A combination of steam explosion (SE) and alkaline peroxide (AP) used to pretreat bamboo was investigated. Steam explosion at 224 °C for 4 min was applied to bamboo, and the pretreated bamboo was delignified by alkaline peroxide. Enzymatic hydrolysis was compared in the pretreated samples. Steam pretreatment led to remarkable hemicellulose solubilization (63.2%). Lignin solubilization (93.1%) was achieved by alkaline peroxide treatment of steam-pretreated bamboo at 80 °C for 1 h in 0.88% (v/v) H2O2, whereas only 33.4% of lignin was solubilized when using raw bamboo. Pretreatment methods resulted in a low degree of polymerization and increased hydrolysis of cellulose. A maximum glucose yield of 90.5% was achieved with a combined steam explosion and alkaline peroxide pretreatment. The surface structure of treated bamboo and the adsorption of enzyme on the substrate were characterized by X-ray photoelectron spectroscopy. Delignification decreased enzyme adsorption and increased enzymatic conversion. SEM analyses indicated that SE-AP pretreatment disrupted lignin networks and exposed crystalline cellulose in bamboo more effectively than SE or AP pretreatment alone. [ABSTRACT FROM AUTHOR]

Abstract: A two-stage pretreatment method was proposed and tested for deconstruction of recalcitrant Miscanthus. During a 1st pretreatment at 50°C, 1.0–4.0% alkaline peroxide solutions were used to partially remove hemicellulose and lignin. The remaining solids were subjected to a 2nd pretreatment at 121°C with electrolyzed water. Using 15 filter paper units of cellulase per gram cellulose, a digestibility of 95% was achieved by the two-stage method, which was higher than 81% obtained from a 1% H2SO4 pretreatment (200°C, 8min). A mass balance for the two-stage process showed that 63% hemicellulose and 64% lignin were removed from the Miscanthus samples after the 1st pretreatment. The Scanning Electron Microscopy images and Fourier Transform Infrared Spectroscopy spectra revealed that after the 1st pretreatment, crystalline cellulose fibers were partially exposed and the linkages between residual lignin and hemicellulose disappeared. After the 2nd pretreatment, cellulose fibers were completely exposed even with cracks developed. [Copyright &y& Elsevier]