We briefly summarize the results from a set of experiments designed to demonstrate the effects of high magnetic fields applied during thermal annealing of amorphous Nd2Fe14B produced through melt-spinning. A custom-built differential scanning calorimeter was used to determine the crystallization temperatures in zero-field and in applied fields of 20 kOe and 90 kOe, which guided subsequent heat treatments to evaluate phase evolution. X-ray diffraction was used for phase identification and transmission electron microscopy was employed for observation of the crystallite size and morphology. Magnetization measurements were also used to evaluate the resulting magnetic phases after thermomagnetic processing. While the applied magnetic fields do not appear to affect the crystallization temperature, significant effects on the kinetics of phase evolution are observed and correlated strongly to the magnetic behavior. [ABSTRACT FROM AUTHOR]

Fe-Si electric steel is the most widely used soft magnetic material in electric machines and transformers. Increasing the silicon content from 3.2 wt.% to 6.5 wt.% brings about large improvement in the magnetic and electrical properties. However, 6.5 wt.% silicon steel is inherited with brittleness owing to the formation of B2 and D03 ordered phase. To obtain ductility in Fe-6.5wt.% silicon steel, the ordered phase has to be bypassed with methods like rapid cooling. In present paper, the effect of cooling rate on magnetic and mechanical properties of Fe-6.5wt.% silicon steel is studied by tuning the wheel speed during melt spinning process. The cooling rate significantly alters the ordering and microstructure, and thus the mechanical and magnetic properties. X-ray diffraction data shows that D03 ordering was fully suppressed at high wheel speeds but starts to nucleate at 10m/s and below, which correlates with the increase of Young’s modulus towards low wheel speeds as tested by nanoindentation. The grain sizes of the ribbons on the wheel side decrease with increasing wheel speeds, ranging from ∼100 μm at 1m/s to ∼8 μm at 30m/s, which lead to changes in coercivity. [ABSTRACT FROM AUTHOR]