Search

Ultra-high-performance concrete (UHPC) has promising applications in civil engineering. However, the elastic modulus of UHPC is relatively low compared with its compressive strength, which may result in insufficient stiffness in service. This work was carried out to explore the feasibility of producing UHPC with high elastic modulus by nano-Al2O3 (NA). Based on particle densely packing theory, the initial mixture of UHPC was designed via the modified Andreasen and Andersen model. An experimental investigation was conducted to systematically examine the effects of NA on different properties of UHPC, including its fluidity, mechanical properties, durability, and microstructure. It was found that: (1) Compared with UHPC without NA, the flexural strength, compressive strength, and elastic modulus of UHPC were improved by 7.38–16.87%, 4.08–20.58%, and 2.89–14.08%, respectively, because of the incorporation of NA; (2) the addition of NA had a prohibiting impact on the threshold pore diameter and porosity of UHPC, which suggested that NA could be conducive to its pore structure; (3) the incorporation of NA led to a decline of 2.9–11.76% in the dry shrinkage of UHPC, which suggested that incorporating NA in a proper amount could reduce the risk of cracking and alleviate the dry shrinkage of UHPC; (4) the optimal amount of NA in UHPC was 1.0%, considering the effects of NA on workability, mechanical properties, microstructure, and the durability of UHPC. [ABSTRACT FROM AUTHOR]

• UHPC with high elastic modulus was design by MAA particle packing model. • Workability, microstructure, and mechanical strength of HEMUHPC were studied. • Elastic modulus of HEMUHPC ranged from 40.50 GPa to 47.13 GPa. • Relationship between elastic modulus and compressive strength was a power function. • Optimal content of alumina micro-powder in HEMUHPC was 10%. Elastic modulus is an important parameter in engineering structural design for evaluating the stiffness of concrete members. Ultra-high-performance concrete (UHPC) has excellent mechanical properties and durability, but the relatively low elastic modulus prohibits the widespread use of the UHPC. In this study, high elastic modulus UHPC (HEMUHPC) was designed according to Modified Andreasen and Andersen particle packing model proposed by Funk and Dinger. Effects of alumina micro-powder (the content of alumina is higher than 99%, and the particle size is lower than 100 μ m) on the workability, microstructure, and mechanical properties of HEMUHPC were systematically investigated. The reason for the improvement of elastic modulus of HEMUHPC was revealed by nano indentation test. It was found that, 1) the porosity and threshold pore diameter of HEMUHPC were reduced because of the addition of alumina micro-powder; 2) the flexural strength, compressive strength, and elastic modulus of HEMUHPC were increased by 3.54–11.23%, 8.89–22.83%, and 6.19–16.37%, respectively, due to the addition of alumina micro-powder; 3) the optimal content of alumina micro-powder was 10%, considering its effects on the workability, mechanical properties, and microstructure of HEMUHPC; 4) Nano indentation experiments showed that the elastic modulus of the alumina micro-powder was 90–135 GPa, which is much higher than the elastic modulus of hydration products of HEMUHPC, and thus the elastic modulus of the HEMUHPC matrix could be improved, due to the addition of alumina micro-powder. [ABSTRACT FROM AUTHOR]

Ultra-high-performance concrete (UHPC) has received increasing attention in recent years due to its remarkable ductility, durability, and mechanical properties. However, the manufacture of UHPC can cause serious environmental issues. This work addresses the feasibility of using aeolian sand to produce UHPC, and the mix design, environmental impact, and mechanical characterization of UHPC are investigated. We designed the mix proportions of the UHPC according to the modified Andreasen and Andersen particle packing model. We studied the workability, microstructure, porosity, mechanical performance, and environmental impact of UHPC with three different water/binder ratios. The following findings were noted: (1) the compressive strength, flexural strength, and Young's modulus of the designed UHPC samples were in the ranges of 163.9–207.0 MPa, 18.0–32.2 MPa, and 49.3–58.9 GPa, respectively; (2) the compressive strength, flexural strength, and Young's modulus of the UHPC increased with a decrease in water/binder ratio and an increase in the steel fibre content; (3) the compressive strength–Young's modulus correlation of the UHPC could be described by an exponential formula; (4) the environmental impact of UHPC can be improved by decreasing its water/binder ratio. These findings suggest that it is possible to use aeolian sand to manufacture UHPC, and this study promotes the application of aeolian sand for this purpose. [ABSTRACT FROM AUTHOR]