A series of blue phosphors based on Eu2+-activated boracite Zn 3 B 7 O 13 Cl were synthesized by high-temperature solid-state reaction. The phase composition and crystal structure were confirmed by XRD Rietveld refinements, while the optical transitions and band natures were analyzed using absorption spectra. The blue luminescence of Zn 3 B 7 O 13 Cl:Eu2+ shows a narrow band spectrum peaked at 405 nm due to the 4f65 d→4f7(8S 7/2) transitions. Additionally, the sharp line transition of 4f7 (6P 7/2)→4f7 (8S 7/2) was also detected even at 300 K. The experiments confirm that the blue luminescence efficiency of Zn 3 B 7 O 13 (Cl 1-x F x):0.03Eu2+ (x = 0, 0.05, 0.1, 0.2, 0.3) is improved with the increase of the substitution of F− for Cl−. To further improve the luminescence efficiency, the samples were post-annealed at 850 °C in a reducing atmosphere. The results demonstrate that the post-annealing can improve the luminescence efficiency and thermal stability in as-prepared Zn 3 B 7 O 13 (Cl 1-x F x):0.03Eu2+ (x = 0, 0.05, 0.1, 0.2, 0.3) by eliminating the residual Eu3+. The maximum efficiency and thermal activation energy were confirmed in post-annealed Zn 3 B 7 O 13 (Cl 1-x F x):0.03Eu2+ (x = 0.3), which are 65% and 0.31 eV, respectively. The luminescence mechanisms and thermal stability of Eu2+ activators were discussed. • Zn 3 B 7 O 13 Cl:Eu2+ shows an efficient narrowband blue luminescence. • Sharp line transition of 4f7 (6P 7/2).→4f7 (8S 7/2) was also detected even at 300 K. • Luminescence efficiency increases with the substitution of F− for Cl− in the lattice. • Post-annealing eliminates residual Eu3+ resulting in significant improvement of luminescence. [ABSTRACT FROM AUTHOR]

In this work, an anion-alloying strategy using chloride substitution is used to improve the gamma response performance of cutting-edge Cs 2 LiLaBr 6 :Ce single crystal scintillators. Single crystals of Cs 2 LiLa(Br , Cl) 6 :Ce (CLLBC:Ce) with a size of Ф12 mm × 50 mm were successfully grown by the Bridgman method. The effects of chloride substitution amount on crystal structure, band structure, luminescence properties and the scintillation properties were systematically investigated. The light yield and energy resolution of CLLB:Ce were enhanced as the increase of Cl− content. The highest light yield and optimal energy resolution were achieved on the Cs 2 LiLaBr 4 Cl 2 :Ce, about 86% of the commercial LaBr 3 :Ce single crystal and 4.1% at 662 keV. On a basis of the results of first-principle calculation and pure optical method, the band structures of Cs 2 LiLa(Br,Cl):Ce were constructed, indicating a tendency of band-gap to increase as the Cl− content increases. The origin of light yield improvement was also proposed. • The strategy of chloride substitution is used to improve the performance of Cs 2 LiLaBr 6 :Ce single crystal scintillators. • The results of first-principle calculation and pure optical method indicate that the band-gap becomes bigger as the Cl− content increases. • Cs 2 LiLaBr 4 Cl 2 :Ce shows the highest light yield and optimal energy resolution, about 86% of the commercial LaBr 3 :Ce single crystal and 4.1% at 662 keV. • The origin of light yield improvement was also proposed. [ABSTRACT FROM AUTHOR]