Search

The keyhole behaviors were observed directly by laser welding experiment with quartz glass. Based on Fresnel absorption of laser beam and multi-reflection combined with volume of fluid (VOF) method, a three-dimensional mathematical model was established to study the role of welding speed on keyhole behaviors and keyhole-induced porosity formation in laser welding of aluminum alloy. The keyhole behaviors and weld pool fluid flow were discussed, and the result shows that, although the welding speed varies, the mechanism of keyhole collapse was similar. However, the keyhole stability at higher welding speed was improved due to reduced weld depth fluctuations, spatter number, keyhole depth to width ratio, and keyhole collapse frequency. Furthermore, the improved keyhole stability impeded the keyhole collapse, and the lower weld depth and solidification rate facilitated bubble escaping from the weld pool easily, which are the main factors for suppression of porosity at higher welding speed. [ABSTRACT FROM AUTHOR]

The droplet escape condition in laser welding is established in this paper. A three-dimensional numerical model is developed to study the weld pool convection and spatter formation at full penetration during the fiber laser welding of 5083 aluminum alloy. It is found that when laser power is 9 kW, the bottom of the keyhole is dynamically opened and closed. When the bottom of the keyhole is closed, the molten metal at the bottom of the back keyhole wall flows upwards along the fusion line. When the bottom of the keyhole is opened, few spatters can be seen around the keyhole at the top surface, two flow patterns exists in the rear part of the keyhole: a portion of molten metal flows upwards along the fusion line, other portion of molten metal flows to the bottom of the keyhole, which promote the spatter formation at the bottom of the keyhole rear wall. [ABSTRACT FROM AUTHOR]

The instability of the keyhole and bubble being captured by solidification interface are the main factors that affect the formation of porosity in laser welding of both aluminum alloy and steel. In laser welding of aluminum alloy, the more violent fluid flow behind the keyhole, the larger depth to width ratio can cause the keyhole more unstable, and susceptive to collapse that can be described as three necessary steps. The much larger solidification rate and longer escaping distance make the bubble easily captured by the solidification interface, and easily combined. All of these reasons contribute to the formation of larger number and size of porosity in laser welding of aluminum alloy. The numerical and experimental results are in good agreement. [ABSTRACT FROM AUTHOR]

The droplet escape condition is established, a three-dimensional numerical model is built to investigate the behavior of the weld pool in fiber laser welding of 5083 aluminum alloy, the shear stress caused by the metallic vapor flow that has great influence on spatter formation is considered. A high speed photography system is used to capture the transient images of the weld pool, the spatter formation is discussed. The numerical and experimental results show that the spatters generate mainly around the keyhole. Two factors are responsible for the spatter formation: the surface tension of the molten metal around the keyhole is low. The recoil pressure caused by evaporation and the shear stress caused by metallic vapor flow accelerate the upward moving melt around the keyhole. Increasing the welding speed and placing the nozzle at the trailing position can decrease the upward momentum of the molten metal around the keyhole, and stabilize the keyhole, which are help to suppress the formation of spatter. [ABSTRACT FROM AUTHOR]

• Keyhole and plume features were automatically extracted from the image processing method; • Effects of Mg content was helpful to keep the opening of keyhole; • Effects of Mg content leaded to the frequent swelling generation at the rear weldpool. This paper concerns the effects of Mg content on keyhole behaviours during the laser welding process of 5754, 5083 and 5A06 Al-Mg alloys. The features of the vapour plume and keyhole area are extracted from high-speed images with image processing methods. The increase of Mg content leads to the increase of hydrodynamic pressure caused by metal evaporation and decrease of surface tension acting on the keyhole wall. The strong metal evaporation and decrease of surface tension help the formation of keyhole, which both result in a large size of keyhole with deep penetration and low frequency of keyhole collapse. However, the impact of metal vapour could be enhanced by the increase of evaporation and the decrease of both surface tension and viscosity, which leads to the frequent generation of swelling at the rear weldpool and poor formation of the weld bead. [ABSTRACT FROM AUTHOR]