Search

The weak compressive strength of dried ceramic foams is a disadvantage of fabricating ultralight ceramic foams, especially for the ceramic foams with porosity exceeding 95%. In this study, dried alumina foams were enhanced by agar and PVA-freezing-thawing using sodium dodecyl sulfate as surfactant. It is found that the two additives have no negative influence on adsorption of sodium dodecyl sulfate on alumina particles as well as the hydrophobic character of alumina particles. Stable alumina particle-stabilized foams were prepared with less than 0.5 wt% agar and 1.0 wt% PVA. High additive concentration above the critical values weakens stability of wet foams, which is probably due to the aggregate of alumina particles caused by long-chain molecules connecting. The compressive strength of dried alumina foams has a significant improvement with the employment of agar and PVA-freezing-thawing. The dried foams prepared with 1wt% PVA assisted by freezing-thawing has porosity of 97.1% and compressive strength of 0.16 MPa, which could maintain integrity of dried foams without destruction in the fabricating process. [ABSTRACT FROM AUTHOR]

Abstract The mechanical strength of highly porous ceramic foams shows significant attenuation with the increase of porosity, especially for ceramic foams with very high porosity level above 95%. Ultra-light bulk composite ceramic foams were fabricated via introducing 20 wt% zirconia in alumina-based cell wall, aiming at improving mechanical strength of alumina based ceramic foams. The preparation and stability of alumina and zirconia particles synergistically stabilized foams were investigated. The obtained bulk ceramic foams manifested an exciting combination of both high porosity above 96% and excellent specific compressive strength, due to their closed pore structure, defect-free cell wall with uniform thickness, and uniformly distributed zirconia grains in alumina matrix. The alumina/zirconia composite ceramic foams with porosity of 96.7% exhibited compressive strength of 1.11 ± 0.07 MPa, which was much higher than that of alumina ceramic foams in the case of same porosity. [ABSTRACT FROM AUTHOR]

Ultralight ceramics with striking mechanical properties and improved pore connectivity could have wide applications in areas ranging from catalyst support to hot gas filtration. However, creating such materials has proven to be a challenging target. This work demonstrated a novel methodology to prepare porous MgAl 2 O 4 ceramics by calcining gelled MgO–Al 2 O 3 –SiO 2 particle-stabilized foams. The striking green strength of dried foams can be achieved as a consequence of MgO hydration and subsequent formation of gelled Mg(OH) 2 and MgO–SiO 2 –H 2 O skeleton. The decomposition of colloidal substance at elevated temperature resulted in the formation of small pores on the cell wall, thus forming the hierarchical porous architecture and improving the pore connectivity. The highly porous MgAl 2 O 4 ceramics fired at 1600°C possessed the integrated properties of ultrahigh porosity (87.0%), improved pore connectivity and satisfactory compressive strength (7.93 MPa), showing great potential to be used in multiple industrial fields. [ABSTRACT FROM AUTHOR]

Abstract A facile method for preparation of SiC nanofibrous network reinforced hierarchical structured porous Si 3 N 4 based ceramics via annealing Si-Si 3 N 4 binary particle-stabilized foam in coke bed is reported in this work for the first time. The atmosphere created by coke bed enables the fabrication of Si 3 N 4 based porous ceramics at 1450 °C without using sintering additives. As prepared specimens possess a relative high compressive strength due to the partial oxidation of Si 3 N 4 particles. This novel structure with three levels of hierarchy characterized by flexible SiC nanofibrous network, cell walls and unit cells can be characterized. The vaporization of silicon powder results in formation of Si(g), SiO(g) and allows subsequent generation of SiC nanofibrous network, leading to a considerable number of micro-pores on cell walls simultaneously. As-prepared porous ceramics contained 76.7% porosity and had compressive strength of 10.81 MPa. [ABSTRACT FROM AUTHOR]