This research investigates the combined effect of steel and natural fibre on the mechanical properties and spalling resistance of ultra-high performance concrete (UHPC) before and after exposure to elevated temperatures. The effects of two parameters, namely temperature (ambient temperature, 200 °C, 400 °C and 600 °C) and fibre type (solely macro end hooked steel fibre (MHS) and hybrid of micro straight steel fibre (MSS), macro end hooked steel (MHS) fibre and micro jute (MJ) fibre) on the mechanical properties, spalling resistance and mass loss of UHPC were studied. Micrographs from scanning electron microscope (SEM) test were utilized to appraise the steel fibre and jute fibre before and after exposure to elevated temperatures. The test results exhibited that the residual tensile strength and flexural strength were significantly declined after exposure to high temperatures for UHPC specimens reinforced with macro steel fibre only. Moreover, explosive thermal spalling occurred for this group of specimens under 600 °C. Whereas the combined use of jute fibre and micro-macro steel fibre was an effective approach to prevent the explosive thermal spalling under 600 °C and improve the residual tensile strength, flexural strength and toughness of UHPC. Furthermore, preliminary empirical expressions have been developed in this study to predict the residual mechanical properties of UHPC as a function of natural fibre content, steel fibre content and temperature. [ABSTRACT FROM AUTHOR]

The current investigation aims to choose an alternate potential replacement for the nonbiodegradable synthetic fibers used in polymer composites. This goal motivated the thorough characterization of Rosa hybrida bark (RHB) fibers. The research explored fiber characterization such as morphological, mechanical, thermal, and physical properties. The suggested fiber features a percentage of cellulose, hemicellulose molecules, and lignin of 52.99 wt%, 18.49 wt%, and 17.34 wt%, respectively according to chemical composition studies, which improves its mechanical properties. It is suitable for lightweight applications due to its decreased density (1.194 gcm−3). The purpose of the Fourier transform infrared spectroscope was to observe and record how various chemical groups were distributed throughout the surface of the fiber. The presence of 1.41 nm-sized crystalline cellulose and further XRD analysis showed a crystallinity index of 75.48 %. Scanning electron microscope studies revealed that RHB fibers have a rough surface. According to a single fiber tensile test, for gauge length (GL) 40 mm, Young's modulus and tensile strength of RHB fibers were 6.57 GPa and 352.01 MPa, respectively, and for GL 50 mm, 9.02 GPa and 311 MPa, respectively. Furthermore, thermo-gravimetric examination revealed that the isolated fibers were thermally stable up to 290 °C and the kinetic activation energy was found to be 75.32 kJ/mol. The fibers taken from the Rosa hybrida flower plants' bark exhibit qualities similar to those of currently used natural fibers, making them a highly promising replacement for synthetic fibers in polymer matrix composites. [ABSTRACT FROM AUTHOR]