We investigate the formations of wurtzite (WZ) SiC nano polytypes in zinc blende (ZB) SiC nanofilms hetero-grown on Si-(100) substrates via low pressure chemical vapor deposition (LPCVD) by adjusting the Si/C ratio of the introduced precursors. Through SEM, TEM, and Raman characterizations, we find that the nanofilms consist of discrete WZ SiC nano polytypes and ZB SiC polytypes composed of WZ polytypes (WZ + ZB) and disordered ZB SiC polytypes, respectively, according to Si/C ratios of 0.5, 1.5, and 3. We attribute the WZ polytype formation to being due to a kinetic mechanism based on the Si/C surface saturation control. [ABSTRACT FROM AUTHOR]

The effect of high-temperature annealing on AlN thin film grown by metalorganic chemical vapor deposition was investigated using atomic force microscopy, Raman spectroscopy, and deep ultra-violet photoluminescence (PL) with the excitation wavelength as short as ∼ 177 nm. Annealing experiments were carried out in either N2 or vacuum atmosphere with the annealing temperature ranging from 1200 °C to 1600 °C. It is found that surface roughness reduced and compressive strain increased with the annealing temperature increasing in both annealing atmospheres. As to optical properties, a band-edge emission peak at 6.036 eV and a very broad emission band peaking at about 4.7 eV were observed in the photoluminescence spectrum of the as-grown sample. After annealing, the intensity of the band-edge emission peak varied with the annealing temperature and atmosphere. It is also found that a much stronger emission band ranging from 2.5 eV to 4.2 eV is superimposed on the original spectra by annealing in either N2 or vacuum atmosphere. We attribute these deep-level emission peaks to the VAL—ON complex in the AlN material. [ABSTRACT FROM AUTHOR]