Pure, Pb 2+ and Bi 3+ doped Li 4 SrCa(SiO 4 ) 2 materials were prepared by using a conventional solid state reaction. The phase of Li 4 SrCa(SiO 4 ) 2 was determined using the powder XRD. The photoluminescent properties of Pb 2+ and Bi 3+ doped Li 4 SrCa(SiO 4 ) 2 materials were investigated using a spectrofluorometer at room temperature. The emission bands of Li 4 SrCa(SiO 4 ) 2 : Pb 2+ and Li 4 SrCa(SiO 4 ) 2 : Bi 3+ were observed at 290 and 380 nm, respectively. Li 4 SrCa(SiO 4 ) 2 with different Pb 2+ and Bi 3+ doping concentrations were analyzed at room temperature. The Stokes shifts of Li 4 SrCa(SiO 4 ) 2 : Pb 2+ and Li 4 SrCa(SiO 4 ) 2 : Bi 3+ were calculated to be 5678 and 5942 cm −1 , respectively. [ABSTRACT FROM AUTHOR]

Abstract: Li6CaB3O8.5: M3+ (M3+: Dy and Sm) phosphors were synthesized by a solution combustion synthesis. The synthesized materials were characterized by using the powder XRD. The emission and excitation spectra of these materials were measured at room temperature with a spectrofluorometer. Both Li6CaB3O8.5: Dy3+ and Li6CaB3O8.5: Sm3+ phosphors emit red, yellow and green light. Consequently, these materials are promising phosphors for white LEDs. [Copyright &y& Elsevier]

Abstract: Pure, Pb2+ and Bi3+ doped LiCaBO3 materials were prepared by a solution combustion synthesis method. The phase of LiCaBO3 were determined using the powder XRD and FTIR. The photoluminescent properties of Pb2+ and Bi3+ doped LiCaBO3 materials were investigated using spectrofluorometer at room temperature. The emission bands of LiCaBO3: Pb2+ and LiCaBO3: Bi3+ were observed at 296 and 378nm, respectively. LiCaBO3 with different Pb2+ and Bi3+ doping concentrations were analyzed at room temperature. The Stokes shifts of LiCaBO3: Pb2+ and LiCaBO3: Bi3+ were calculated to be 3952 and 6440cm−1, respectively. [Copyright &y& Elsevier]

Abstract: Pure and Pb2+ doped LiSr4(BO3)3 materials were prepared by a solution combustion synthesis method. The phase analysis of all synthesized materials were determined using the powder XRD. The synthesized materials were investigated using spectrofluorometer at room temperature. The excitation and emission bands of LiSr4(BO3)3: Pb2+ were observed at 284 and 328nm, respectively. The dependence of the emission intensity on the Pb2+ concentration for the LiSr4(BO3)3 were studied in detail. It was observed that the concentration quenching of Pb2+ in LiSr4(BO3)3 is 0.005mol. The Stokes shifts of LiSr4(BO3)3: Pb2+ phosphor was calculated to be 4723cm–1. [Copyright &y& Elsevier]