Search

Nitrile butadiene rubber (NBR) is a water-lubricated bearing material that demonstrates excellent vibrational absorption and impact resistance; however, rapid wear under abnormal conditions is still a serious problem. Graphene (Gra) and carbon nanotubes (CNTs) are two types of carbon nanomaterials with different dimensions and excellent mechanical and friction properties. In this work, Gra and CNTs were used to fill the NBR, and a multifunctional friction and wear testing machine was used to study their impacts on the friction between NBR and ZCuSn10Zn2 under water lubrication conditions. The results indicate that both Gra and CNTs can effectively reduce the adhesion and the friction coefficient of NBR during the friction process. The two-dimensional lamellar structure of Gra is more likely to precipitate from the NBR matrix to generate a surface lubrication film, which can effectively reduce the friction coefficient. Both Gra and CNTs can prevent crack initiation and propagation in NBR during the wear process, thereby effectively reducing the wear of NBR. Compared with the two-dimensional structure of Gra, the one-dimensional linear structure of carbon nanotubes can "trap" the NBR molecular chains more effectively during the friction process, thus reducing the initiation and propagation of wear cracks and further improving the wear performance of NBR. • Effect of different dimensions of carbon nanomaterials on friction behavior of NBR. • Effect mechanism of two-dimensional graphene and one-dimensional carbon nanotubes on friction behavior of NBR. • NBR wear mechanism enhanced by two-dimensional graphene and one-dimensional carbon nanotubes. [ABSTRACT FROM AUTHOR]

This paper investigates how nano-SiO 2 interacts with NBR to affect the tribological properties of water-lubricated NBR-based composites using the Rtec friction and wear tester and the molecular dynamics simulation method. The surface-modified nano-SiO 2 (SiO 2(TESPT)) particles were prepared by modifying the hydroxyl groups on the surface of nano-SiO 2 with Silicon 69 (TESPT), and cast copper alloy (ZCuSn10Zn2) was used as the counterface material in the friction test and wear test. The results showed that different interfacial interplay between nano-SiO 2 and NBR makes for distinct wear mechanisms of NBR-based composites. With weak interface bonding between nano-SiO 2 and NBR, NBR/SiO 2 can easily get worn as nano-SiO 2 particles detach from the matrix during the wear process, leaving pits and cracks on the worn surface. Instead, SiO 2(TESPT) has stronger interface bonding with the matrix, which can prevent the detachment of SiO 2(TESPT) , restrict the movement of molecular chains in NBR, and reduce the temperature peak of the friction pair. SiO 2(TESPT) exerts a dual influence on the tribological properties of NBR: while significantly improving the wear resistance of NBR, it can also notably increase the friction coefficient of the composite. • TESPT was used to modify the surface of nano-SiO 2 to enhance its interfacial bonding with NBR-based composites. • Strong interfacial bonding has dual effects on tribological properties of NBR-based composites. • Strong interfacial bonding can improve the wear property of NBR-based composites. • The study reveals the tribological mechanism of NBR enhanced by stronger interfacial interaction between nano-SiO 2 and NBR. [ABSTRACT FROM AUTHOR]