Search

Small amplitude oscillatory shear is carried out during isothermal degradation of poly(lactic acid) (PLA) in order to determine the evolution of the characteristic relaxation time with degradation time and temperature. After reducing the relaxation time data to a single mastercurve, a 4-parameter function is fitted to the data to allow prediction of the change in relaxation time following an arbitrary thermal history. The method enables separation of the effects of temperature and of degradation on the relaxation time, both of which lead to a horizontal shift of dynamic data along the frequency axis, and hence enable a correction for thermal degradation during rheometry to be carried out. To validate the method, two isothermal frequency sweeps were measured with different temperature histories, producing different mastercurves due to dissimilar in-test thermal degradation. After correcting for thermal degradation using the function and the thermal histories, the two frequency sweeps reduce to the same viscoelastic mastercurve in the undegraded pre-test state. [ABSTRACT FROM AUTHOR]

In automated layup manufacturing processes of fiber-reinforced polymer composites, the quality of the manufactured part is strongly dependent on frictional behavior. Improper control of frictional forces can lead to defect formation. Frictional sliding rheometry tests provide an innovative methodology to accurately characterize the tool-ply friction of unidirectional (UD) prepreg employing unique annular plate geometries. The effect of processing parameters (temperature, velocity, and normal force) on the frictional response of a carbon fiber prepreg was studied. Moreover, utilizing custom designed plate geometries coupled with optically transparent fixtures allowed for in-situ quantification of the prepreg-rigid surface contact area along with simultaneous characterization of the process parameter-dependent frictional mechanisms. Our findings highlight the reduction in frictional forces with increasing temperature, attributed to the increased resin flowability, while increases in sliding rates resulted in a pronounced increase in the frictional forces. The effect of applied load on the frictional characteristics was more complicated due to contributions from both the adhesive and normal forces. Finally, the results were interpreted in light of the contact area measurements performed at different temperatures, normal force, and sliding rate. • Frictional sliding properties of carbon fiber prepregs are characterized with an annular plate geometry in a rheometer. • Effect of processing variables (temperature, sliding velocity, and normal force) on the frictional properties of the prepreg is investigated. • Optical microscopy facilitates quantification of the contact area between the prepreg and rigid substrate. • Frictional sliding behavior transitions from mixed to hydrodynamic lubrication regime of a Stribeck curve. • Frictional forces are controlled by both adhesive forces and applied load, leading to deviations from Amontons' law. [ABSTRACT FROM AUTHOR]

An adaptable flexural test fixture is proposed to characterise the mechanical properties of miniature beam specimens (≤10 mg) at ambient conditions or in the presence of fluids at elevated temperatures. The fixture is validated using representative amorphous and semi-crystalline polymers. The response of miniature specimens is compared against that of medium-sized specimens (≤1 g) on the same fixture and on conventional test equipment. Good agreement is found between the specimen sizes for all materials, but the comparisons highlight small differences attributed to factors such as specimen dimensional accuracy, crystallinity and span-to-thickness ratios. Flexural tests in water at 37 °C using both specimen sizes were performed to investigate the evolution of mechanical behaviour of hydrolytically degraded polylactides. Here, specimen size influences the diffusion timescale of acidic by-products which can reduce or enhance autocatalysis. • Designed and built a 3-point bending test fixture for miniature (<10 mg) through to small (<1 g) polymer specimens. • Fixture can be immersed in a heated water bath for measurements. • Dry and wet amorphous and semi-crystalline polymers were used for validation against conventional test equipment. • Good agreement was found in the flexural properties measured with the fixture compared to conventional equipment. [ABSTRACT FROM AUTHOR]