To design more environmentally friendly, economical, and efficient demulsifiers for oily wastewater treatment, hydrophobic octadecylphosphonic acid (ODPA)-modified Fe3O4 nanoparticles (referred to as Fe3O4@ODPA) were prepared by condensation of hydroxyl groups between ODPA and Fe3O4 nanoparticles using the co-precipitation method. The prepared magnetite nanoparticles were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscope (SEM), Fourier transform infrared (FTIR) spectroscopy, and thermogravimetric/differential thermogravimetric (TG/DTG) analysis. The water contact angles (θW) of Fe3O4@ODPA nanoparticles were more than 120°, indicating hydrophobic nature, and the diameter of the obtained spherical-shaped magnetite nanoparticles was 12–15 nm. The ODPA coating amount (AO) (coating weight per gram Fe3O4) and specific surface area (SO) of Fe3O4@ODPA were 0.124–0.144 g·g−1 and 78.65–91.01 m2·g−1, respectively. To evaluate the demulsification ability, stability, and reusability, the magnetite nanoparticles were used to demulsify an n-hexane-in-water nanoemulsion. The effects of the magnetite nanoparticle dosage (CS), pH value of nanoemulsion, and NaCl or CaCl2 electrolytes on the demulsification efficiency (RO) were investigated. The RO of Fe3O4@ODPA samples was found to be higher than that of bare Fe3O4 samples (S0, ST, and SN) under all CS values. With the increase in CS, the RO of Fe3O4@ODPA samples initially increased and then approached equilibrium value at Cs = 80.0 g·L−1. A maximum RO of ~93% was achieved at CS = 100.0 g·L−1 for the Fe3O4@ODPA sample S2. The pH and two electrolytes had a minor effect on RO. The Fe3O4@ODPA nanoparticles maintained high RO even after being reused for demulsification 11 times. This indicates that the hydrophobic Fe3O4@ODPA samples can be used as an effective magnetite demulsifer for oil-in-water nanoemulsions. [ABSTRACT FROM AUTHOR]

This study aims to examine the impact of the direct and indirect mixing techniques on the dispersion and homogeneity of magnesium oxide (MgO) and silver (Ag) nanoparticles (NPs) mixed with polymethylmethacrylate (PMMA). NPs were mixed with PMMA powder directly (non-ethanol-assisted) and indirectly (ethanol-assisted) with the aid of ethanol as solvent. X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDX), and scanning electron microscope (SEM) were used to evaluate the dispersion and homogeneity of MgO and Ag NPs within the PMMA-NPs nanocomposite matrix. Prepared discs of PMMA-MgO and PMMA-Ag nanocomposite were analyzed for dispersion and agglomeration by Stereo microscope. XRD showed that the average crystallite size of NPs within PMMA-NP nanocomposite powder was smaller in the case of ethanol-assisted mixing compared to non-ethanol-assisted mixing. Furthermore, EDX and SEM revealed good dispersion and homogeneity of both NPs on PMMA particles with ethanol-assisted mixing compared to the non-ethanol-assisted one. Again, the PMMA-MgO and PMMA-Ag nanocomposite discs were found to have better dispersion and no agglomeration with ethanol-assisted mixing when compared to the non-ethanol-assisted mixing technique. Ethanol-assisted mixing of MgO and Ag NPs with PMMA powder obtained better dispersion, better homogeneity, and no agglomeration of NPs within the PMMA-NP matrix. [ABSTRACT FROM AUTHOR]

In this paper, we discuss the preparation of Li-doped ZnO nanostructures through combustion and report on their structural, morphological, optical, and electrocatalysis properties. X-ray diffraction analyses show that the samples have a structure crystallized into the usual hexagonal wurtzite ZnO structure according to the P63mc space group. The scanning electron microscope images conceal all samples' nanosphere bundles and aggregates. The reflectance spectra analysis showed that the direct bandgap values varied from 3.273 eV (for pure ZnO, i.e., ZnL1) to 3.256 eV (for high Li-doped ZnO). The measured capacitance concerning frequency has estimated the variation of dielectric constant, dielectric loss, and AC conductivity against AC electric field frequency. The dielectric constant variations and AC conductivity are analyzed and discussed by well-known models such as Koop's phenomenological theory and Jonscher's law. The Raman spectra have been recorded and examined for the prepared samples. Rhodamine B was electro-catalytically degraded in all prepared samples, with the fastest time for ZnL5 being 3 min. [ABSTRACT FROM AUTHOR]

This work was aimed to assess the antidiabetic effect of orally administered Prosochit®-based nanoparticles of insulin in an animal model. Five batches of insulin-loaded nanoparticles were prepared as dry water-in-oil-in-water emulsions using different emulsifiers (prosopis gum, Prosochit® 201, Prosochit® 101, Prosochit® 102, and chitosan) for the outer emulsion. Unloaded Prosochit® 101-based nanoparticles were also formulated. The morphology and size distribution of the nanoparticles were studied using a scanning electron microscope and Zetasizer. Forty alloxan-induced diabetic Wistar rats were divided into eight groups. The different groups were administered daily with different formulations (unloaded nanoparticles, the 5 loaded nanoparticles equivalent to 50 IU insulin per kg, purified water, and Actrapid) for 14 days. Blood glucose level was monitored and determined over 24 h. Fasting blood sugar was also taken on days 3, 5, 7, and 14. A graph of the percent blood glucose level relative to time 0 h was plotted against time. The particles showed a water-in-oil-in-water constitution. Both the drug-loaded and the unloaded Prosochit®-based nanoparticles were of nano dimension. There was a significant difference (p < 0.0001) in the antidiabetic effects of all insulin-loaded nanoparticles compared with the negative control. There was no significant difference across the insulin-loaded nanoparticles of prosopis gum, Prosochit® 201, Prosochit® 102, and chitosan while the insulin-loaded Prosochit® 101 nanoparticles showed the best activity, which is comparable to subcutaneous insulin, reducing blood glucose levels to 32.20 ± 3.79%. All the oral Prosochit®-based insulin nanoparticles are characterized by appreciable antidiabetic activity with the activity of Prosochit® 101-based nanoformulation being comparable to that of the subcutaneous insulin. [ABSTRACT FROM AUTHOR]

In this paper, inorganic oxide MgO nanoparticles-doped polymer dispersed liquid crystal (PDLC) films were made from a mixture of the prepolymer, SLC1717 liquid crystal, and MgO nanoparticles by the polymerization induced phase separation (PIPS) process. To observe the effect of MgO concentration, PDLC was dispersed with 0.2, 0.4, 0.6, and 0.8 wt.% MgO. Electro-optical properties of the films have been investigated using LCD parameter meter and Scanning Electron Microscope (SEM) at room temperature. It is established that MgO nanoparticles affect the microstructure of PDLC films significantly because of the formed agglomerates of MgO nanoparticles. Results show an improvement in the electro-optical properties and a decrease in the driving voltage for doped systems with MgO nanoparticles. When the doping amount of MgO is 0.8 wt.%, the threshold voltage (Vth) is reduced to about 7.5 V. Therefore, MgO-doped PDLC is expected to become an excellent choice in the field of energy-saving. [ABSTRACT FROM AUTHOR]

Soft reliner and glaze are materials used over full or partial dental prosthesis to prevent excessive pressure on the supporting tissues. They are also indicated as supportive treatment for dental stomatitis, especially when modified by the addition of medications. The objective of the work was to evaluate the antimicrobial effect of silver-coated silica nanoparticles in a glaze and a soft reliner. The nanoparticles were synthesized, characterized, and tested by minimum inhibitory concentration (MIC) for C. albicans SC5314. Then, the nanoparticles were incorporated to a glaze and a soft reliner, which were called nanocomposites. Then, the nanocomposites were divided into six groups (n = 12): CG: glaze/reliner; CR: reliner; G1: glaze + 1% nanoparticles/reliner; G2: glaze + 2.5% nanoparticles/reliner; R1: reliner + 1%; R2: reliner + 2.5%. The nanocomposites were characterized by a goniometer and by a scanning electron microscope. The antibiofilm test was performed against C. albicans SC5314. According to the MIC results, the non-functionalized nanoparticles reduced fungal growth at 1000 μg/mL and the functionalized nanoparticles at 2000 μg/mL. The functionalized nanoparticle had a superior dispersion being selected for the antibiofilm test. There was a reduction of 64% in CFU/specimen count for the glaze, not statistically significant (p = 0.244). For the soft reliner, there was an increase in CFU/specimen with the presence of nanoparticles, still not statistically significant (p = 0.264). In conclusion, it is necessary to conduct new studies to increase the release of silver, thus improving nanoparticles' antifungal potential. [ABSTRACT FROM AUTHOR]

Staphylococcus aureus (S. aureus) is a Gram-positive bacteria considered one of the leading causes of community and hospital-acquired illnesses or public health concerns. Antibiotic resistance in this microorganism is one of the greatest issues in global health care. The use of metal nanoparticles and their oxides is one of the potential approaches to combating bacteria resistance to antibiotics. The antibacterial properties of ZnO NPs against enterotoxigenic S. aureus were studied. ZnO NPs were tested in vitro by agar diffusion test. They resulted in 26 and 22 mm zones of inhibition for a size of 20 nm and a concentration of 20 mM against 105 and 107 CFU/mL S. aureus, respectively. The MIC of ZnO NPs of various sizes, 20 and 50 nm, with 105 CFU/mL was 2.5 and 5 mM, respectively. MIC with 107 CFU/mL was five mM for 20 and 50 nm ZnO NPs. Further, the highest growth reduction percentage, 98.99% in the counts of S. aureus was achieved by ZnO NPs of size 20 nm and concentration of 10 mM. Moreover, the obtained ELISA results indicated a significantly decreased concentration of enterotoxin A with all concentrations and sizes of ZnO NPs. PCR analysis showed a significant effect on sea gene in response to ZnO NPs treatments leading to loss of the gene, unlike the unaffected nuc gene. Moreover, morphological changes and cell shape distortion were detected by scanning electron microscope for bacterial cells treated with ZnO NPs. [ABSTRACT FROM AUTHOR]

Biofilms are matrix-enclosed communities of bacteria that are highly resistant to antibiotics. Adding nanomaterials with antibacterial activity to the implant surfaces may be a great solution against biofilm formation. Due to its potent and widespread antibacterial effect, silver nanoparticles were considered the most potent agent with different biological activities. In the present investigation, silver nanoparticles (AgNPs) were newly synthesized as antibiofilm agents using sugarcane process byproduct (molasses) and named Mo-capped AgNPs. The synthesized nanoparticles showed promising antimicrobial activity against S. aureus ATCC 6538 and C. albicans DAY185. Statistically designed optimization through response surface methodology was evaluated for maximum activity and better physical characteristics, namely the nanoparticles' size and polydispersity index (PDI), and it was revealed that molasses concentration was the main effective factor. Minimal biofilm eradication concentration (MBEC) of Mo-capped AgNPs against S. aureus ATCC 6538 and C. albicans DAY185 was 16 and 32 µg/mL, respectively. Scanning electron microscope study of Mo-capped AgNP-treated biofilm revealed that AgNPs penetrated the preformed biofilm and eradicated the microbial cells. The optimally synthesized Mo-capped AgNPs were spherically shaped, and the average size diameter ranged between 29 and 88 nm with high proportions of Ag+ element (78.0%) recorded. Fourier-transform infrared spectroscopy (FTIR) analysis indicated the importance of molasses ingredients in capping and stabilizing the produced silver nanoparticles. [ABSTRACT FROM AUTHOR]

This study aims at the characterisation of red and orange glass tesserae from the 4th-century Roman villa of Noheda (Spain). Due to the limited number of analyses available for such ancient materials, many questions remain unanswered about the production processes in the Roman period. Six samples were chosen for their hue variations, including two samples showing banded patterns of red and orange. Differences in copper speciation were investigated by X-ray absorption spectroscopy and compared with colour and compositional variations obtained by EPMA. The shapes and sizes of colouring crystals could be investigated using scanning and transmission electron microscope imaging. The brown-red colour is due to metallic copper nano-particles and corresponds to a low-copper and low-lead group usually described in the literature. The orange samples and bands are coloured by copper oxide C u 2 O nanoparticles with remaining Cu+ in the glass and have greater contents of Cu. Compositional analyses reveal that the same base glass is used in the red and orange bands with additions of Cu, Sn, Pb and probable Fe. Furthermore, based on our results and on the literature review, a high-copper low-lead group of glasses highlights the variability of compositions observed in cuprite colours. [ABSTRACT FROM AUTHOR]

This article attempts to highlight a phenomenon that more or less permanently damages emulsion paint layers, the surfaces of which remain sufficiently permeable for dust particles to become permanently anchored there; when the particles are nanometric, this can cause a permanent change in appearance. Based on scientific documents, empirical observations, laboratory analyses, case studies, and reconstructions of characteristic pictorial layers, this paper aims to highlight the medium- and long-term risks that alter these surfaces, in order to realize strategies for better prevention. The physico-chemical nature of these vulnerable materials will be discussed first, followed by the dust's involvement; finally, the topic will be illustrated through concrete examples, with photos taken using digital, 4 K optical, and Scanning Electron Microscope equipment (SEM), in order to show how the problem of dust particle accumulation impacts even the most contemporary works of art. [ABSTRACT FROM AUTHOR]

The metabolites of the fungal strain Rhizopus oryaze were used as a biocatalyst for the green-synthesis of magnesium oxide nanoparticles (MgO-NPs). The production methodology was optimized to attain the maximum productivity as follows: 4 mM of precursor, at pH 8, incubation temperature of 35 °C, and reaction time of 36 h between metabolites and precursor. The as-formed MgO-NPs were characterized by UV-Vis spectroscopy, TEM, SEM-EDX, XRD, DLS, FT-IR, and XPS analyses. These analytical techniques proved to gain crystalline, homogenous, and well-dispersed spherical MgO-NPs with an average size of 20.38 ± 9.9 nm. The potentiality of MgO-NPs was dose- and time-dependent. The biogenic MgO-NPs was found to be a promising antimicrobial agent against the pathogens including Staphylococcus aureus, Bacillus subtilis, Pseudomonas aeruginosa, Escherichia coli, and Candida albicans with inhibition zones of 10.6 ± 0.4, 11.5 ± 0.5, 13.7 ± 0.5, 14.3 ± 0.7, and 14.7 ± 0.6 mm, respectively, at 200 μg mL–1. Moreover, MgO-NPs manifested larvicidal and adult repellence activity against Culex pipiens at very low concentrations. The highest decolorization percentages of tanning effluents were 95.6 ± 1.6% at 100 µg/ 100 mL after 180 min. At this condition, the physicochemical parameters of tannery effluents, including TSS, TDS, BOD, COD, and conductivity were reduced with percentages of 97.9%, 98.2%, 87.8%, 95.9%, and 97.3%, respectively. Moreover, the chromium ion was adsorbed with percentages of 98.2% at optimum experimental conditions. [ABSTRACT FROM AUTHOR]

A correction has been made to Figure 1 to show the morphology of ambient nanoparticles in Chiang Mai, Thailand, as observed in the scanning electron microscope (SEM) analysis [[2]] - the newly added reference 92. Ambient Nanoparticles (PM 0.1) Mapping in Thailand. A correction has been made to "Phairuang et al. (2021) [32], reported on the source apportionment of PM SB 0.1 sb particles in Bangkok", the updated one should be "Phairuang et al. (2021) [53], reported on the source apportionment of PM SB 0.1 sb particles in Bangkok". [Extracted from the article]

Ceria nanoparticles (CeO2 NPs) are generally considered in various functional applications, such as catalysts in fuel cells, sensors, and antioxidant and oxidase-like enzymes in the biological environment. The CeO2 NPs were synthesized using the E. globulus leaf extract-mediated hydrothermal technique. The synthesized NPs were characterized by various analytical instruments including powder X-ray diffractometer (PXRD), scanning electron microscope (SEM), transmission electron microscope (TEM) and dynamic light scattering (DLS) analysis. The XRD results showed an average NPs sizes of 13.7 nm. Cytotoxic study results showed an IC50 value of 45.5 µg/L for A549 and 58.2 µg/L for HCT 116, indicating that CeO2 NPs are more toxic to A549 compared to HCT116 cell lines. The generation of ROS was responsible for its cytotoxic activity against cancer cell lines. Specific surface area (40.96 m2/g) and pore diameter (7.8 nm) were measured using Brunauer-Emmett-Teller (BET) nitrogen adsorption-desorption isotherms. CeO2 NPs with a high surface area were used as photocatalyst in degrading sunset yellow (SY) dye under UV-irradiation and 97.3% of the dye was degraded within 90 min. These results suggest that the synthesized CeO2 NPs could be used as a good photocatalyst as well as a cytotoxic agent against human cancer cell lines. [ABSTRACT FROM AUTHOR]

Skin loss is one of the oldest and still not totally resolved problems in the medical field. Since spontaneous healing of the dermal defects would not occur, the regeneration of full thickness of skin requires skin substitutes. Tissue engineering constructs would provide a three dimensional matrix for the reconstruction of skin tissue and the repair of damage. The aim of the present work is to develop a chitin based scaffold, by blending it with poly(butylene succinate) (PBS), an aliphatic, biodegradable and biocompatible synthetic polymer with excellent mechanical properties. The presence of chondroitin sulfate nanoparticles (CSnp) in the scaffold would favor cell adhesion. A chitin/PBS/CSnp composite hydrogel scaffold was developed and characterized by SEM (Scanning Electron Microscope), FTIR (Fourier Transform Infrared Spectroscopy), and swelling ratio of scaffolds were analyzed. The scaffolds were evaluated for the suitability for skin tissue engineering application by cytotoxicity, cell attachment, and cell proliferation studies using human dermal fibroblasts (HDF). The cytotoxicity and cell proliferation studies using HDF confirm the suitability of the scaffold for skin regeneration. In short, these results show promising applicability of the developed chitin/PBS/CSnps ternary composite hydrogel scaffolds for skin tissue regeneration. [ABSTRACT FROM AUTHOR]

Enhancement of the production yield of boron nitride nanotubes (BNNTs) with high purity was achieved using an amorphous boron-based precursor and a nozzle-type reactor. Use of a mixture of amorphous boron and Fe decreases the milling time for the preparation of the precursor for BNNTs synthesis, as well as the Fe impurity contained in the B/Fe interdiffused precursor nanoparticles by using a simple purification process. We also explored a nozzle-type reactor that increased the production yield of BNNTs compared to a conventional flow-through reactor. By using a nozzle-type reactor with amorphous boron-based precursor, the weight of the BNNTs sample after annealing was increased as much as 2.5-times with much less impurities compared to the case for the flow-through reactor with the crystalline boron-based precursor. Under the same experimental conditions, the yield and quantity of BNNTs were estimated as much as ~70% and ~1.15 g/batch for the former, while they are ~54% and 0.78 g/batch for the latter. [ABSTRACT FROM AUTHOR]

Magnesium alloys are attractive for the production of lightweight parts in modern automobile and aerospace industries due to their advanced properties. Their mechanical properties are usually enhanced by the incorporation with reinforcement particles. In the current study, reinforced AZ31 magnesium alloy was fabricated through the addition of bulk Al and the incorporation of SiC nanoparticles using a stir casting process to obtain AZ31-SiC nanocomposites. Scanning electron microscope (SEM) investigations revealed the formation of Mg17Al12 lamellar intermetallic structures and SiC clusters in the nanocomposites. Energy dispersive spectroscopy (EDS) detected the uniform distribution of SiC nanoparticles in the AZ31-SiC nanocomposites. Enhancements in hardness and yield strength (YS) were detected in the fabricated nanocomposites. This behavior was referred to a joint strengthening mechanisms which showed matrix-reinforcement coefficient of thermal expansion (CTE) and elastic modulus mismatches, Orowan strengthening, and load transfer mechanism. The mechanical properties and wear resistance were gradually increased with an increase in SiC content in the nanocomposite. The maximum values were obtained from nanocomposites containing 1 wt% of SiC (AZ31-1SiC). AZ31-1SiC nanocomposite YS and hardness were improved by 27% and 30%, respectively, compared to AZ31 alloy. This nanocomposite also exhibited the highest wear resistance; its wear mass loss and depth of the worn surface decreased by 26% and 15%, respectively, compared to AZ31 alloy. [ABSTRACT FROM AUTHOR]

Electrocatalytic water splitting is a promising solution to resolve the global energy crisis. Tuning the morphology and particle size is a crucial aspect in designing a highly efficient nanomaterials-based electrocatalyst for water splitting. Herein, green synthesis of nickel oxide nanoparticles using phytochemicals from three different sources was employed to synthesize nickel oxide nanoparticles (NiOx NPs). Nickel (II) acetate tetrahydrate was reacted in presence of aloe vera leaves extract, papaya peel extract and dragon fruit peel extract, respectively, and the physicochemical properties of the biosynthesized NPs were compared to sodium hydroxide (NaOH)-mediated NiOx. Based on the average particle size calculation from Scherrer's equation, using X-ray diffractograms and field-emission scanning electron microscope analysis revealed that all three biosynthesized NiOx NPs have smaller particle size than that synthesized using the base. Aloe-vera-mediated NiOx NPs exhibited the best electrocatalytic performance with an overpotential of 413 mV at 10 mA cm−2 and a Tafel slope of 95 mV dec−1. Electrochemical surface area (ECSA) measurement and electrochemical impedance spectroscopic analysis verified that the high surface area, efficient charge-transfer kinetics and higher conductivity of aloe-vera-mediated NiOx NPs contribute to its low overpotential values. [ABSTRACT FROM AUTHOR]

The effect of copper oxide and zinc oxide nanoparticles (NPs) on the mechanical and thermal properties of ground waste concrete inorganic polymers (GWC IPs) has been investigated. NPs are added to GWC IPs at loadings of 0.1, 0.5, 1, and 2% w/w. The phase composition and microstructure of NPs GWC IPs have also been examined using X-ray diffraction (XRD), Raman spectroscopy and scanning electron microscope (SEM/EDS) techniques. Results show that the mechanical properties of GWC IPs are improved (23 MPa) due to addition of NPs (1% ZnO). In particular, GWC IPs embedded with 0.5% CuO and 1% ZnO NPs exhibited relatively improved compressive strength. The addition of NPs decreases the macroporosity and increases the mesoporosity of IPs matrix and decreases relatively the ability of IPs matrix to water absorption. The antimicrobial activity of GWC IPs doped with 0.5 and 1% CuO NPs against E. coli was also determined. [ABSTRACT FROM AUTHOR]

Control over both dispersion and the particle size distribution of supported metal particles is of paramount importance for the catalytic activity of composite materials. We describe the synthesis of materials with Cu nanoparticles well-dispersed on different amine-functionalized supports, using the extract of Wallich Spurge as a green, reducing agent. Graphene oxide (GO), mesoporous silica (MCM-41), mesoporous zirconia, and reduced graphene oxide-mesoporous silica (RGO-MCM-41) were explored as supports. Cu nanoparticles were better stabilized on RGO-MCM-41 compared to other supports. The novel composite materials were characterized by X-ray diffraction (XRD), Raman spectra, Scanning electron microscope (SEM), Transmission electron microscopy analysis and HR-TEM. SEM and EDX techniques. High angle XRD confirmed the conversion of graphene oxide to reduced graphene oxide (RGO) with plant extract as a reducing agent. Both XRD and TEM techniques confirmed the Cu nanoparticle formation. The catalytic activity of all the prepared materials for the Ullmann coupling reactions of carbon-, oxygen-, and nitrogen-containing nucleophiles with iodobenzene was evaluated. From the results, 5 wt% Cu on amine-functionalized reduced graphene oxide/mesoporous silica nanocomposite (5 wt%Cu(0)-AAPTMS@RGO-MCM-41) exhibited excellent efficiency with 97% yield of the C-C coupling product in water at 80 °C in 5 h. The activity remained unaltered almost up to the fourth cycle. The Cu nanoparticles stabilized by organic amine group on RGO hybrid facilitated sustained activity. [ABSTRACT FROM AUTHOR]

Nanocomposite film of poly(vinyl alcohol) (PVA) incorporated with bacterial cellulose nanocrystals (BCNCs) and magnetite nanoparticles (Fe3O4) is reported in this study. The BCNC-Fe3O4 nanoparticles and PVA film was prepared by in situ synthesis technique using chemical co-precipitation. Different concentrations of BCNC-Fe3O4 (20%, 40% and 60% w/w) were mechanically dispersed in PVA solution to form the nanocomposite film. Transmission electron microscopy (TEM) analysis of BCNC-Fe3O4 nanoparticles showed irregular particle sizes ranging from 4.93 to 30.44 nm with an average size distribution of 22.94 nm. The presence of characteristic functional groups of PVA, BCNC and Fe3O4 were confirmed by Fourier transform infrared (FTIR) spectroscopy and X-ray diffraction (XRD) analysis. Scanning electron microscope (SEM) attached energy dispersive spectroscopy (EDS) and vibrating sample magnetometer (VSM) analysis revealed that, the iron content and magnetic property increased with increasing BCNC-Fe3O4 content. The saturation magnetizations (MS) value increased from 5.14 to 11.56 emu/g. The PVA/ BCNC-Fe3O4 at 60% showed the highest Young's modulus value of 2.35 ± 0.16 GPa. The prepared film could be a promising polymeric nanomaterial for various magnetic-based applications and for the design of smart electronic devices. [ABSTRACT FROM AUTHOR]

The droplet evaporation effect on the preparation of polyetherimide (PEI) nanoparticles by thermally induced phase separation (TIPS) was studied. PEI nanoparticles were prepared in two routes. In route I, the droplet evaporation process was carried out after TIPS. In route II, the droplet evaporation and TIPS processes were carried out simultaneously. The surface tension and shape parameters of samples were measured via a drop shape analyzer. The Z-average particle diameter of PEI nanoparticles in the PEI/dimethyl sulfoxide solution (DMSO) suspension at different time points was tested by dynamic light scattering, the data from which was used to determine the TIPS time of the PEI/DMSO solution. The natural properties of the products from both routes were studied by optical microscope, scanning electron microscope and transmission electron microscope. The results show that PEI nanoparticles prepared from route II are much smaller and more uniform than that prepared from route I. Circulation flows in the droplet evaporation were indirectly proved to suppress the growth of particles. At 30 °C, PEI solid nanoparticles with 193 nm average particle size, good uniformity, good separation and good roundness were obtained. Route I is less sensitive to temperature than route II. Samples in route I were still the accumulations of micro and nanoparticles until 40 °C instead of 30 °C in route II, although the particle size distribution was not uniform. In addition, a film structure would appear instead of particles when the evaporation temperature exceeds a certain value in both routes. This work will contribute to the preparation of polymer nanoparticles with small and uniform particle size by TIPS process from preformed polymers. [ABSTRACT FROM AUTHOR]

In the present study, biocompatible manganese nanoparticles have been linked with zinc and iron molecules to prepare different derivatives of Mn0.5Zn0.5ErxYxFe2−2xO4 NPs (x = 0.02, 0.04, 0.06, 0.08, 0.10), using an ultrasonication approach. The structure, surface morphology, and chemical compositions of Mn0.5Zn0.5ErxYxFe2−2xO4 NPs were elucidated by X-ray diffractometer (XRD), High-resolution transmission electron microscopy (HR-TEM), scanning electron microscope (SEM), and Energy Dispersive X-Ray Analysis (EDX) techniques. The bioactivity of Mn0.5Zn0.5ErxYxFe2−2xO4 NPs on normal (HEK-293) and (HCT-116) colon cancer cell line was evaluated. The Mn0.5Zn0.5ErxYxFe2−2xO4 NPs treatment post 48 h resulted in a significant reduction in cells (via MTT assay, having an IC50 value between 0.88 µg/mL and 2.40 µg/mL). The specificity of Mn0.5Zn0.5ErxYxFe2−2xO4 NPs were studied by treating them on normal cells line (HEK-293). The results showed that Mn0.5Zn0.5ErxYxFe2−2xO4 NPs did not incur any effect on HEK-293, which suggests that Mn0.5Zn0.5ErxYxFe2−2xO4 NPs selectively targeted the colon cancerous cells. Using Candida albicans, antifungal activity was also studied by evaluating minimum inhibitory/fungicidal concentration (MIC/MFC) and the effect of nanomaterial on the germ tube formation, which exhibited that NPs significantly inhibited the growth and germ tube formation. The obtained results hold the potential to design nanoparticles that lead to efficient bioactivity. [ABSTRACT FROM AUTHOR]

This paper studied the effect of additives of 0.5–20 wt.% synthetic CaSiO3 wollastonite on the thermodynamic, mechanical, and tribological characteristics and structure of polymer composite materials (PCM) based on ultra-high-molecular weight polyethylene (UHMWPE). Using thermogravimetric analysis, X-ray fluorescence, scanning electron microscope, and laser light diffraction methods, it was shown that autoclave synthesis in the multicomponent system CaSO4·2H2O–SiO2·nH2O–KOH–H2O allows one to obtain neeindle-shaped nanosized CaSiO3 particles. It was shown that synthetic wollastonite is an effective filler of UHMWPE, which can significantly increase the deformation-strength and tribological characteristics of PCM. The active participation of wollastonite in tribochemical reactions occurring during friction of PCM by infrared spectroscopy was detected: new peaks related to oxygen-containing functional groups (hydroxyl and carbonyl) appeared. The developed UHMWPE/CaSiO3 materials have high wear resistance and can be used as triboengineering materials. [ABSTRACT FROM AUTHOR]

The effect of various combinations of filler materials on the performance of polypropylene (PP)-based composites was investigated. PP in particulate form was used as the matrix. Milled short carbon fiber (SCF) micro-size, graphite nano-platelet (GNP), and titanium dioxide nanoparticles (nTiO2) were used as fillers. These fillers were incorporated in the polymer matrix to produce mono-filler (PP/SCF and PP/nanofiller) and hybrid composites. Hybrid composites consist of PP/10SCF/GNP, PP/10SCF/nTiO2, and PP/10SCF/GNP/nTiO2. The effect of the addition of SCF, GNP, and nTiO2 on PP-based composites was investigated by analyzing their morphological, mechanical, and physical properties. The addition of mono-filler to the PP matrix improved the mechanical properties of the composites when compared to the neat PP. The ultimate tensile strength (UTS), flexural modulus, flexural strength, and impact toughness of the hybrid composites with 15 wt % total loading of fillers, were higher than that of mono-filler composites with 15 wt % SCF (PP/15SCF). A maximum increase of 20% in the flexural modulus was observed in the hybrid composite with 10 wt % of SCF with the additional of 2.5 wt % GNP and 2.5 wt % nTiO2 when compared to PP/15SCF composite. The addition of 2.5 wt % nTiO2 to the 10 wt % SCF reinforced PP, resulted in increasing the strain at break by 15% when compared to the PP/10SCF composite. A scanning electron microscope image of the PP/10SCF composite with the addition of GNP improved the interfacial bonding between PP and SCF compared with PP/SCF alone. A decrease in the melt flow index (MFI) was observed for all compositions. However, hybrid composites showed a higher decrease in MFI. [ABSTRACT FROM AUTHOR]

A binary carbonate salt eutectic (Li2CO3-K2CO3)-based nanofluid was in situ synthesized by mixing with a precursor material, aluminum nitrate nonahydrate (Al(NO3)3·9H2O). Thermal decomposition of the precursor was successfully carried out to synthesize alumina (Al2O3) nanoparticles at 1 wt.% concentration. A thermogravimetric analysis (TGA) confirmed a complete thermal decomposition of aluminum nitrate nonahydrate to alumina nanoparticles. A transmission electron microscope (TEM) was employed to confirm the size and shape of the in situ formed nanoparticles; the result showed that they are spherical in shape and the average size was 28.7 nm with a standard deviation of 11.7 nm. Electron dispersive X-ray spectroscopy (EDS) confirmed the observed nanoparticles are alumina nanoparticles. A scanning electron microscope (SEM) was employed to study microstructural changes in the salt. A differential scanning calorimeter (DSC) was employed to study the heat capacity of the in situ synthesized nanofluid. The result showed that the heat capacity was enhanced by 21% at 550 °C in comparison with pure carbonate salt eutectic. About 10–11 °C decrease of the onset melting point of the binary carbonate salt eutectic was observed for the in situ synthesized nanofluids. [ABSTRACT FROM AUTHOR]

This study assessed the antimicrobial efficacy of synthesized zinc oxide nanoparticles produced using aqueous extracts of pomegranate leaves and flowers designated ZnO-NPs-PL, ZnO-NPs-PF. In the study, oxides of zinc were successfully employed to fabricate nanoparticles using extracts from leaves and flowers of pomegranate (Punica granatum). The nanoparticles obtained were characterized spectroscopically. X-ray diffractive analysis (XRD) revealed the elemental components and nature of the synthesized particles. The fabricated zinc oxide nanoparticle (ZnO-NPs) showed a crystalline structure. The morphology of the nanoparticles as shown by scanning electron microscopy (SEM) was unevenly spherical and the functional groups involved in stabilization, reduction and capping were confirmed using Fourier Transform Infra-Red (FT-IR) Spectroscopy. Confirmation of the nanoparticles by UV–Vis analysis showed absorption bands of 284 and 357 nm for pomegranate leaf and flower extract, respectively, mediated ZnO-NPs. Evaluation of the antimicrobial efficacy of the fabricated nanoparticles showed that ZnO-NPs were effective against all selected pathogenic strains, Staphylococcus aureus, Bacillus cereus, Pseudomonas aeruginosa, Klebsiella pneumoniae, Streptococcus pneumoniae, Salmonella diarizonae, Salmonella typhi, Enterococcus faecalis, Enterococcus faecium, Escherichia coli, Moraxella catarrhalis, Aeromonas hydrophila and Listeria monocytogenes, used in the analysis. The effectiveness of these nanoparticles could be linked to their sizes and shapes as obtained using a transmission electron microscope (TEM) and scanning electron microscope (SEM). Our reports revealed that increasing the concentration of the nanoparticles resulted in an increase in the antibacterial activity exerted by the nanoparticles, thus suggesting that both ZnO-NPs can effectively be used as alternative antibacterial agents. Further research is required to assess their mechanisms of action and toxicity. [ABSTRACT FROM AUTHOR]

The article discusses a study on the synthesis of tri-n-octylphosphine oxide (TOPO)-coated CdSe/ZnS microparticles. The study used an optical microscope and a scanning electron microscope in characterizing the microparticles. It found more than 100 particles to ensure a statistically representative size. It also examined the effect of organic solvents on the microparticles.

Parkinson's disease (rp) is a progressive neurodegenerative disorder. Ropinirole (RP) is a newer generation dopamine agonist used for the treatment of PD. It is prescribed as oral dosage form. However, limited oral bioavailability and frequent dosing limits the RP usage. The objective of the current investigation was to develop, optimize, evaluate pharmacokinetic (PK) and pharmacodynamic (PCD) activity of RP loaded solid lipid nanoparticles (RP-SLNs) and nanostructured lipid carriers (RP-NLCs) and containing hydrogel (RP-SLN-C and RP-NLC-C) formulations for improved oral and topical delivery. RP loaded lipid nanoparticles were optimized and converted to hydrogel using carbopol 934 as the gelling polymer. PK and PCD studies in haloperidol-induced PD were conducted in male Wistar rats. In vitro and ex vivo permeation studies showed sustained release profile and enhanced permeation compared with control formulations. Differential scanning calorimeter and X-ray diffraction studies revealed amorphous transformation; scanning electron microscope showed the spherical shape of RP in lipid nanoparticles. PK studies showed 2.1 and 2.7-folds enhancement from RP-SLN and RP-NLC from oral administration, 3.0 and 3.3-folds enhancement from RP-SLN-C and RP-NLC-C topical administration, compared with control formulations, respectively. RP-SLN-C and RP-NLC-C showed 1.4 and 1.2-folds topical bioavailability enhancement compared with RP-SLN and RP-NLC oral administration, respectively. PCD studies showed enhanced dopamine, glutathione, catalase levels and reduced lipid peroxidation levels, compared with the haloperidol-induced PD model. Overall, the results demonstrated that lipid nanoparticles and corresponding hydrogel formulations can be considered as an alternative delivery approach for the improved oral and topical delivery of RP for the effective treatment of PD. [ABSTRACT FROM AUTHOR]

Antimicrobial medicine and food packages based on bio-based film containing essential oils have attracted great attention worldwide. However, the controlled release of essential oils from these film nanocomposites is still a big challenge. In this study, a long-term antibacterial film nanocomposite composed of zein film and cinnamon essential oil (CEO) loaded MCM-41 silica nanoparticles was prepared. The CEO was loaded into MCM-41 particles via modified supercritical impregnation efficiently with a high drug load (>40 wt%). The morphologies of the prepared nanoparticles and film nanocomposite were characterized by a scanning electron microscope. The release behaviors of CEO under different temperatures, high humidity, continuous illumination and in phosphate buffer solution (PBS) solution were investigated. The results showed that the film nanocomposite had an outstanding release-control effect. The addition of MCM-41 nanoparticles also improved the mechanical properties of zein films. The antibacterial effect of CEO was significantly prolonged by the film nanocomposite; indicating the CEO film nanocomposite fabricated via modified supercritical CO2 impregnation was a potential long-term antibacterial medicine or food package material. [ABSTRACT FROM AUTHOR]

In order to study the effect of nano-CeO2 particles doping on the electrochemical corrosion behavior of pure Ni-Fe-Co-P alloy coating, Ni-Fe-Co-P-CeO2 composite coating is prepared on the surface of 45 steel by scanning electrodeposition. The morphology, composition, and phase structure of the composite coating are analyzed by means of scanning electron microscope (SEM), energy dispersive spectroscopy (EDS), and X-ray diffraction (XRD). The corrosion behavior of the coatings with different concentrations of nano-CeO2 particles in 50 g/L NaCl solution is studied by Tafel polarization curve and electrochemical impedance spectroscopy. The corrosion mechanism is discussed. The experimental results show that the obtained Ni-Fe-Co-P-CeO2 composite coating is amorphous, and the addition of nano-CeO2 particles increases the mass fraction of P. With the increase of the concentration of nano-CeO2 particles in the plating solution, the surface flatness of the coating increases. The surface of Ni-Fe-Co-P-1 g/L CeO2 composite coating is uniform and dense, and its self-corrosion potential is the most positive; the corrosion current and corrosion rate are the smallest, and the charge transfer resistance is the largest, showing the best corrosion resistance. [ABSTRACT FROM AUTHOR]

This study report on the synthesis of spinel CuFe2O4 nanostructures by surfactant-assisted method. The catalysts were characterized by X-ray diffraction (XRD), laser Raman, transition electron microscope (TEM), scanning electron microscope (SEM), energy dispersive X-ray (EDX), hydrogen temperature programmed reduction (H2-TPR), and Brunauer-Teller-Emmett-Teller (BET) surface area techniques. CuFe2O4 was active for pinene oxidation using tertiary butyl hydroperoxide (TBHP) to pinene oxide, verbenol, and verbenone aroma oxygenates. Under optimized reaction conditions, the spinel CuFe2O4 catalyst could afford 80% pinene conversion at a combined verbenol/verbenone selectivity of 76% within the reaction time of 20 h. The changes in catalyst synthesis solvent composition ratios induced significantly varying redox, phases, and textural structure features, which resulted in various catalytic enhancement effect. Characterization results showed the spinel CuFe2O4 catalyst possessing less than 5 wt% impurity phases, Cu(OH)2, and CuO to afford the best catalytic performance. The CuFe2O4 catalyst was recyclable to up to five reaction cycles without loss of its activity. The recyclability of the bimetal CuFe2O4 oxide catalyst was simply rendered by use of an external magnet to separate it from the liquid solution. [ABSTRACT FROM AUTHOR]

Acrylic resin PMMA (poly-methyl methacrylate) is used in the manufacture of denture bases but its mechanical properties can be deficient in this role. This study investigated the mechanical properties (flexural strength, fracture toughness, impact strength, and hardness) and fracture behavior of a commercial, high impact (HI), heat-cured denture base acrylic resin impregnated with different concentrations of yttria-stabilized zirconia (ZrO2) nanoparticles. Six groups were prepared having different wt% concentrations of ZrO2 nanoparticles: 0% (control), 1.5%, 3%, 5%, 7%, and 10%, respectively. Flexural strength and flexural modulus were measured using a three-point bending test and surface hardness was evaluated using the Vickers hardness test. Fracture toughness and impact strength were evaluated using a single edge bending test and Charpy impact instrument. The fractured surfaces of impact test specimens were also observed using a scanning electron microscope (SEM). Statistical analyses were conducted on the data obtained from the experiments. The mean flexural strength of ZrO2/PMMA nanocomposites (84 ± 6 MPa) at 3 wt% zirconia was significantly greater than that of the control group (72 ± 9 MPa) (p < 0.05). The mean flexural modulus was also significantly improved with different concentrations of zirconia when compared to the control group, with 5 wt% zirconia demonstrating the largest (23%) improvement. The mean fracture toughness increased in the group containing 5 wt% zirconia compared to the control group, but it was not significant. However, the median impact strength for all groups containing zirconia generally decreased when compared to the control group. Vickers hardness (HV) values significantly increased with an increase in ZrO2 content, with the highest values obtained at 10 wt%, at 0 day (22.9 HV0.05) in dry conditions when compared to the values obtained after immersing the specimens for seven days (18.4 HV0.05) and 45 days (16.3 HV0.05) in distilled water. Incorporation of ZrO2 nanoparticles into high impact PMMA resin significantly improved flexural strength, flexural modulus, fracture toughness and surface hardness, with an optimum concentration of 3–5 wt% zirconia. However, the impact strength of the nanocomposites decreased, apart from the 5 wt% zirconia group. [ABSTRACT FROM AUTHOR]