Oxygen evolution reaction (OER) is critical in water splitting for green hydrogen gas production due to its sluggish kinetics; however, commercial OER catalysts commonly suffer from high cost, low catalytic activity and poor stability. Herein, we developed a C+ ion implantation method to modify single crystal diamond, and the resultant surface amorphous layer not only raised the active site number but also increased the content of the C=O group, thus significantly improving the OER activity. The C+ ion implanted high-temperature and high-pressure (C+-HTHP) and chemical vapor deposition (C+-CVD) diamonds both exhibit low OER overpotential with η 10 of 317 mV and 325 mV respectively, superior to those of HTHP diamond (360 mV), CVD diamond (395 mV) and RuO 2 (364 mV). The potentiostatic testing shows that the C+ implanted diamonds almost didn't undergo the rise of OER overpotential upon catalysis for more than 12 h at a current density of 10 mA cm−2, suggesting a high catalytic stability, owing to the strong bonding between single crystal diamond and amorphous carbon layer. For the first time, we utilized carbon ion implantation to prepare diamond-based high-performance OER catalyst, which broadens the understanding of carbon-based materials in OER catalysis. [ABSTRACT FROM AUTHOR]

Lift-off is a promising method to prepare thin, high-finish, and freestanding large-area single crystal and polycrystalline diamonds. However, accurate control of the damage layer characteristic to achieve both stress release and lift-off process is difficult. In this work, high-energy C+ was implanted in single crystal diamond and polycrystalline diamond to create subsurface damage. The defect behavior and structural transformation of the ion implantation and annealing process were investigated. The homoepitaxial growth was subsequently carried out and the epitaxial layer was lifted off from the substrate by selectively etching the damaged layer. The results show that the cap layer and the substrate (below the damage layer) keep the sp3 carbon structure before and after annealing, which is confirmed by the atomic-scale electron energy loss spectroscopy (EELS). The high-resolution transmission electron microscopy (HRTEM) images show that after annealing at 1000 °C for 1 h, the damaged layer was transformed from amorphous carbon to a mixture of graphite and amorphous carbon, providing the damaged layer that could be removed by electrochemical solution. Meanwhile, the distorted diamond area was changed to a sharp interface, which ensures the low roughness of the substrate surface after the lift-off process. After etching for 30 h, a freestanding polycrystalline diamond film with a thickness of 100 μm and a surface roughness of 1.68 nm was obtained. The roughness of the lift-off substrate surface is 1.10 nm, indicating the epitaxial growth can be repeated directly without polishing. [Display omitted] • The defect behavior and structural transformation of the high-energy C+ implanted diamonds were investigated. • The stress state of the diamonds before and after ion implantation and after lift-off process were evaluated. • A 100 μm-thick freestanding polycrystalline diamond film with a surface roughness of 1.68 nm was successful obtained. [ABSTRACT FROM AUTHOR]