specific intended use of final product. The article presents a comparison of AZ91 magnesium alloys processed by different casting technologies. A short characteristic was offered for materials processed by the traditional semi-continuous casting process, which uses the solidification rates comprised in a range of 5 - 20°C/s, and for materials made in the process of Rapid Solidification, where the solidification rate can reach 106 °C/s. As a result of the casting process, a feedstock in the form of billets and thin strips was obtained and was subjected next to the process of plastic forming. The article presents the results of structural analysis of the final product. The mechanical properties of the ø7 mm extruded rods were also evaluated and compared. [ABSTRACT FROM AUTHOR]

Copyright of Archives of Metallurgy & Materials is the property of Polish Academy of Sciences and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

Copyright of Archives of Metallurgy & Materials is the property of Polish Academy of Sciences and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

The present paper describes experimental and qumerical analyses for prediction of microstructure changes during hot plate rolling, which was conducted in Metal Forming Department Czestochowa, Technical University. Models describing kinetics of recrystallization of deformed austenite and precipitation of niobium carbon-nitrides were evaluated in semi-industrial conditions. The main objective of simulation using finite element methods was to determine temperature and strain distributions in the roll gap and parameters of mi crostructure through thickness of rolled plates. The experimental results were compared with computer simulation results, which showed thai: retained strains accumulated during the previous passes have a big influence on stability of distribution of mechanical properties. [ABSTRACT FROM AUTHOR]