Abstract: The high‐temperature stability of YSZ and MSZ specimens was investigated in CaF2–MgF2–MgO molten salt at 1200°C. YSZ was mostly composed of m‐ZrO2 and a small part of YF3 in the early stages. The formation of YF3 was attributed to the chemical reaction between Y2O3 and MgF2, which can lead to the leaching of Y2O3 from YSZ. With an increase in exposure time, the degraded surface was coarser, and considerable amount of cracks, pores, and spallations were formed. Furthermore, no Y2O3 was found up to 120 μm of the YSZ bulk in the early stages. MSZ was composed of t‐ZrO2 after 24 hours. However, the volume fraction of m‐ZrO2 was 72% after 72 hours, and CaZrO3 was formed by the chemical reaction between CaO and ZrO2 after 168 hours. In addition, the volume fraction of m‐ZrO2 was 60% in 2.5 wt% MgO and 49% in 10 wt% MgO. In 5 wt% MgO, CaZrO3 was formed. We demonstrate that the high‐temperature stability of MSZ was better than that of YSZ, and that 10 wt% MgO was much more stable than the other concentrations of MgO. [ABSTRACT FROM AUTHOR]

Combustion based synthesis of AlN nanoparticles using the "solid nitrogen" promotion reaction was investigated in Al2O3 + 3Mg system in nitrogen atmosphere. A controlled amount of Mg + 0.5NH4Cl mixture as a solid source of nitrogen was blended with the Al2O3 + 3Mg starting system and the synthesis reaction of AlN nanoparticles was conducted using the exothermic heat of the entire reaction system. The resulting AlN nanoparticles were characterized by X-ray diffraction (XRD), Raman and Fourier transform infrared spectroscopy (FTIR), PL spectroscopy, field-emission scanning electron microscopy, transmission electron microscopy, and Brunauer-Emmett-Teller surface area techniques. The analysis results confirmed that single phase and crystalline AlN nanoparticles with an average size of 50-500 nm were obtained from the developed approach. Photoluminescence spectra of AlN nanopowders under the excitation of 230-270 nm UV light revealed that AlN emits yellow-red light having a wavelength near to 590 nm. The chemistry of the combustion process is discussed and the basic reactions that led to the formation of AlN are presented. [ABSTRACT FROM AUTHOR]