Search

Inorganic cesium lead halide perovskites offer a pathway towards thermally stable photovoltaics. However, moisture‐induced phase degradation restricts the application of hole transport layers (HTLs) with hygroscopic dopants. Dopant‐free HTLs fail to realize efficient photovoltaics due to severe electrical loss. Herein, we developed an electrical loss management strategy by manipulating poly(3‐hexylthiophene) with a small molecule, i.e., SMe‐TATPyr. The developed P3HT/SMe‐TATPyr HTL shows a three‐time increase of carrier mobility owing to breaking the long‐range ordering of "edge‐on" P3HT and inducing the formation of "face‐on" clusters, over 50 % decrease of the perovskite surface defect density, and a reduced voltage loss at the perovskite/HTL interface because of favorable energy level alignment. The CsPbI2Br perovskite solar cell demonstrates a record‐high efficiency of 16.93 % for dopant‐free HTL, and superior moisture and thermal stability by maintaining 96 % efficiency at low‐humidity condition (10–25 % R. H.) for 1500 hours and over 95 % efficiency after annealing at 85 °C for 1000 hours. [ABSTRACT FROM AUTHOR]

Inorganic cesium lead halide perovskites offer a pathway towards thermally stable photovoltaics. However, moisture‐induced phase degradation restricts the application of hole transport layers (HTLs) with hygroscopic dopants. Dopant‐free HTLs fail to realize efficient photovoltaics due to severe electrical loss. Herein, we developed an electrical loss management strategy by manipulating poly(3‐hexylthiophene) with a small molecule, i.e., SMe‐TATPyr. The developed P3HT/SMe‐TATPyr HTL shows a three‐time increase of carrier mobility owing to breaking the long‐range ordering of "edge‐on" P3HT and inducing the formation of "face‐on" clusters, over 50 % decrease of the perovskite surface defect density, and a reduced voltage loss at the perovskite/HTL interface because of favorable energy level alignment. The CsPbI2Br perovskite solar cell demonstrates a record‐high efficiency of 16.93 % for dopant‐free HTL, and superior moisture and thermal stability by maintaining 96 % efficiency at low‐humidity condition (10–25 % R. H.) for 1500 hours and over 95 % efficiency after annealing at 85 °C for 1000 hours. [ABSTRACT FROM AUTHOR]

Metal‐halide perovskite solar cells (PSCs) exhibit outstanding power conversion efficiencies (PCEs) when fabricated as mm‐sized devices, but creation of high‐performing large‐area modules that are stable on a sufficiently long timescale still presents a significant challenge. Herein, the quality of large‐area perovskite film is improved by using ionic liquid additives via forming a new Pb‐N bonding between the ionic liquid and Pb2+. This new bond can be modulated by a critical screening of the anion structure of the ionic liquid. The selected ionic liquid effectively reduces the defects of the perovskite films and markedly elongate their carrier lifetimes. As a result, a champion PCE of 24.4% for small‐area (0.148 cm2) devices and 20.4% for larger‐area (10.0 cm2) modules under AM 1.5G irradiation is achieved. More importantly, the modified devices retain 90% of their peak PCE after aging for 1900 h at 65 ± 5 °C (ISOS‐T‐1) and 80% after continuous light soaking for 750 h. The non‐encapsulated modules maintained 80% of their peak PCE after 1100 h of aging in the air with a relative humidity of 35 ± 5% and temperature of 25 ± 5 °C under dark (ISOS‐D‐1), showing great potential for future commercialization. [ABSTRACT FROM AUTHOR]