Search

Abstract The occurrence of plasticity below the macroscopic yield stress during tensile monotonic loading of nearly lamellar Ti-45Al-2Nb-2Mn(at%)-0.8 vol% TiB 2 at both 25 °C and 700 °C, and in two conditions of lamellar thickness, was measured by digital image correlation strain mapping of a remodelled Au surface speckle pattern. Such initial plasticity, not necessarily related to the presence of common stress concentrators such as hard particles or cracks, could occur at applied stresses as low as 64% of the general yield stress. For a same applied strain it was more prominent at room temperature, and located as slip and twinning parallel to, and near to or at (respect.) lamellar interfaces of all types in soft mode-oriented colonies. These stretched the full colony width and the shear strain was most intense in the centre of the colonies. Further, the most highly operative microbands of plasticity at specimen fracture were not those most active prior to yielding. The strain mapping results from polycrystalline tensile loading were further compared to those from microcompression testing of soft-mode stacks of lamellae milled from single colonies performed at the same temperatures. Combined with post-mortem transmission electron microscopy of the pillars, the initial plasticity by longitudinal dislocation glide was found to locate within 30–50 nm of the lamellar interfaces, and not at the interfaces themselves. The highly localised plasticity that precedes high cycle fatigue failure is therefore inherently related to the lamellar structure, which predetermines the locations of plastic strain accumulation, even in a single loading cycle. Graphical abstract Image 1 [ABSTRACT FROM AUTHOR]

The stress required to activate twinning of the longitudinal < 11 2 ¯ ] { 111 } system in the lamellar γ-TiAl phase of the alloy Ti-45Al-2Nb-2Mn (at.%)-0.8 vol.% TiB 2 was measured at several temperatures up to 700 °C by in situ micropillar compression of soft mode oriented γ-TiAl/α 2 -Ti 3 Al lamellar stacks. The lamellae undergoing deformation twinning were identified by electron backscatter diffraction orientation mapping. In some cases, such lamellae were not constrained by domain or colony boundaries and longitudinal twinning was the only deformation mechanism observed based on digital image correlation strain maps. The resolved shear stress for such unconstrained twinning was found to increase monotonically with temperature from 25 °C to 700 °C. This is consistent with the stacking fault energy increasing with temperature as found in many metallic alloys, suggesting that the increased ease of deformation twinning at high temperature in bulk TiAl alloys is due to the increased ease with which the twinning shear can be accommodated by the neighbouring domains and lamellae with increasing temperature, rather than a thermal softening of the intrinsic twinning mechanism. [ABSTRACT FROM AUTHOR]

In this paper the occurrence of twinning parallel to the lamellae during compression at 700 °C of a polycrystalline nearly lamellar commercial γ-TiAl alloy, Ti-45Al-2Nb-2Mn(at%)-0.8 vol% TiB 2 , has been studied and shown to lead to the formation of cracks at colony boundaries. However, the occurrence of this longitudinal twinning mode was less common by at least a factor of ten in tests at room temperature. Furthermore, the debonding of colony boundaries caused by the shear strain of longitudinal twinning is exacerbated when the same γ-TiAl variant favourably oriented for twinning occurs repeatedly in the lamellar structure. This effect was caused by the preferential nucleation of certain γ-TiAl variants in the presence of TiB 2 boride reinforcement. It is shown that the boride additions increase the probability of double, triple or even higher order multiply stacked γ-variants. This increases the resulting shear strain that must be accommodated and hence the probability of crack nucleation. [ABSTRACT FROM AUTHOR]