Search

Ultralight ceramics with striking mechanical properties and improved pore connectivity could have wide applications in areas ranging from catalyst support to hot gas filtration. However, creating such materials has proven to be a challenging target. This work demonstrated a novel methodology to prepare porous MgAl 2 O 4 ceramics by calcining gelled MgO–Al 2 O 3 –SiO 2 particle-stabilized foams. The striking green strength of dried foams can be achieved as a consequence of MgO hydration and subsequent formation of gelled Mg(OH) 2 and MgO–SiO 2 –H 2 O skeleton. The decomposition of colloidal substance at elevated temperature resulted in the formation of small pores on the cell wall, thus forming the hierarchical porous architecture and improving the pore connectivity. The highly porous MgAl 2 O 4 ceramics fired at 1600°C possessed the integrated properties of ultrahigh porosity (87.0%), improved pore connectivity and satisfactory compressive strength (7.93 MPa), showing great potential to be used in multiple industrial fields. [ABSTRACT FROM AUTHOR]

Abstract In the present work, Al 2 O 3 -Si 3 N 4 porous ceramics with a cactus-like architecture were fabricated by calcining Al 2 O 3 -Si binary particle-stabilized foams in the nitrogen atmosphere. A large number of acicular Si 3 N 4 nanobelts were constructed on the surface of cell walls as a consequence of CVD process to achieve an interlaced network. Such structure was beneficial to realize a high capture efficiency of particulate matters (PM) during filtration. Resultant products having a bulk density of 0.38 g/cm3 at an apparent porosity of 86% can potentially be applied as the air filters in environment field. [ABSTRACT FROM AUTHOR]

Abstract A facile method for preparation of SiC nanofibrous network reinforced hierarchical structured porous Si 3 N 4 based ceramics via annealing Si-Si 3 N 4 binary particle-stabilized foam in coke bed is reported in this work for the first time. The atmosphere created by coke bed enables the fabrication of Si 3 N 4 based porous ceramics at 1450 °C without using sintering additives. As prepared specimens possess a relative high compressive strength due to the partial oxidation of Si 3 N 4 particles. This novel structure with three levels of hierarchy characterized by flexible SiC nanofibrous network, cell walls and unit cells can be characterized. The vaporization of silicon powder results in formation of Si(g), SiO(g) and allows subsequent generation of SiC nanofibrous network, leading to a considerable number of micro-pores on cell walls simultaneously. As-prepared porous ceramics contained 76.7% porosity and had compressive strength of 10.81 MPa. [ABSTRACT FROM AUTHOR]

Abstract We reveal that zeta potential has a notable effect on properties of foamed suspension, which remains poorly explored. It is demonstrated low zeta potential is beneficial for foam stability, and the experimental results show that absolute value of zeta potential of 30–40 mV is the boundary between stable foams and unstable foams. High zeta potential above 40 mV gives rise to instability of foamed colloidal suspension, owing to strong interparticle repulsion force that prevents particles from forming a closely packed particle network at liquid/air interfaces. Besides, it is found that high zeta potential leads to low foamability of foamed colloidal suspension. It is also demonstrated herein that stable and uniform foams with thin and homogeneous-thickness wall without agglomerates can be prepared at the isoelectric point (IEP) using long-chain surfactant, which generates weak agglomerated particles that can be re-separated to monodisperse particles due to the steric hindrance effect of surfactant. [ABSTRACT FROM AUTHOR]