Search

Kowalska et al. [[17]] report near-IR luminescence properties of selected rare-Earth ions (Er SP 3+ sp , Pr SP 3+ sp , Ho SP 3+ sp , Tm SP 3+ sp ) in titanate-germanate glasses under excitation of Yb SP 3+ sp . 35683100 17 Kowalska K., Kuwik M., Pisarska J., Pisarski W.A. Near-IR luminescence of rare-earth ions (Er3+, Pr3+, Ho3+, Tm3+) in titanate-germanate glasses under excitation of Yb3+. Rare-Earth ions, as optically active ions, are usually incorporated into the crystalline phases. [Extracted from the article]

This paper deals with broadband near-infrared luminescence properties of lead germanate glass triply doped with Yb3+/Er3+/Tm3+. Samples were excited at 800 nm and 975 nm. Their emission intensities and lifetimes depend significantly on Er3+ and Tm3+ concentrations. For samples excited at 800 nm, broadband emissions corresponding to the overlapped 3H4 → 3F4 (Tm3+) and 4I13/2 → 4I15/2 (Er3+) transitions centered at 1.45 µm and 1.5 µm was identified. Measurements of decay curves confirm reduction of 3H4 (Tm3+), 2F5/2 (Yb3+) and 4I13/2 (Er3+) luminescence lifetimes and the presence of energy-transfer processes. The maximal spectral bandwidth equal to 269 nm for the 3F4 → 3H6 transition of Tm3+ suggests that our glass co-doped with Yb3+/Er3+/Tm3+ is a good candidate for broadband near-infrared emission. The energy transfer from 4I13/2 (Er3+) to 3F4 (Tm3+) and cross-relaxation processes are responsible for the enhancement of broadband luminescence near 1.8 µm attributed to the 3F4 → 3H6 transition of thulium ions in lead germanate glass under excitation of Yb3+ ions at 975 nm. [ABSTRACT FROM AUTHOR]

Novel multicomponent titanate-germanate glasses singly doped with transition metal (Cr3+) and rare earth ions (Eu3+) were synthesized and the glass transition temperatures and thermal stability parameters were determined using DSC measurements. X-ray diffraction analysis confirmed fully amorphous nature of the received samples. Their structural and optical properties were compared with germanate glasses without TiO2. Correlation between local structure and optical properties in titanate-germanate glasses is well evidenced by FT-IR, Raman, EPR, and luminescence spectroscopy. In particular, luminescence spectra and their decays are examined for glass samples, where GeO2 was partially substituted by TiO2. [ABSTRACT FROM AUTHOR]

Modified barium gallo-germanate glass hosts are still worthy of attention in studying structure–property relationships. In this work, two different series of glass systems based on (60-x)GeO2-xTiO2-30BaO-10Ga2O3 and (60-x)GeO2-xB2O3-30BaO-10Ga2O3 (x = 10, 30, 50 mol%) were synthesized, and their properties were studied using spectroscopic techniques. X-ray diffraction (XRD) patterns revealed that all fabricated glasses were fully amorphous material. The absorption edge shifted toward the longer wavelengths with a gradual substitution of GeO2. The spectroscopic assignments of titanium ions were performed with excitation and emission spectra compared to the additional sample containing an extremely low content of TiO2 (0.005 mol%). On the basis of Raman and FT-IR investigations, it was found that increasing the TiO2 content caused a destructive effect on the GeO4 and GeO6 structural units. The Raman spectra of a sample containing a predominantly TiO2 (50 mol%) proved that the band was located near 650 cm−1, which corresponded to the stretching vibration of Ti-O in TiO6 unit. The deconvoluted IR results showed that the germanate glass network consisted of the coexistence of two BO3 and BO4 structural groups. Based on the experimental investigations, we concluded that the developed materials are a promising candidate for use as novel glass host matrices for doping rare-earth and/or transition metal ions. [ABSTRACT FROM AUTHOR]

In this paper, the effect of the GeO2:TiO2 molar ratio in glass composition on the spectroscopic properties of germanate glasses was systematically investigated. The visible luminescence bands associated with characteristic 1D2 → 3H4 (red), 5S2, 5F4 → 5I8 (green), and 1D2 → 3F4 (blue) transitions of Pr3+, Ho3+, and Tm3+ ions in systems modified by TiO2 were well observed, respectively. It was found that the luminescence intensity of glasses containing Pr3+ and Ho3+ ions increases, whereas, for Tm3+-doped systems, luminescence quenching with increasing content of TiO2 was observed. Based on Commission Internationale de I'Eclairage (CIE) chromaticity coordinates (x, y) analysis, it was demonstrated that the value of chromaticity coordinates for all glasses depends on the GeO2:TiO2 molar ratio. The addition of TiO2 to system compositions doped with Tm3+ ions shifts the (x, y) to the center of the CIE diagram. However, chromaticity coordinates evaluated for glasses containing Pr3+ ions move to a purer red color. Our results confirm that the spectroscopic properties of the studied glasses strongly depend on TiO2 content. Moreover, it can be stated that germanate-based glass systems modified by TiO2 can be used for optoelectronics in RGB technology as red (Pr3+), green (Ho3+), and blue (Tm3+) emitters. [ABSTRACT FROM AUTHOR]

Inorganic glasses co-doped with rare-earth ions have a key potential application value in the field of optical communications. In this paper, we have fabricated and then characterized multicomponent TiO2-modified germanate glasses co-doped with Yb3+/Ln3+ (Ln = Pr, Er, Tm, Ho) with excellent spectroscopic properties. Glass systems were directly excited at 980 nm (the 2F7/2 → 2F5/2 transition of Yb3+). We demonstrated that the introduction of TiO2 is a promising option to significantly enhance the main near-infrared luminescence bands located at the optical telecommunication window at 1.3 μm (Pr3+: 1G4 → 3H5), 1.5 μm (Er3+: 4I13/2 → 4I15/2), 1.8 μm (Tm3+: 3F4 → 3H6) and 2.0 μm (Ho3+: 5I7 → 7I8). Based on the lifetime values, the energy transfer efficiencies (ηET) were estimated. The values of ηET are changed from 31% for Yb3+/Ho3+ glass to nearly 53% for Yb3+/Pr3+ glass. The investigations show that obtained titanate–germanate glass is an interesting type of special glasses integrating luminescence properties and spectroscopic parameters, which may be a promising candidate for application in laser sources emitting radiation and broadband tunable amplifiers operating in the near-infrared range. [ABSTRACT FROM AUTHOR]

An investigation of the structural and luminescent properties of the transparent germanate glass-ceramics co-doped with Ni2+/Er3+ for near-infrared optical fiber applications was presented. Modification of germanate glasses with 10–20 ZnO (mol.%) was focused to propose the additional heat treatment process controlled at 650 °C to obtain transparent glass-ceramics. The formation of 11 nm ZnGa2O4 nanocrystals was confirmed by the X-ray diffraction (XRD) method. It followed the glass network changes analyzed in detail (MIR—Mid Infrared spectroscopy) with an increasing heating time of precursor glass. The broadband 1000–1650 nm luminescence (λexc = 808 nm) was obtained as a result of Ni2+: 3T2(3F) → 3A2(3F) octahedral Ni2+ ions and Er3+: 4I13/2 → 4I15/2 radiative transitions and energy transfer from Ni2+ to Er3+ with the efficiency of 19%. Elaborated glass–nanocrystalline material is a very promising candidate for use as a core of broadband luminescence optical fibers. [ABSTRACT FROM AUTHOR]