Abstract: Continuous-flow process conditions for the reduction to gold nanoparticles were varied following a variation scheme aiming at impacting each of the elementary steps—mixing, reaction, polymer diffusion and polymer binding. While the last three variations are done by proper material choice (reducer; polymeric stabilizer), flow processing using a multilamination micromixer intensified the mass transfer in all these steps and particularly improved the first mixing step of the reactants. As reducers L-ascorbic acid (H2Asc) and sodium borohydride (NaBH4) were used and as gold particle precursor chloroauric acid (HAuCl4). All processing runs were analysed by plasmon absorption and transmission electron microscopy to reveal size, shape and polydispersity. For the HAuCl4–H2Asc system, the smallest particles were 0.8–4nm (7.5mL/min) and 0.6–3nm (10.0mL/min) for the HAuCl4–NaBH4 system. This is at the upper edge of performance reported for batch systems in literature, i.e. among the smallest gold particles generated. While the particles made for the HAuCl4–H2Asc system were polydisperse and polyshaped for most process conditions (however being spherical and relatively uniform at the two largest flow rates investigated), processing with the HAuCl4–NaBH4 system resulted in particles sizes with small mean deviation and almost ideal spherical shape. With polyvinyl alcohol (PVA) as stabilizer, stable colloids were obtained for one week (violet coloured) up to at least 2 months (pink coloured) in case of reaction with ascorbic acid, and for at least 1 month in case of reaction with NaBH4. [Copyright &y& Elsevier] more...

Abstract: The acid catalyzed sol–gel type synthesis of polyorganosiloxane core-shell nanoparticles with removable PDMS core in aqueous dispersion leads to the inherent formation of a bimodal size distribution with smaller spheres having approximately 26nm radii and larger nanoparticles with 60nm in radius. The origin of the self-organized bimodality is investigated and finally attributed to a combination of stabilization of the growing particles due to i) a miniemulsion-type stabilization by the ultrahydrophobe PDMS and ii) by surface co-stabilization by the employed surfactant. The significant influence of temperature, pH, stirrer speed and amount of the surfactant on the particle sizes allows for the design and fine-tuning of different nanoparticles sizes and distributions. [Copyright &y& Elsevier] more...