Search

This study investigated the performance of recycled polypropylene (RPP)/peanut shell powder (PSP) composites with untreated PSP and treated PSP with alkaline peroxide. The RPP/PSP and RPP/PSPH2O2 composites were prepared by melt mixing and compression molding at different PSP loadings (10 wt.% to 40 wt.%). The samples were characterized by processing properties, tensile properties, Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), and water absorption behavior. The treated PSP enhanced the stabilization torque, tensile strength, elongation at break, tensile modulus, and water absorption of RPP/PSP-H2O2 composites. FTIR spectra and SEM showed that the elimination of lignin content strongly influenced the fractured surface and chemical characteristics of the RPP/PSP-H2O2 composites. [ABSTRACT FROM AUTHOR]

Low-pressure steam explosion (LPSE) combined with alkaline peroxide (AP) pretreatment was first employed to separate hemicellulose from Lespedeza stalks. The monosaccharide composition and molecular weight distribution of the obtained hemicellulose fractions were characterized in this study. The results show that the hemicellulose extracted from Lespedeza stalks consisted of xylose, glucose, galactose, and mannose, which was a mixture of arabinoxylans and xyloglucans or β-glucans. The yield of hemicellulose fractions after AP pretreatment ranged from 11.2% (2.5% hydrogen peroxide (H2O2), w/v for 12 h) to 12.2% (3.3% H2O2, w/v for 72 h). The molecular weight of hemicellulose decreased from 2,458 g/mol to 1,984 g/mol after AP pretreatment, indicating its degradation reaction. The structure of hemicellulose was analyzed by Fourier transform infrared spectroscopy, proton nuclear magnetic resonance, and heteronuclear single quantum coherence. The AP pretreatment partially cleaved the backbone and the ether linkage between lignin and hemicelluloses. Also, branched-chain α-Darabinofuranosyl in which β-D-xylose substituted at the C-3 position (monosubstituted) was removed, illustrating a partial debranching reaction. Therefore, the combination of low-pressure steam explosion and alkaline peroxide pretreatment (LPSE-AP) is an effective pretreatment method to separate hemicellulose from Lespedeza stalk. [ABSTRACT FROM AUTHOR]

A combination of steam explosion (SE) and alkaline peroxide (AP) used to pretreat bamboo was investigated. Steam explosion at 224 °C for 4 min was applied to bamboo, and the pretreated bamboo was delignified by alkaline peroxide. Enzymatic hydrolysis was compared in the pretreated samples. Steam pretreatment led to remarkable hemicellulose solubilization (63.2%). Lignin solubilization (93.1%) was achieved by alkaline peroxide treatment of steam-pretreated bamboo at 80 °C for 1 h in 0.88% (v/v) H2O2, whereas only 33.4% of lignin was solubilized when using raw bamboo. Pretreatment methods resulted in a low degree of polymerization and increased hydrolysis of cellulose. A maximum glucose yield of 90.5% was achieved with a combined steam explosion and alkaline peroxide pretreatment. The surface structure of treated bamboo and the adsorption of enzyme on the substrate were characterized by X-ray photoelectron spectroscopy. Delignification decreased enzyme adsorption and increased enzymatic conversion. SEM analyses indicated that SE-AP pretreatment disrupted lignin networks and exposed crystalline cellulose in bamboo more effectively than SE or AP pretreatment alone. [ABSTRACT FROM AUTHOR]

As part of a program to reduce electrical energy consumption in the refining process, the effects of the ozone and alkaline peroxide treatments on fibre and handsheet properties, prior and subsequent to low consistency (LC) refining, were assessed and compared by applying different levels of ozone and a range of peroxide and alkali charges to a primary stage hemlock thermomechanical pulp (TMP). Both highly alkaline peroxide treatments and ozone treatments decreased the specific energy required for strong mechanical pulp. The improvement in pulp strength through alkaline peroxide treatment mainly resulted from pulp surface changes caused by generation of acid groups. The highly alkaline peroxide treatments significantly increased pulp brightness but did not promote the further fibrillation during the subsequent LC refining. On the other hand, ozone treatments provided tensile strength increases, along with small brightness enhancements for the dark hemlock TMP, and increased the tensile gains obtained through LC refining. The effects of ozone treatments on tensile strength before and after LC refining were the result of pulp surface modifications, fibre swelling, and loss of fibre wall integrity due to non-selective chemical attack. High levels of ozone treatment caused tear strength to decrease during subsequent LC refining. [ABSTRACT FROM AUTHOR]