Highly uniform coalescent moniliforme-shape α-Fe2O3 straight nanochains built up of single crystal building blocks are synthesized via a facile one-pot solution-phase route at 180 °C using FeCl3, which have interesting magnetic behaviors based on their unique structure. Surprisingly, an exceptionally high TM (Morin transition temperature) is observed. Highly uniform coalescent moniliforme-shape α-Fe2O3 straight nanochains built up of single crystal building blocks are synthesized via a facile one-pot solution-phase route at 180 °C using FeCl3, which have interesting magnetic behaviors based on their unique structure. [ABSTRACT FROM AUTHOR]

Nickel ferrite (NiFe2O4) nanomaterials with different morphologies, including nano-spheres (10–25 nm in diameter), nano-rods (50–60 nm in diameter and ~1 μm in length), and nano-octahedrons (side length ~150 nm), have been synthesized by a single mild hydrothermal method at 160 °C without any surfactant. The crystal structures have been investigated by TEM, HRTEM, and studied by simulations using the program Materials Studio. The variations in the morphology, as well as the preferential crystal growth directions, depend only on the pH value of the reaction solution. A phase formation mechanism is thus proposed. Magnetization measurements at T = 300 K indicate that the NiFe2O4 nano-spheres of 10–25 nm diameter are superparamagnetic with non-saturating magnetization at H = 7 kOe. The saturation magnetization, MS, of the nanorods is 40 emu g−1, less than the bulk value, MS = 46.7 to 55 emu g−1. The coercivity is HC = 40 Oe, reduced from the bulk value of 100 Oe. On the other hand, the nano-octahedrons have a saturation magnetization of MS = 50 emu g−1, the same as the bulk value. However the coercivity, HC = 50 Oe is also much reduced from the bulk value. [ABSTRACT FROM AUTHOR]

TbMnO3 thin films with different crystallographic orientations were deposited epitaxially on LaAlO3 [100] and SrTiO3 [100] single crystal substrates by using pulsed laser deposition. Magnetization measurements were performed along the [110], [-110], and [001] directions of the films. Obvious magnetic anisotropy and low temperature ferromagnetism were found. Transitions at T ∼ 10, 32, 120, and 125 K along different directions are observed. The susceptibility anomalies, remarkably anisotropic, are discussed on the frame of the domain wall and strain-induced distortion. Particularly, the lattice mismatch and the anisotropic thermal expansion between the films and substrates are likely responsible for the distortion behaviors. [ABSTRACT FROM AUTHOR]