Search

It is an effective way to develop basswood (Tilia americana, hardwood)-derived thick carbon electrode for high energy density supercapacitors. The wood-derived anisotropic structural carbon electrodes have different transfer kinetics of the electrolyte, which will significantly affect the electrochemical performance especially at high current density. Therefore, the relationship between the sectional wood-derived electrodes and the electrochemical performance of supercapacitors were systematically studied. The results show that the high specific surface area (542 m2 g−1) of cross-sectional wood-derived carbon contributes to the excellent electrochemical performance (specific/area capacitance ~ 3040 mF cm−2/118 F g−1 at 1 mA cm−2, cycle stability ~ 82.2% after 10,000 cycles at 50 mA cm−2, and capacitive contribution of 76.64% at 5 mV s−1), which is attributed to the hierarchical porous structure and easily allows electrolytes to enter the interior even at high current density. This work provides a fundamental understanding of the dynamic behaviors of electrolyte at different wood sections, and it is expected to be extended to other wood species and wood-like structures for energy storage applications. [ABSTRACT FROM AUTHOR]

Designing energy storage devices from thick carbon electrodes with high areal/volumetric energy density via a simple and green way is very attractive but still challenging. Cellulose, as an excellent precursor for thick carbon electrodes with abundant sources and low cost, is usually activated by a chemical activator and pyrolysis route to achieve high electrochemical performance. However, there are still some problems to be addressed, such as the harsh activation conditions, easy collapse of porous structures, and the high cost. Herein, a 3D self‐supporting thick carbon electrode derived from wood‐based cellulose is proposed for high areal and volumetric energy density of supercapacitor from a mild, simple, and green enzymolysis treatment. Benefiting from the high specific surface area (1418 m2 g−1) and abundant active sites on the surface of wood‐derived hierarchically porous structures and enzymolysis‐induced micropores and mesopores, the assembled symmetry supercapacitor from the thick carbon electrode can realize the high areal/volumetric energy density of 0.21 mWh cm−2/0.99 mWh cm−3 with excellent stability of 86.58% after 15 000 long‐term cycles at 20 mA cm−2. Significantly, the simple and universal strategy to design material with high specific surface area, provides a new research idea for realizing multi‐functional application. [ABSTRACT FROM AUTHOR]

[Display omitted] • High P-doped (9.24 at%) thick carbon electrodes (CW-P) by phytic acid treatment. • SSC exhibits high capacitance of 4.7F cm−2/206.5F g−1 at 1.0 mA cm−2. • Excellent capacitance retention of 90.5% after 20 000 cycles (@20 mA cm−2). • High energy density up to 0.94 mW h cm−2 (41.2 Wh kg−1). • High power density up to 0.6 mW cm−2 (26.3 W kg−1). Keeping outstanding electrochemical performance under high mass loading is critical to develop functional thick electrodes. Here, we report a high phosphorus-doped wood-derived carbon thick electrode for supercapacitor via phytic acid treatment, which can form hydrogen bonds with cellulose molecules in the wood. The content of phosphorus reaches up to 9.24 at% in carbonized wood with P-doping (CW-P-9.24), higher than most previously reported P-doped carbonaceous materials. CW-P-9.24 electrode (800 μm, 17.17 mg cm−2) exhibits greatly improved electrochemical performance, especially in energy density and cyclic stability. Significantly, the symmetrical supercapacitor device exhibits high areal and specific capacitance of 4.7 F cm−2 and 206.5 F g−1 at 1.0 mA cm−2 with prominent retention of 90.5% through the long-term cycling at 20 mA cm−2 for 20,000 cycles, and 0.94 mW h cm−2 (41.2 Wh kg−1) at power density of 0.6 mW cm−2 (26.3 W kg−1), and possesses excellent volumetric capacitance and energy density of 29.3 F cm−3 and 5.8 Wh cm−3, respectively. The outstanding performance can be attributed to the excellent hierarchical structure, low tortuosity, and high phosphorus doping with fast accessible channels at high current density. The extraordinary performance of CW-P has been elucidated by density functional theory calculations, which confirm the enhanced activity by P-doping. These results demonstrate that the CW-P electrode is promising for practical application in energy storage devices and encourage more investigations for thick electrode. [ABSTRACT FROM AUTHOR]