Search

Abstract The mechanical strength of highly porous ceramic foams shows significant attenuation with the increase of porosity, especially for ceramic foams with very high porosity level above 95%. Ultra-light bulk composite ceramic foams were fabricated via introducing 20 wt% zirconia in alumina-based cell wall, aiming at improving mechanical strength of alumina based ceramic foams. The preparation and stability of alumina and zirconia particles synergistically stabilized foams were investigated. The obtained bulk ceramic foams manifested an exciting combination of both high porosity above 96% and excellent specific compressive strength, due to their closed pore structure, defect-free cell wall with uniform thickness, and uniformly distributed zirconia grains in alumina matrix. The alumina/zirconia composite ceramic foams with porosity of 96.7% exhibited compressive strength of 1.11 ± 0.07 MPa, which was much higher than that of alumina ceramic foams in the case of same porosity. [ABSTRACT FROM AUTHOR]

Compressive strength is one of the most important mechanical properties for ceramic foams but the dependence of compressive strength of highly porous ceramic foams on porosity remains unclear up to now, especially for the ceramic foams with porosity above 94%. In this paper, the relationship between compressive strength and porosity of ceramic foams with high porosity in the range of 79–98% was studied for the first time. The alumina ceramic foams and zirconia foams were prepared by particle-stabilized foaming method using sodium dodecyl sulfonate (SDS) as foaming agent. It was found that the function relation between compressive strength and porosity depended on porosity level. Specifically, compressive strength of ceramic foams fitted well with Rice Model when the porosity ranged from 79% to 94%. When the porosity increased above 95%, compressive strength of ceramic foams showed linear relation to porosity, which was probably due to the characteristic of highly porous ceramic foams with thin and lamellate cell wall. [ABSTRACT FROM AUTHOR]

Ultralight ceramics with striking mechanical properties and improved pore connectivity could have wide applications in areas ranging from catalyst support to hot gas filtration. However, creating such materials has proven to be a challenging target. This work demonstrated a novel methodology to prepare porous MgAl 2 O 4 ceramics by calcining gelled MgO–Al 2 O 3 –SiO 2 particle-stabilized foams. The striking green strength of dried foams can be achieved as a consequence of MgO hydration and subsequent formation of gelled Mg(OH) 2 and MgO–SiO 2 –H 2 O skeleton. The decomposition of colloidal substance at elevated temperature resulted in the formation of small pores on the cell wall, thus forming the hierarchical porous architecture and improving the pore connectivity. The highly porous MgAl 2 O 4 ceramics fired at 1600°C possessed the integrated properties of ultrahigh porosity (87.0%), improved pore connectivity and satisfactory compressive strength (7.93 MPa), showing great potential to be used in multiple industrial fields. [ABSTRACT FROM AUTHOR]

Abstract A facile method for preparation of SiC nanofibrous network reinforced hierarchical structured porous Si 3 N 4 based ceramics via annealing Si-Si 3 N 4 binary particle-stabilized foam in coke bed is reported in this work for the first time. The atmosphere created by coke bed enables the fabrication of Si 3 N 4 based porous ceramics at 1450 °C without using sintering additives. As prepared specimens possess a relative high compressive strength due to the partial oxidation of Si 3 N 4 particles. This novel structure with three levels of hierarchy characterized by flexible SiC nanofibrous network, cell walls and unit cells can be characterized. The vaporization of silicon powder results in formation of Si(g), SiO(g) and allows subsequent generation of SiC nanofibrous network, leading to a considerable number of micro-pores on cell walls simultaneously. As-prepared porous ceramics contained 76.7% porosity and had compressive strength of 10.81 MPa. [ABSTRACT FROM AUTHOR]